Dependence of Organic Interlayer Diffusion on Glass-Transition Temperature in OLEDs.

Organic light-emitting diodes (OLEDs) are subject to thermal stress from Joule heating and the external environment. In this work, neutron reflectometry (NR) was used to probe the effect of heat on the morphology of thin three-layer organic films comprising materials typically found in OLEDs. It was found that layers within the films began to mix when heated to approximately 20 °C above the glass-transition temperature (Tg) of the material with the lowest Tg. Diffusion occurred when the material with the lowest Tg formed a supercooled liquid, with the rates of interdiffusion of the materials depending on the relative Tg's. If the supercooled liquid formed at a temperature significantly lower than the Tg of the higher-Tg material in the adjacent layer, then pseudo-Fickian diffusion occurred. If the two Tg's were similar, then the two materials can interdiffuse at similar rates. The type and extent of diffusion observed can provide insight into and a partial explanation for the "burn in" often observed for OLEDs. Photoluminescence measurements performed simultaneously with the NR measurements showed that interdiffusion of the materials from the different layers had a strong effect on the emission of the film, with quenching generally observed. These results emphasize the importance of using thermally stable materials in OLED devices to avoid film morphology changes.

[1]  E. Baranoff,et al.  Iridium-based emitters containing pendant triphenylene moieties for bluish-green OLEDs with improved efficiency upon thermal annealing , 2017 .

[2]  J. Kido,et al.  Influence of solution- and thermal-annealing processes on the sub-nanometer-ordered organic-organic interface structure of organic light-emitting devices. , 2017, Nanoscale.

[3]  T. Darwish,et al.  Diffusion at Interfaces in OLEDs Containing a Doped Phosphorescent Emissive Layer , 2016 .

[4]  Junji Kido,et al.  Simultaneous Realization of High EQE of 30%, Low Drive Voltage, and Low Efficiency Roll‐Off at High Brightness in Blue Phosphorescent OLEDs , 2016 .

[5]  J. Kido,et al.  Molecular Interdiffusion between Stacked Layers by Solution and Thermal Annealing Processes in Organic Light Emitting Devices. , 2015, ACS applied materials & interfaces.

[6]  Seok-Ho Hwang,et al.  Above 30% external quantum efficiency in green delayed fluorescent organic light-emitting diodes. , 2015, ACS applied materials & interfaces.

[7]  Wook Song,et al.  Light emission mechanism of mixed host organic light-emitting diodes , 2015 .

[8]  R. Richert,et al.  Thermal stability of vapor-deposited stable glasses of an organic semiconductor. , 2015, The Journal of chemical physics.

[9]  M. Ediger,et al.  Influence of substrate temperature on the transformation front velocities that determine thermal stability of vapor-deposited glasses. , 2015, The journal of physical chemistry. B.

[10]  G. He,et al.  Achieving above 30% external quantum efficiency for inverted phosphorescence organic light-emitting diodes based on ultrathin emitting layer , 2014 .

[11]  Xiao Chen,et al.  Life prediction of OLED for constant-stress accelerated degradation tests using luminance decaying model , 2014 .

[12]  Kwon-Hyeon Kim,et al.  A Fluorescent Organic Light‐Emitting Diode with 30% External Quantum Efficiency , 2014, Advanced materials.

[13]  Bo Seong Kim,et al.  Engineering of Mixed Host for High External Quantum Efficiency above 25% in Green Thermally Activated Delayed Fluorescence Device , 2014 .

[14]  Sangsig Kim,et al.  Analysis of thermal degradation of organic light-emitting diodes with infrared imaging and impedance spectroscopy. , 2013, Optics express.

[15]  Jun Yeob Lee,et al.  Above 30% External Quantum Efficiency in Blue Phosphorescent Organic Light‐Emitting Diodes Using Pyrido[2,3‐b]indole Derivatives as Host Materials , 2013, Advanced materials.

[16]  Christian Mayr,et al.  Organic Light‐Emitting Diodes with 30% External Quantum Efficiency Based on a Horizontally Oriented Emitter , 2013 .

[17]  Junji Kido,et al.  Development of high performance OLEDs for general lighting , 2013 .

[18]  M. Ediger,et al.  Manipulating the properties of stable organic glasses using kinetic facilitation. , 2013, The Journal of chemical physics.

[19]  Kiejin Lee,et al.  Post-annealing effect on the interface morphology and current efficiency of organic light-emitting diodes , 2013 .

[20]  Kookheon Char,et al.  Hole transport materials with high glass transition temperatures for highly stable organic light-emitting diodes , 2012 .

[21]  T. Darwish,et al.  Deuteration of molecules for neutron reflectometry on organic light-emitting diode thin films , 2012 .

[22]  I. Gentle,et al.  Diffusion – the Hidden Menace in Organic Optoelectronic Devices , 2012, Advanced materials.

[23]  D. Beke,et al.  Nanoscale volume diffusion , 2011, Journal of Materials Science.

[24]  Jeremy L. Ruggles,et al.  Investigating Morphology and Stability of Fac‐tris (2‐phenylpyridyl)iridium(III) Films for OLEDs , 2011 .

[25]  F. Klose,et al.  The multipurpose time-of-flight neutron reflectometer “Platypus” at Australia's OPAL reactor , 2011 .

[26]  Andrew Nelson,et al.  Motofit – integrating neutron reflectometry acquisition, reduction and analysis into one, easy to use, package , 2010 .

[27]  Jang‐Joo Kim,et al.  Substrate thermal conductivity effect on heat dissipation and lifetime improvement of organic light-emitting diodes , 2009 .

[28]  Hyun-Jung Kim,et al.  Interface morphologies and interlayer diffusions in organic light emitting device by x-ray scattering , 2009 .

[29]  Sanghoon Song,et al.  Study of thermal degradation of organic light emitting device structures by X-ray scattering , 2007 .

[30]  Giuseppe Nenna,et al.  A Study on Thermal Degradation of Organic LEDs Using IR Imaging , 2007 .

[31]  A. Nelson,et al.  Platypus: a time-of-flight neutron reflectometer at Australia’s new research reactor , 2006 .

[32]  Andrew Nelson,et al.  Co-refinement of multiple-contrast neutron/X-ray reflectivity data using MOTOFIT , 2006 .

[33]  Shizuo Tokito,et al.  Observation of phosphorescence from tris(8-hydroxyquinoline) aluminum thin films using triplet energy transfer from iridium complexes , 2005 .

[34]  Li-Jun Wan,et al.  Direct evidence of molecular aggregation and degradation mechanism of organic light-emitting diodes under joule heating: an STM and photoluminescence study. , 2005, The journal of physical chemistry. B.

[35]  Jianbin Xu,et al.  Real-time visualization of thermally activated degradation of the ITO/CuPC/NPB/Alq3 stack used in one of the organic light-emitting diodes , 2004 .

[36]  Stephen R. Forrest,et al.  The path to ubiquitous and low-cost organic electronic appliances on plastic , 2004, Nature.

[37]  Y. Tao,et al.  High‐Tg Carbazole Derivatives as Blue‐Emitting Hole‐Transporting Materials for Electroluminescent Devices , 2003 .

[38]  Xiaoyuan Hou,et al.  Bubble formation in organic light-emitting diodes , 2000 .

[39]  Ming Lu,et al.  Real-Time Observation of Temperature Rise and Thermal Breakdown Processes in Organic LEDs Using an IR Imaging and Analysis System , 2000 .

[40]  Stephen R. Forrest,et al.  Hole Transporting Materials with High Glass Transition Temperatures for Use in Organic Light-Emitting Devices , 1998 .

[41]  Katsutoshi Nagai,et al.  Multilayer White Light-Emitting Organic Electroluminescent Device , 1995, Science.

[42]  A. Miura,et al.  Molecular design for nonpolymeric organic dye glasses with thermal stability : relations between thermodynamic parameters and amorphous properties , 1993 .

[43]  C. Tang,et al.  Organic Electroluminescent Diodes , 1987 .

[44]  John Crank,et al.  The Mathematics Of Diffusion , 1956 .

[45]  A. Smigelskas.  Zinc diffusion in alpha brass , 1947 .