Stabilisation and characterisation of a new βIII-phase in Zr-doped Bi2O3

The solid state system Bi2O3:ZrO2 has been investigated up to 28 mol% ZrO2 using X-ray and neutron powder diffraction, ac impedance spectroscopy and differential thermal analysis. X-Ray powder diffraction has shown that a solid solution is formed with general composition Bi2 − xZrxO3 + x/2 (0.05 ≤ x ≤ 0.17) for samples calcined at 850 °C. Members of the solid solution adopt a new β-Bi2O3 type structure termed βIII, which is closely related to Pb2F2O. The defect structure of a sample of composition x = 0.15 has been determined by combined high-resolution neutron and X-ray powder diffraction. High temperature powder X-ray diffraction has been used to confirm the structure of the high temperature polymorph, which is a cubic δ-Bi2O3 analogue. In the βIII-phase, solid solution formation proceeds through an anion interstitial mechanism with respect to the hypothetical end member βIII-Bi2O3, with interstitial oxide ions located in channels parallel to the c-axis. The defect structure involves a pair of Zr atoms coordinated to interstitial ions in the channels. A possible conduction mechanism is proposed. Differential thermal analysis and ac impedance measurements indicate a complex phase transition to a highly conducting polymorph (σ700 = 1.02 S cm−1) at temperatures above ca. 690 °C on heating. Crystal parameters: T = 298 K, Bi1.85Zr0.15O3.075, M = 449.49, tetragonal, P42/nmc, a = 7.7206(8), c = 5.6370(6) A, Z = 4, U = 336.0(1) A3, Dc = 8.889(3) g cm−3; T = 1023 K, cubic, Fmm, a = 5.6277(4) A, U = 178.24(4) A3, Z = 2, Dc = 8.379(2) g cm−3.

[1]  G. Mairesse,et al.  Recent Material Developments in Fast Oxide Ion Conductors , 1998 .

[2]  A. Sleight,et al.  New phases in the ZrO2–Bi2O3 and HfO2–Bi2O3 systems , 1998 .

[3]  F. Krok,et al.  Defect structure of quenched γ-BINIVOX , 1998 .

[4]  F. Krok,et al.  Defect structure of quenched γ-BICOVOX by combined X-ray and neutron powder diffraction , 1996 .

[5]  W. Göpel,et al.  Oxide ion conducting solid electrolytes based on Bi2O3 , 1996 .

[6]  David A. Fletcher,et al.  The United Kingdom Chemical Database Service , 1996, J. Chem. Inf. Comput. Sci..

[7]  L. Gauckler,et al.  The bismuth-oxygen system , 1995 .

[8]  A. Virkar,et al.  Effect of Aliovalent Dopants on the Kinetics of Phase Transformation and Ordering in RE2O3-Bi2O3 (RE = Yb, Er, Y, or Dy) Solid Solutions , 1993 .

[9]  Lars Eriksson,et al.  TREOR, a semi-exhaustive trial-and-error powder indexing program for all symmetries , 1985 .

[10]  H. A. Harwig,et al.  The polymorphism of bismuth sesquioxide , 1979 .

[11]  Takehiko Takahashi,et al.  Oxide ion conductors based on bismuthsesquioxide , 1978 .

[12]  H. A. Harwig.  On the Structure of Bismuthsesquioxide: The α, β, γ, and δ-phase , 1978 .

[13]  R. D. Shannon,et al.  Revised values of effective ionic radii , 1970 .

[14]  R. D. Shannon,et al.  Effective ionic radii in oxides and fluorides , 1969 .

[15]  W. C. Hamilton.  Significance tests on the crystallographic R factor , 1965 .

[16]  F. Hund.  Fluoritmischphasen der Dioxide von Uran, Thorium, Cer und Zirkonium mit Wismutoxid , 1964 .