Role of chlorides in hot corrosion of a cast Fe–Cr–Ni alloy. Part I: Experimental studies

Abstract High alloy stainless steels are often used in corrosive, high temperature applications because they form a protective, adherent Cr 2 O 3 scale. When the environment in such applications includes condensed molten salts, especially alkali sulfates and alkali chlorides, these alloys are likely to undergo hot corrosion, even at moderate temperatures compared to their typical maximum application temperature. The chemical (or electrochemical) reactions and transport modes for hot corrosion in a system involving a multi-component alloy and a multi-component salt are complex, but some insight can be gained with the help of a multi-component thermochemical model to identify major reactions. The present work consists of two parts: (a) experimental measurements of hot corrosion rates and characterization of corrosion products on a commercial, cast super-duplex stainless steel (HH), which result from exposure to thin deposits of a mixture of alkali sulfates and alkali chlorides, and (b) an evaluation of possible corrosion reactions by a multi-component thermochemical model. In laboratory hot corrosion tests alloy coupons experienced rapid oxidation rates, penetration of the oxide scale, scale blistering, and scale spallation (on cooling). Compared to simple air oxidation, alkali sulfate deposits increased the corrosion rate by a factor of about 200, but mixtures of alkali sulfate and alkali chloride increased the rate by about 20,000 times. A principal goal of the study was to identify the role of alkali chlorides in accelerating hot corrosion.

[1]  G. W. Goward,et al.  Mechanisms for the hot corrosion of nickel-base alloys , 1973 .

[2]  Khlefa Alarbe Esaklul,et al.  Handbook of case histories in failure analysis , 1992 .

[3]  D. A. Shores,et al.  Transport Considerations in the Hot Corrosion of Ni by Molten Alkali Carbonates , 1990 .

[4]  Per Kofstad,et al.  High Temperature Corrosion , 1988 .

[5]  K. Chiang,et al.  Low temperature hot corrosion , 1983 .

[6]  E. Reese,et al.  Einfluß von Natriumchlorid auf die Oxidation von hochlegierten Chrom- und Chrom-Nickel-Stählen , 1993 .

[7]  H. Evans,et al.  Chromium-depleted zones and the oxidation process in stainless steels , 1976 .

[8]  R. Rapp.  The Hot Corrosion of Metals by Molten Salts , 1981 .

[9]  V. Nagarajan,et al.  Preliminary observations of the thermodynamic predictions of Fe-Cr-Ni alloys in coal gasifier environments , 1979 .

[10]  D. Young.  Oxidation behaviour of some modern heat-resistant cast steels , 1982 .

[11]  H. Grabke,et al.  Einfluß von Chloriden auf die Oxidation des 2¼ Cr‐1 Mo‐Stahls , 1992 .

[12]  R. Rapp,et al.  Halogen Corrosion of Metals , 1976 .

[13]  H. Nelson,et al.  Phase relations in the Fe-Ni-Cr-S system and the sulfidation of an austenitic stainless steel , 1979 .

[14]  G. Rundell,et al.  Oxidation resistance of eight heat-resistant alloys at 870°, 980°, 1095°, and 1150°C , 1991 .

[15]  M. Mcnallan,et al.  Mixed Oxidation of Iron–Chromium Alloys in Gases Containing Oxygen and Chlorine at 900 to 1200°K , 1990 .

[16]  D. Baxter,et al.  Breakdown of chromium oxide scales in sulfur-containing environments at elevated temperatures , 1989 .

[17]  F. Stott,et al.  The Corrosion of metals in an oxidizing-chloridizing environment at high temperature , 1988 .

[18]  M. Hara,et al.  Accelerated oxidation of chromium by trace of sodium chloride vapor , 1991 .

[19]  Howard F. McMurdie,et al.  Phase diagrams for ceramists , 1964 .

[20]  D. A. Shores,et al.  Cracking and Spoiling of Oxide Scale from 304 Stainless Steel at High Temperatures , 1994 .

[21]  D. Young,et al.  The High Temperature Corrosion of Metals in Sulfidizing-Oxidizing Environments: A Critical Review , 1989 .

[22]  D. A. Shores,et al.  Study of cracking and spalling of Cr2O3 scale formed on Ni-30Cr alloy , 1993 .