Laser-induced formation and surface processing of High-Temperature superconductors

The use of lasers in the formation and surface processing of high-temperature superconductors (HTS) is reviewed. Presently, thin film fabrication by reactive laser sputtering, and surface patterning by laser-induced reduction/metallization and ablation are the most promising applications. The great majority of the investigations have been performed for Y-Ba-Cu-O.

[1]  W. Zander,et al.  Direct preparation of high-Tc-superconducting films by laser ablation , 1988 .

[2]  H. Koinuma,et al.  Reversible Resistivity Control of Ba2YCu3O7-δ Thin Films by Laser Annealing , 1988 .

[3]  K. Müller,et al.  Susceptibility Measurements Support High-Tc Superconductivity in the Ba-La-Cu-O System , 1987 .

[4]  Excimer-laser-induced ablation of the high-Tc superconductor Bi-Ca-Sr-Cu-O , 1988 .

[5]  Datta,et al.  Superconductivity at 90 K in the Tl-Ba-Cu-O system. , 1988, Physical review letters.

[6]  Chu,et al.  Superconductivity up to 114 K in the Bi-Al-Ca-Sr-Cu-O compound system without rare-earth elements. , 1988, Physical review letters.

[7]  Wolfram Wersing,et al.  Excimer‐laser‐induced etching of ceramic PbTi1−xZrxO3 , 1987 .

[8]  W. J. Green,et al.  Superconducting thin films of Bi‐Sr‐Ca‐Cu‐O obtained by laser ablation processing , 1988 .

[9]  T. Venkatesan,et al.  Superconducting Y1Ba2Cu3O7−x films on Si , 1988 .

[10]  D. Bäuerle.  Chemical processing with lasers: Recent developments , 1988 .

[11]  E. M. Sherwood.  Less Common Metals , 1956 .

[12]  Orlando Auciello,et al.  Spectroscopic analysis of electronically excited species in XeCl excimer laser‐induced plasmas from the ablated high‐temperature superconductor YBa2Cu3O7 , 1988 .

[13]  R. Feigelson,et al.  Laser-heated pedestal growth of high Tc Bi-Sr-Ca-Cu-O superconducting fibers , 1988 .

[14]  Osamu Eryu,et al.  Y-Ba-Cu Oxide Films Formed with Pulsed-Laser Induced Fragments , 1988 .

[15]  S. Kawai,et al.  Formation of Bi-Sr-Ca-Cu-O Thin Films by a Laser Sputtering Method , 1988 .

[16]  Chu,et al.  Superconductivity at 93 K in a new mixed-phase Yb-Ba-Cu-O compound system at ambient pressure. , 1987, Physical review letters.

[17]  T. Venkatesan,et al.  Transmission electron microscopy studies of superconducting Y-Ba-Cu-O films prepared by laser deposition , 1988 .

[18]  S. Ogale,et al.  Pulsed laser etching of high Tc superconducting films , 1987 .

[19]  L. Schultz,et al.  Epitaxial growth of YBa2Cu3O7−x thin films by a laser evaporation process , 1988 .

[20]  Hoi Sing Kwok,et al.  Deposition of superconducting Y‐Ba‐Cu‐O films at 400 °C without post‐annealing , 1988 .

[21]  S. Wahid,et al.  Superconductivity in thin films of Bi‐Sr‐Ca‐Cu oxide deposited via laser ablation of oxide pellets , 1988 .

[22]  J. Narayan,et al.  Microstructural and compositional variations in laser‐deposited superconducting thin films , 1988 .

[23]  T. Venkatesan,et al.  Observation of two distinct components during pulsed laser deposition of high Tc superconducting films , 1988 .

[24]  A. Morimoto,et al.  Preparation of Ba2YCu3Ox Superconducting Films by Laser Evaporation and Rapid Laser Annealing , 1988 .

[25]  D. Ehrlich,et al.  Reversible laser chemically induced phase transformations in thin‐film Ba2YCu3Ox superconductors , 1988 .

[26]  M. L. Mandich,et al.  Preparation of high Tc and Jc films of Ba2YCu3O7 using laser evaporation of a composite target containing BaF2 , 1988 .

[27]  J. Tarascon,et al.  Smooth high Tc Y1Ba2Cu3Ox films by laser deposition at 650 °C , 1988 .

[28]  C. Eom,et al.  Preparation of oriented Bi‐Ca‐Sr‐Cu‐O thin films using pulsed laser deposition , 1988 .

[29]  H. Hal,et al.  The influence of substrate material and annealing procedure on the properties of superconducting thin films , 1988 .

[30]  C. K. Chiang,et al.  Magnetic behavior of both superconducting thin films and their deposition targets , 1988 .

[31]  T. Venkatesan,et al.  Preparation of Y‐Ba‐Cu oxide superconductor thin films using pulsed laser evaporation from high Tc bulk material , 1987 .

[32]  O. W. Holland,et al.  Formation of thin superconducting films by the laser processing method , 1987 .

[33]  Osamu Eryu,et al.  Energy Beam Irradiation of High-Tc Superconductors Y1Ba2Cu3O7-y and Ho1Ba2Cu3O7-y , 1987 .

[34]  Chu,et al.  Evidence for superconductivity above 40 K in the La-Ba-Cu-O compound system. , 1987, Physical review letters.

[35]  C. Guarnieri,et al.  Thin-film Bi-Sr-Ca-Cu-O high-temperature superconductors using pulsed laser evaporation from sintered disks , 1988 .

[36]  R. D. Greenough,et al.  Spectroscopic and ion probe measurements of KrF laser ablated Y‐Ba‐Cu‐O bulk samples , 1988 .

[37]  Arunava Gupta,et al.  Direct laser writing of superconducting patterns of Y1Ba2Cu3O7−δ , 1988 .

[38]  J. Tarascon,et al.  Substrate effects on the properties of Y‐Ba‐Cu‐O superconducting films prepared by laser deposition , 1988 .

[39]  G. G. Peterson,et al.  Superconducting thin films of Y‐Ba‐Cu‐O produced by neodymium:yttrium aluminum garnet laser ablation , 1988 .

[40]  T. Yoshitake,et al.  Structure and superconducting properties of Y1Ba2Cu3O7−δ films prepared by transversely excited atmospheric pressure CO2 pulsed laser evaporation , 1988 .

[41]  H. Sankur,et al.  Formation of dielectric and semiconductor thin films by laser-assisted evaporation , 1988 .

[42]  Jean-Marie Tarascon,et al.  As‐deposited high Tc and Jc superconducting thin films made at low temperatures , 1988 .

[43]  K. Müller,et al.  Possible highTc superconductivity in the Ba−La−Cu−O system , 1986 .

[44]  A. Kapenieks,et al.  Laser-induced surface metallization of ceramic PLZT , 1986 .

[45]  M. Scheuermann,et al.  Magnetron sputtering and laser patterning of high transition temperature Cu oxide films , 1987 .

[46]  J. Tarascon,et al.  Epitaxial ordering of oxide superconductor thin films on (100) SrTiO3 prepared by pulsed laser evaporation , 1987 .

[47]  Laser-induced surface reduction of the high-Tc superconductor YBa2Cu3O7−x , 1988 .

[48]  P. Siffert,et al.  Deposition of high Tc YBaCuO and BiSrCaCuO superconducting thin films by pulsed excimer laser evaporation , 1988 .

[49]  Hiroshi Maeda,et al.  A New High-T c Oxide Superconductor without a Rare Earth Element , 1988 .

[50]  Wayne A. Weimer,et al.  Plasma emission from laser ablation of the high-temperature superconductor YBa2Cu3O7 , 1988 .

[51]  J. Santiago-Avilés,et al.  Surface compositional and topographical changes resulting from excimer laser impacting on YBa2Cu3O7 single phase superconductors , 1988 .

[52]  A. Hermann,et al.  Bulk superconductivity at 120 K in the Tl–Ca/Ba–Cu–O system , 1988, Nature.

[53]  C. A. Magee,et al.  Nature of the pulsed laser process for the deposition of high Tc superconducting thin films , 1988 .

[54]  M. Eyett,et al.  Influence of the beam spot size on ablation rates in pulsed‐laser processing , 1987 .