Superparamagnetic anisotropic elastomer connectors exhibiting reversible magneto-piezoresistivity

An anisotropic magnetorheological composite formed by dispersions of silver-covered magnetite microparticles (Fe3O4@Ag) in polydimethylsiloxane (PDMS) displaying electrical conduction only in one preferred direction is presented. A set-up for applying and detecting electrical conduction through the composite is described and applied to characterize the behavior of the system in on-off commutation cycles. The composite is obtained by loading the polymer with relatively low concentration of fillers (5% w/w of the total weight) and curing it in the presence of a uniform magnetic field. The fillers appear in the final composite as an array of needles, i.e. pseudo-chains of particles aligned in the direction of the magnetic field. Using Fe3O4 nanoparticles (13 nm) it is possible to obtain cured composites in a superparamagnetic state, that is, without magnetic hysteresis at room temperature. Hysteresis is not found in the elastic properties either; in particular, Mullins effects (change of physical properties after the first strain-stress cycle) were not observed. No measurable transversal electrical conduction was detected (transversal resistivity larger than 62 Mohms∙cm). Thus, significant electrical conductivity is present only between contact points that are exactly facing each other at both sides of the composites in the direction parallel to the needles. The I-V curves in that direction have ohmic behavior and exhibit both piezoresistance and magnetoresistance, that is, the electrical conductivity in the direction parallel to the pseudo-chains increases when a pressure (i.e. compressive stress) is applied at constant magnetic field and/or when a magnetic field is applied at constant pressure. The materials do not exhibit magnetoelectric or piezoresistive hysteresis. These characteristics illustrate the high potentiality of these systems in elastic connectors where electrical conduction can be varied by external mechanical or magnetic forces.

[1]  Miklós Zrínyi,et al.  Smart composites with controlled anisotropy , 2005 .

[2]  O. E. Pérez,et al.  Magnetic and elastic properties of CoFe2O4- polydimethylsiloxane magnetically oriented elastomer nanocomposites , 2011 .

[3]  Ioan Bica,et al.  The influence of hydrostatic pressure and transverse magnetic field on the electric conductivity of the magnetorheological elastomers , 2012 .

[4]  D. Inglis.  A method for reducing pressure-induced deformation in silicone microfluidics. , 2010, Biomicrofluidics.

[5]  M. Knobel,et al.  Superparamagnetism and other magnetic features in granular materials: a review on ideal and real systems. , 2008, Journal of nanoscience and nanotechnology.

[6]  G. Bossis,et al.  Micromechanical analysis of an elastomer filled with particles organized in chain-like structure , 2006 .

[7]  Young-Soo Choi,et al.  A novel pressure sensor with a PDMS diaphragm , 2008 .

[8]  Federica Valentini,et al.  Magnetic tuning of the electrochemical reactivity through controlled surface orientation of catalytic nanowires. , 2006, Journal of the American Chemical Society.

[9]  O. E. Pérez,et al.  Anisotropic magnetoresistance and piezoresistivity in structured Fe3O4-silver particles in PDMS elastomers at room temperature. , 2012, Langmuir : the ACS journal of surfaces and colloids.

[10]  Yu Sun,et al.  Precision patterning of PDMS membranes and applications , 2008 .

[11]  M. Zrínyi,et al.  Magnetic Field-Responsive Smart Polymer Composites , 2007 .

[12]  E. Giannelis,et al.  Low-Energy Magnetic Excitations and Morphology in Layered Hybrid Perovskite−Poly(dimethylsiloxane) Nanocomposites , 2005 .

[13]  R. Whatmore,et al.  Direct and converse magnetoelectic effect in laminate bonded terfenol-D-PZT composites , 2006 .

[14]  G. Kurlyandskaya,et al.  Influence of the preparation procedure on the properties of polyaniline based magnetic composites , 2007 .

[15]  G. Bossis,et al.  Piezoresistivity of magnetorheological elastomers , 2008, Journal of physics. Condensed matter : an Institute of Physics journal.

[16]  G. Bossis,et al.  Mullins effect in elastomers filled with particles aligned by a magnetic field , 2006 .

[17]  F. Gordaninejad,et al.  Sensing Behavior of Magnetorheological Elastomers , 2009 .

[18]  Matthew R J Carroll,et al.  Size Analysis of PDMS-Magnetite Nanoparticle Complexes: Experiment and Theory , 2008 .

[19]  Pierre Gilormini,et al.  Author manuscript, published in "European Polymer Journal (2009) 601-612" A review on the Mullins ’ effect , 2022 .

[20]  Mehdi Farshad,et al.  Magnetoactive elastomer composites , 2004 .

[21]  Cornelia Hison,et al.  The potentiality of composite elastic magnets as novel materials for sensors and actuators , 2003 .

[22]  Silvio D. Rodríguez,et al.  A model for the dependence of the electrical conductance with the applied stress in insulating-conducting composites , 2010 .

[23]  Robert A. Anderson,et al.  Controlling percolation in field-structured particle composites: Observations of giant thermoresistance, piezoresistance, and chemiresistance , 2003 .

[24]  M. Zrínyi,et al.  Magnetic field sensitive functional elastomers with tuneable elastic modulus , 2006 .

[25]  Amit K. Gupta,et al.  Fabrication of polydimethylsiloxane composites with nickel nanoparticle and nanowire fillers and study of their mechanical and magnetic properties , 2009 .

[26]  Note: Mechanical study of micromachined polydimethylsiloxane elastic microposts. , 2010, The Review of scientific instruments.

[27]  Li Sun,et al.  Mechanical characterization of magnetic nanowire–polydimethylsiloxane composites , 2009 .