An environment‐friendly thermal insulation material from cellulose and plasma modification

Cellulose aerogels were prepared by combining the NaOH/thiourea/H2O solvent system and the freeze-drying technology. Hydrophobic aerogels were obtained with the cold plasma modification technology. The results showed that cellulose aerogel had good heat insulation performance, while the main factors affecting thermal conductivity were density and porosity. Thermal conductivity decreased with the decrease of density and the increase of porosity. It could be as low as 0.029 W/(m K). Cellulose aerogel adsorbed moisture easily. The moisture adsorption had a significant influence on the heat insulation performance of aerogel. After conducting hydrophobic modification using CCl4 as plasma, cellulose aerogel was changed from hydrophilic to hydrophobic and water contact angle was as high as 102°. Hydrophobic modification did not affect the heat insulation performance of aerogel. This work provided a foundation for the possibility of applying cellulose aerogels in the insulating material field. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 3652–3658, 2013

[1]  A. Hunt,et al.  Mean Free Path and Apparent Thermal Conductivity of a Gas in a Porous Medium , 1995 .

[2]  P. Achard,et al.  Cellulose-based aerogels , 2006 .

[3]  H. Sugimura,et al.  Wettablity of Poly(ethylene terephthalate) Substrates Modified by a Two‐Step Plasma Process: Ultra Water Repellent Surface Fabrication , 2004 .

[4]  J. Feijen,et al.  Immobilization of functionalized alkyl-poly(ethylene oxide) surfactants on poly(ethylene) surfaces by means of an argon plasma treatment. , 1997, Journal of biomaterials science. Polymer edition.

[5]  Fabienne Poncin-Epaillard,et al.  Synthesis of transparent superhydrophobic polyethylene surfaces , 2006 .

[6]  Lina Zhang,et al.  Effects of coagulants on porous structure of membranes prepared from cellulose in NaOH/urea aqueous solution , 2006 .

[7]  T. Budtova,et al.  Aerocellulose: new highly porous cellulose prepared from cellulose-NaOH aqueous solutions. , 2008, Biomacromolecules.

[8]  K. I. Jensen.  Passive solar component based on evacuated monolithic silica aerogel , 1992 .

[9]  P. Achard,et al.  Use of cellulose-based carbon aerogels as catalyst support for PEM fuel cell electrodes: Electrochemical characterization , 2007 .

[10]  Lina Zhang,et al.  Multifilament Fibers Based on Dissolution of Cellulose in NaOH/Urea Aqueous Solution: Structure and Properties , 2007 .

[11]  Hao Jin,et al.  Nanofibrillar cellulose aerogels , 2004 .

[12]  Lina Zhang,et al.  Novel Fibers Prepared from Cellulose in NaOH/Urea Aqueous Solution , 2004 .

[13]  Xiaojun Wu,et al.  Synthesis and characterization of cellulose derivatives prepared in NaOH/urea aqueous solutions , 2004 .

[14]  K. Barral.  Low-density organic aerogels by double-catalysed synthesis , 1998 .

[15]  F. Poncin‐Epaillard,et al.  Surface modification of hexatriacontane by CF4 plasmas studied by optical emission and threshold ionization mass spectrometries , 1998 .

[16]  R. Gerlach,et al.  Experimental and theoretical investigations of SiO2-aerogel matched piezo-transducers , 1994 .

[17]  L. Ratke,et al.  Synthesis and characterisation of nanofibrillar cellulose aerogels , 2008 .

[18]  Gang Chen,et al.  Phonon heat conduction in nanostructures , 2000 .

[19]  Wei Huang,et al.  Surface modification of polyimide films via plasma polymerization and deposition of allylpentafluorobenzene , 2002 .

[20]  J. Badyal,et al.  Pulsed Plasma Deposition of Super-Hydrophobic Nanospheres , 2002 .

[21]  S. Komarneni,et al.  Nanocomposite aerogels: The SiO_2–Al_2O_3 system , 1993 .

[22]  Lina Zhang,et al.  Unique gelation behavior of cellulose in NaOH/urea aqueous solution. , 2006, Biomacromolecules.

[23]  W. Brown,et al.  A viscosity-molecular weight relationship for cellulose in cadoxen and a hydrodynamic interpretation , 1965 .

[24]  T. Chandy,et al.  Use of plasma glow for surface-engineering biomolecules to enhance bloodcompatibility of Dacron and PTFE vascular prosthesis. , 2000, Biomaterials.

[25]  Pierre-Olivier Chapuis,et al.  Nanoscale heat transfer at contact between a hot tip and a substrate , 2006 .

[26]  Jianjun Shi,et al.  Reinforced low density alginate-based aerogels: Preparation, hydrophobic modification and characterization , 2012 .

[27]  H. Fink,et al.  Characterization of Highly Porous Materials from Cellulose Carbamate , 2008 .

[28]  Bing M. Fung,et al.  Organic Aerogels with Very High Impact Strength , 2001 .

[29]  S. Kistler,et al.  Coherent Expanded Aerogels and Jellies. , 1931, Nature.

[30]  J. Nam,et al.  Highly-loaded silver nanoparticles in ultrafine cellulose acetate nanofibrillar aerogel , 2008 .

[31]  Lina Zhang,et al.  Preparative fractionation of polysaccharides by columns packed with regenerated cellulose gels , 1998 .

[32]  R. A. Young,et al.  Surface fluorination of paper in CF4-RF plasma environments , 2002 .

[33]  Lina Zhang,et al.  Primarily Industrialized Trial of Novel Fibers Spun from Cellulose Dope in NaOH/Urea Aqueous Solution , 2010 .

[34]  S. Kistler.  Coherent Expanded-Aerogels , 1931 .