Effects of Si-rich oxide layer stoichiometry on the structural and optical properties of Si QD/SiO2 multilayer films

The effects of the stoichiometry of the Si-rich oxide (SRO) layer, O/Si ratio, on the structural and optical properties of SRO/SiO2 multilayer films were investigated in this work. SRO/SiO2 multilayer films with different O/Si ratios were grown by a co-sputtering technique, and Si quantum dots (QDs) were formed with post-deposition annealing. By transmission electron microscopy (TEM) and glancing incidence x-ray diffraction (GIXRD), it was found that the Si QD size decreases with increases in O/Si ratio. The photoluminescence (PL) spectrum varies with the O/Si ratio in band position, shape and intensity. In addition, it was observed that the absorption edge blue-shifts with increases in the O/Si ratio. The change in the absorption edge is consistent with strengthening quantum confinement effects in Si QDs, as indicated by TEM and GIXRD. The optical properties were also investigated by 2D photoluminescence excitation (2D-PLE) and lifetime measurements. The origin of emission and absorption is discussed based on the absorption, PL, 2D-PLE and decay time measurements.

[1]  F. Priolo,et al.  Formation and evolution of luminescent Si nanoclusters produced by thermal annealing of SiOx films , 2004 .

[2]  Size and density control of Si-nanocrystals realized by SiOx/SiO2 superlattice , 2007 .

[3]  Harry A. Atwater,et al.  Defect‐related versus excitonic visible light emission from ion beam synthesized Si nanocrystals in SiO2 , 1996 .

[4]  Lorenzo Pavesi,et al.  Optical gain in monodispersed silicon nanocrystals , 2004 .

[5]  The effect of size distributions of Si nanoclusters on photoluminescence from ensembles of Si nanoclusters , 1996 .

[6]  J. Misiewicz,et al.  Influence of the annealing temperature and silicon concentration on the absorption and emission properties of Si nanocrystals , 2007 .

[7]  J. Barreto,et al.  Field effect luminescence from Si nanocrystals obtained by plasma-enhanced chemical vapor deposition , 2006 .

[8]  M. Green,et al.  Effects of boron doping on the structural and optical properties of silicon nanocrystals in a silicon dioxide matrix , 2008, Nanotechnology.

[9]  R. Elliman,et al.  Kinetics ofH2passivation of Si nanocrystals inSiO2 , 2003 .

[10]  L. D. Negro,et al.  Optical gain in different silicon nanocrystal systems , 2005 .

[11]  C. Ammerlaan,et al.  Structural and optical properties of Si-nanoclusters embedded in silicon dioxide , 2006 .

[12]  B. Abeles,et al.  Crystallization kinetics of amorphous Si/SiO2 superlattice structures , 1988 .

[13]  M. Lannoo,et al.  Electronic Structure of Amorphous Silicon , 1997 .

[14]  M. Lannoo,et al.  ELECTRONIC STRUCTURE OF AMORPHOUS SILICON NANOCLUSTERS , 1997 .

[15]  J. Shin,et al.  Intense blue-white luminescence from carbon-doped silicon-rich silicon oxide , 2004 .

[16]  Fabrice Gourbilleau,et al.  Absorption Mechanisms of Silicon Nanocrystals in Cosputtered Silicon-Rich-Silicon Oxide Films , 2008 .

[17]  T. Inokuma,et al.  Structure and grain boundary defects of recrystallized silicon films prepared from amorphus silicon deposited using disilane , 1995 .

[18]  Gavin Conibeer,et al.  Silicon quantum dot nanostructures for tandem photovoltaic cells , 2008 .

[19]  M. G. Garnica-Romo,et al.  Structure of heat-treated sol-gel SiO_2 glasses containing silver , 2001 .

[20]  G. Hwang,et al.  On the origin of Si nanocrystal formation in a Si suboxide matrix , 2007 .

[21]  Steven G. Louie,et al.  Quantum confinement and optical gaps in Si nanocrystals , 1997 .

[22]  Magnus Willander,et al.  Study of structural and optical properties of nanocrystalline silicon embedded in SiO2 , 2000 .

[23]  Lorenzo Pavesi,et al.  Optical gain in silicon nanocrystals , 2001 .

[24]  Gavin Conibeer,et al.  Silicon quantum dot/crystalline silicon solar cells , 2008, Nanotechnology.

[25]  U. Kahler,et al.  Visible light emission from Si nanocrystalline composites via reactive evaporation of SiO , 2001 .

[26]  P. Trwoga,et al.  Modeling the contribution of quantum confinement to luminescence from silicon nanoclusters , 1998 .

[27]  J. Heitmann,et al.  Size-controlled highly luminescent silicon nanocrystals: A SiO/SiO2 superlattice approach , 2002 .

[28]  Lorenzo Pavesi,et al.  Dynamics of stimulated emission in silicon nanocrystals , 2003 .

[29]  M. Tabasky,et al.  Investigation of thick, low‐temperature plasma deposited silica films for waveguide fabrication , 1994 .

[30]  Sandip Tiwari,et al.  A silicon nanocrystals based memory , 1996 .

[31]  C. Bulutay.  Interband, intraband, and excited-state direct photon absorption of silicon and germanium nanocrystals embedded in a wide band-gap lattice , 2007, 0706.0773.

[32]  Z. Horváth.  Semiconductor nanocrystals in dielectrics: Optoelectronic and memory applications of related silicon-based MIS devices , 2006 .

[33]  E. Pink,et al.  ALL-SILICON TANDEM CELLS BASED ON "ARTIFICIAL" SEMICONDUCTOR SYNTHESISED USING SILICON QUANTUM DOTS IN A DIELECTRIC MATRIX , 2005 .

[34]  G. G. Qin,et al.  Photoluminescence mechanism model for oxidized porous silicon and nanoscale-silicon-particle-embedded silicon oxide , 2003 .

[35]  B. Cullity,et al.  Elements of X-ray diffraction , 1957 .

[36]  J. McCaffrey.  Improved TEM samples of semiconductors prepared by a small‐angle cleavage technique , 1993, Microscopy research and technique.

[37]  K. Chrissafis,et al.  Crystallization kinetics of amorphous , 2003 .

[38]  Y. Champion,et al.  Synthesis of controlled-chemistry ultrafine FexNi1−x ferromagnetic powders , 2005 .