Determination of the specific capacitance of conducting polymer/nanotubes composite electrodes using different cell configurations

Abstract Composite materials containing 20 wt.% of multiwalled carbon nanotubes (MWNTs) and 80 wt.% of chemically formed conducting polymers (ECP) as polyaniline (PANI) and polypyrrole (PPy) have been prepared and used for supercapacitor electrodes. The well conducting properties of MWNTs and their available mesoporosity allow a good charge propagation in the composites. Moreover, due to the good resiliency of MWNTs, an excellent stability of the supercapacitor electrodes is observed. It has been shown that the capacitance values for the composites strongly depend on the cell construction. In the case of three electrode cells, extremely high values can be found from 250 to 1100 F/g, however in the two electrode cell much smaller specific capacitance values of 190 F/g for PPy/MWNTs and 360 F/g for PANI/MWNTs have been measured. It highlights the fact that only two-electrode cells allow a good estimation of materials performance in electrochemical capacitors. The applied voltage was found to be the key factor influencing the specific capacitance of nanocomposites. For operating each electrode in its optimal potential range, asymmetric capacitors have been built with PPy/MWNTs as negative and PANI/MWNTs as positive electrodes giving capacitance values of 320 F/g per electrode material.

[1]  Shimshon Gottesfeld,et al.  Conducting polymers as active materials in electrochemical capacitors , 1994 .

[2]  G. Chen,et al.  Electrochemical capacitance of nanocomposite films formed by coating aligned arrays of carbon nanotubes with polypyrrole , 2002 .

[3]  O. Park,et al.  Capacitance properties of graphite/polypyrrole composite electrode prepared by chemical polymerization of pyrrole on graphite fiber , 2002 .

[4]  Zhongping Huang,et al.  Electrochemical synthesis of polypyrrole films over each of well-aligned carbon nanotubes , 2001 .

[5]  Xiaohong Li,et al.  Electrochemical capacitance of well-coated single-walled carbon nanotube with polyaniline composites , 2004 .

[6]  G. Chen,et al.  Electrochemical Capacitance of a Nanoporous Composite of Carbon Nanotubes and Polypyrrole , 2002 .

[7]  F. Béguin,et al.  Carbon materials for the electrochemical storage of energy in capacitors , 2001 .

[8]  John R. Reynolds,et al.  Dopant anion controlled ion transport behavior of polypyrrole , 1991 .

[9]  E. Ruckenstein,et al.  New method for the preparation of thick conducting polymer composites , 1991 .

[10]  Stephen W. Feldberg,et al.  On the Mechanism of Electrochemical Switching in Films of Polyaniline , 1987 .

[11]  Shimshon Gottesfeld,et al.  A study of the electrochemical properties of conducting polymers for application in electrochemical capacitors , 1994 .

[12]  F. Béguin,et al.  Nanotubular materials for supercapacitors , 2001 .

[13]  R. Campomanes,et al.  Study of conductivity of polypyrrol-poly(vinyl alcohol) composites obtained photochemically , 1999 .

[14]  Seong Chu Lim,et al.  High-Capacitance Supercapacitor Using a Nanocomposite Electrode of Single-Walled Carbon Nanotube and Polypyrrole , 2002 .

[15]  Xiaohong Li,et al.  Well-dispersed single-walled carbon nanotube/polyaniline composite films , 2003 .

[16]  N. Comisso,et al.  Electrodeposition of polythiophene, polypyrrole and polyaniline by the cyclic potential sweep method , 1987 .

[17]  François Béguin,et al.  Nanotubular materials as electrodes for supercapacitors , 2002 .

[18]  F. Béguin,et al.  Supercapacitors from nanotubes/polypyrrole composites , 2001 .

[19]  S. Bonnamy,et al.  High yield of pure multiwalled carbon nanotubes from the catalytic decomposition of acetylene on in-situ formed cobalt nanoparticles. , 2002, Journal of nanoscience and nanotechnology.

[20]  M. Barak,et al.  Power Sources 4 , 1974 .