High strain-rate failure in carbon/Kevlar hybrid woven composites via a novel SHPB-AE coupled test

Abstract The high strain-rate induced failure characteristics in a carbon/Kevlar hybrid composite subjected to high strain-rate compressive loading were studied using a novel SHPB-AE coupled test. The tests were performed based on a split-Hopkinson pressure bar (SHPB) apparatus and an acoustic emission (AE) technique, respectively. Within the strain-rate range of 1002–1941 s −1 , a high strain-rate compressive test was conducted on the cylindrical carbon/Kevlar hybrid composite specimens located between the incident and transmitted bars. A wide bandwidth type AE sensor was connected to the specimen with a fine copper waveguide to monitor the AE signals in real time during the test. Specific types of failure mechanisms were observed with optical microscopy and scanning electron microscopy. First, AE characteristics originating from the specimens were investigated profoundly to distinguish the AE signals from diverse damage or failure sources. AE signals were then analyzed in terms of the AE amplitude, the AE count, the slope of cumulative AE count and the peak frequency. Finally, signals were classified into four types based on the waveform and corresponding peak frequency by a short time Fourier transforms (STFT). As a result, under high strain-rate compressive loading, the strain level at the damage initiation was shortened with increasing strain-rate. The failure process of the carbon/Kevlar hybrid woven composite showed initial matrix fracture and then brittle carbon fiber breakage. Subsequently, multiple failure mechanisms appeared, such as fiber-matrix debonding, fiber pull-out, excessive deformation and breakage in the Kevlar fiber tips including splitting and fibrillation. The application of the novel SHPB-AE coupled test to the carbon/Kevlar hybrid composite was discussed in depth for characterizing the failure process, and it was an effective and relevant methodology to grasp in situ information on the failures under high strain-rate compressive loading.

[1]  C. Sun,et al.  Models for the strain-rate-dependent behavior of polymer composites , 2001 .

[2]  R.A.W. Mines,et al.  The Hopkinson pressure bar: an alternative to the instrumented pendulum for Charpy tests , 1985 .

[3]  M. Joshi,et al.  Analytical and experimental studies on mechanical behavior of composites under high strain rate compressive loading , 2013 .

[4]  Chwee Teck Lim,et al.  Dynamic mechanical properties of fabric armour , 2001 .

[5]  Qingming Li,et al.  Correlation between the accuracy of a SHPB test and the stress uniformity based on numerical experiments , 2003 .

[6]  T. Kang,et al.  Energy-absorption mechanisms in Kevlar multiaxial warp-knit fabric composites under impact loading , 2000 .

[7]  Xiong Yan,et al.  Investigation of damage mechanisms in self-reinforced polyethylene composites by acoustic emission , 2006 .

[8]  A. Waas,et al.  Split Hopkinson pressure bar testing of 3D woven composites , 2011 .

[9]  C. A. Weeks,et al.  Modeling non-linear rate-dependent behavior in fiber-reinforced composites , 1998 .

[10]  M. Pharaoh,et al.  Identification of failure modes in glass/polypropylene composites by means of the primary frequency content of the acoustic emission event , 2004 .

[11]  Peter J. de Groot,et al.  Real-time frequency determination of acoustic emission for different fracture mechanisms in carbon/epoxy composites , 1995 .

[12]  N. Takeda,et al.  ACOUSTIC EMISSION CHARACTERIZATION OF A GLASS-MATRIX COMPOSITE , 1992 .

[13]  Werner Hufenbach,et al.  Hybrid 3D-textile reinforced composites with tailored property profiles for crash and impact applications , 2009 .

[14]  A. G. Gibson,et al.  Use of acoustic emission to characterize corrosion fatigue damage accumulation in glass fiber reinforced polyester laminates , 1999 .

[15]  M. J. Forrestal,et al.  Pulse shaping techniques for testing elastic-plastic materials with a split Hopkinson pressure bar , 2005 .

[16]  T. Weerasooriya,et al.  Quasi-Static and Dynamic Compressive Behaviors of a S-2 Glass/SC15 Composite , 2003 .

[17]  T. Yokoyama,et al.  Effects of Radial Inertia and End Friction in Specimen Geometry in Split Hopkinson Pressure Bar Tests : A Computational Study , 2012 .

[18]  Clive R. Siviour,et al.  In-plane and through-thickness properties, failure modes, damage and delamination in 3D woven carbon fibre composites subjected to impact loading , 2012 .

[19]  V.P.W. Shim,et al.  An empirical strain rate-dependent constitutive relationship for glass-fibre reinforced epoxy and pure epoxy , 1995 .

[20]  L. Vincent,et al.  Damage mechanisms characterisation of carbon fibre/epoxy composite laminates by both electrical resistance measurements and acoustic emission analysis , 1996 .

[21]  Nam Seo Goo,et al.  Analysis of the bending fracture process for piezoelectric composite actuators using dominant frequency bands by acoustic emission , 2007 .

[22]  Y. Huang,et al.  Tribological properties of three-dimensional braided carbon/Kevlar/epoxy hybrid composites under dry and lubricated conditions , 2007 .

[23]  S. L. Valença,et al.  Evaluation of the mechanical behavior of epoxy composite reinforced with Kevlar plain fabric and glass/Kevlar hybrid fabric , 2015 .

[24]  L. Dong,et al.  Effect of strain rate on the interlaminar shear strength of carbon-fiber-reinforced laminates , 1994 .

[25]  Paul J. Hogg,et al.  Penetration impact resistance of hybrid composites based on commingled yarn fabrics , 2003 .

[26]  Volker Altstädt,et al.  Acoustic emission analysis for characterisation of damage mechanisms in fibre reinforced thermosetting polyurethane and epoxy , 2014 .

[27]  B. Gu,et al.  Experimental investigation of high-strain rate properties of 3-D braided composite material in cryogenic field , 2015 .

[28]  Zhen Yang,et al.  Failure behavior and performance analysis of hybrid-fiber reinforced PAEK composites at high temperature , 1998 .

[29]  Zhihua Wang,et al.  Mechanical behavior and failure mode of woven carbon/epoxy laminate composites under dynamic compressive loading , 2014 .

[30]  V. Kostopoulos,et al.  Damage evolution in center-holed glass/polyester composites under quasi-static loading using time/frequency analysis of acoustic emission monitored waveforms , 2006 .

[31]  Investigation of damage mechanism of flax fibre LPET commingled composites by acoustic emission , 2013 .

[32]  Sang-Tae Kim,et al.  Characteristics of damage and fracture process of carbon fiber reinforced plastic under loading-unloading test by using AE method , 1997 .

[33]  Zafer Kazancı,et al.  Nonlinear Dynamic Analysis of a Laminated Hybrid Composite Plate Subjected to Time-Dependent External Pulses , 2012 .

[34]  N. Choi,et al.  Characterization of the fracture process of notched glass fiber/aluminum hybrid laminates by acoustic emission , 2008 .

[35]  H. Kolsky,et al.  Experimental studies in plastic wave propagation , 1962 .

[36]  A. R. Bunsell,et al.  Failure mechanism discrimination in carbon fibre-reinforced epoxy composites , 1983 .

[37]  D. Serrano,et al.  Acoustic emission based tensile characteristics of sandwich composites , 2004 .

[39]  S. Ahzi,et al.  Impact response of recycled polypropylene-based composites under a wide range of temperature: Effect of filler content and recycling , 2014 .

[40]  Sung-Choong Woo,et al.  Correlation of fracture processes and damage mechanisms of armor structural materials under high strain rates with acoustic emission characteristics , 2014 .

[41]  Antolino Gallego,et al.  Ti and Cr nitride coating/steel adherence assessed by acoustic emission wavelet analysis , 2005 .

[42]  Tae-won Kim,et al.  High-strain-rate impact in Kevlar-woven composites and fracture analysis using acoustic emission , 2014 .

[43]  Xujing Yang,et al.  Experimental and numerical investigations of strain rate effects on mechanical properties of LGFRP composite , 2016 .

[44]  J. Rhazi,et al.  Acoustic emission in carbon fibre composites , 1990 .