Effect of Internal Air Flow on Local Postweld Heat Treatment for Large Diameter ASME P92 Steel-Welded Pipes

Local postweld heat treatment (PWHT) is usually employed in field fabrication of large-sized ASME SA-335 Grade P92 steel pipes. Internal air flow in pipes that arise from field fabrication can result in considerable convection losses on the inside surface of the pipe when the pipe is not strictly sealed off. Welding and local PWHT experiments of a large diameter P92 steel pipe were conducted both with and without internal air flow, and temperature field of both sides of the pipe was measured. The conjugate heat transfer between the pipe and the internal air is simulated using computational fluid dynamics (CFD) method. The effect of internal air flow on temperature field was further investigated. Results indicate that temperature gradient along through-thickness direction and axial direction during local PWHT is significantly increased due to internal air flow. The increasing rate of temperature difference between inner and outer surface at weld centerline to internal air velocity is about 14.5 °C/(m s−1). The maximum temperature is no longer located at the weld centerline, which will lead to a risk of overheating. The temperature drop is severer in the air inlet side than air outlet side at same distance from weld centerline. For local PWHT to be successful, the internal air flow should be strictly limited during local PWHT; otherwise, the width of heated band (HB) should be extended.

[1]  Wei Zhang,et al.  Quantitative description between pre-fatigue damage and residual tensile properties of P92 steel , 2019, Materials Science and Engineering: A.

[2]  Jianming Gong,et al.  Thermal, metallurgical and mechanical analysis of circumferentially multi-pass welded P92 steel pipes , 2018, International Journal of Pressure Vessels and Piping.

[3]  Hongwei Liu,et al.  Laves phase precipitation behavior in the simulated fine-grained heat-affected zone of creep strength enhanced ferritic steel P92 and its role in creep void nucleation and growth , 2017, Welding in the World.

[4]  Bin Wang,et al.  Residual Stress State of X65 Pipeline Girth Welds Before and After Local and Furnace Post Weld Heat Treatment , 2016 .

[5]  Phillip E. Prueter,et al.  Establishing Recommended Guidance for Local Post Weld Heat Treatment Configurations Based on Thermal-Mechanical Finite Element Analysis , 2016 .

[6]  P. Dong,et al.  A Thermal Stress Mitigation Technique for Local Postweld Heat Treatment of Welds in Pressure Vessels , 2015 .

[7]  P. Mohyla,et al.  Effect of Post-Welding Heat Treatment on Mechanical Properties of Joints of Steel P92 Formed by Submerged Arc Welding , 2014, Metal Science and Heat Treatment.

[8]  H. Jing,et al.  Experimental and Numerical Investigation of Heated Band Width for Local Post Weld Heat Treatment of ASME P92 Steel Pipe , 2014 .

[9]  S. Caminada,et al.  Experiences in the use of advanced materials for Ultra Super Critical thermoelectric power plants: ASTM P92 grade and its weldability , 2012 .

[10]  H. Murakawa,et al.  MECHANICAL BEHAVIOR IN LOCAL POSTWELD HEAT TREATMENT. (REPORT III) : CRITERIA FOR HEATED BAND WIDTH BASED ON THROUGH-THICKNESS TEMPERATURE DISTRIBUTIO N , 1998 .

[11]  H. Murakawa,et al.  Mechanical Behavior in Local Post Weld Heat Treatment (Report I) : Visco-Elastic-Plastic FEM Analysis of Local PWHT(Mechanics, Strength & Structure Design) , 1998 .

[12]  Pradeep Kumar,et al.  Role of evolving microstructure on the mechanical behaviour of P92 steel welded joint in as-welded and post weld heat treated state , 2019, Journal of Materials Processing Technology.

[13]  B. Vandenberghe,et al.  T/P23, 24, 911 and 92: New grades for advanced coal-fired power plants—Properties and experience☆ , 2008 .