Photovoltaic module performance and durability following long‐term field exposure

Our investigations of both new and field-aged photovoltaic modules have indicated that, in general, today's commercially available modules area highly reliable product. However, by using new test procedures, subtle failure mechanisms have also been identified that must be addressed in order to achieve 30-year module lifetimes. This paper summarizes diagnostic test procedures, results, and implications of in-depth investigations of the performance and durability characteristics of commercial modules after long-term field exposure. A collaborative effort with U.S. module manufacturers aimed at achieving 30-year module lifetimes is also described.

[1]  R. G. Ross.  Technology developments toward 30-year-life of photovoltaic modules , 1984 .

[2]  R. Cook,et al.  Direct Observation and Analysis of Indentation Cracking in Glasses and Ceramics , 1990 .

[3]  D. Frear.  Microstructural evolution during the thermomechanical fatigue of solder joints , 1991 .

[4]  A. Rosenthal,et al.  A ten year review of performance of photovoltaic systems , 1993, Conference Record of the Twenty Third IEEE Photovoltaic Specialists Conference - 1993 (Cat. No.93CH3283-9).

[5]  D. Frear.  The Mechanics of Solder Alloy Interconnects , 1993 .

[6]  W. Holley,et al.  UV stability and module testing of nonbrowning experimental PV encapsulants , 1996, Conference Record of the Twenty Fifth IEEE Photovoltaic Specialists Conference - 1996.

[7]  F. Pern,et al.  Encapsulation of PV modules using ethylene vinyl acetate copolymer as a pottant: A critical review , 1996 .

[8]  F. Pern,et al.  Spectroscopic, scanning laser OBIC and I-V/QE characterizations of browned EVA solar cells , 1996, Conference Record of the Twenty Fifth IEEE Photovoltaic Specialists Conference - 1996.

[9]  N. Dhere,et al.  Correlation between surface carbon concentration and adhesive strength at the Si cell/EVA interface in a PV module , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[10]  F. Pern,et al.  Improved photostability of NREL-developed EVA pottant formulations for PV module encapsulation , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[11]  D. L. King,et al.  Field Experience with a New Performance Characterization Procedure for Photovoltaic Arrays Field Experience with a New Performance Characterization Procedure for Photovoltaic Arrays , 2022 .

[12]  D. L. King,et al.  Dark current-voltage measurements on photovoltaic modules as a diagnostic or manufacturing tool , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.