Dry processing of high resolution and high aspect ratio structures in GaAs-Al(x)Ga(1-x) As for integrated optics.

The properties of ion-beam milling, rf-sputter etching, and plasma etching for the fabrication of high resolution integrated optical structures in GaAs and Al(x)Ga(l-x)As were investigated. The ion-beam milling rates for a 500-eV Ar beam were measured as a function of the angle of incidence for A2-1350 photoresist, GaAs, Al, Ti, and Ta in vacuum. For Ti and Ta, the ion-beam milling rates were measured for various O(2) partial pressures in the target chamber. For the fabrication of high-resolution patterns, a technique was developed in which a very thin resist pattern is transferred by plasma etching into a layer of Ta prior to ion-beam milling. Both ion-beam milling and rf-sputter etching through the Ta metal mask were used for the fabrication of gratings in GaAs. From measurements made in this study, it was found that rf-sputter etching in an Ar atmosphere results in a resolution comparable to ion-beam milling at normal incidence, but the material removal efficiency is somewhat lower. Third-order Bragg diffraction gratings (period = 0.36-0.37 microm) for GaAs-Al(x)Gal(1-x) As heterostructure lasers and ridged stripes 10 microm wide and 1.5-2.0 microm deep have been prepared by these techniques. High-aspect ratio or skewed-profile gratings were obtained by selection of the ion-beam milling or rf-sputter etching conditions. As previously reported, these structures have been overgrown by MBE A(x)Gal(1-x) As layers to form distributed feedback lasers.

[1]  R. Logan,et al.  Optical waveguides in GaAs–AlGaAs epitaxial layers , 1973 .

[2]  R. A. Logan,et al.  GaAs‐AlxGa1‐xAs injection lasers with distributed Bragg reflectors , 1975 .

[3]  G. Carter,et al.  The growth of topography during sputtering of amorphous solids , 1973 .

[4]  D. J. Barber,et al.  Prediction of ion-bombarded surface topographies using Frank's kinematic theory of crystal dissolution , 1973 .

[5]  Rudolf A.H. Heinecke,et al.  Control of relative etch rates of SiO2 and Si in plasma etching , 1975 .

[6]  M. Cantagrel.  Considerations on high resolution patterns engraved by ion etching , 1975, IEEE Transactions on Electron Devices.

[7]  G. K. Wehner,et al.  Sputtering Yields of Metals for Ar+ and Ne+ Ions with Energies from 50 to 600 ev , 1961 .

[8]  H. W. Yen,et al.  GaAs–Ga1−xAlxAs double‐heterostructure distributed‐feedback diode lasers , 1974 .

[9]  Amnon Yariv,et al.  cw operation of distributed‐feedback GaAs‐GaAlAs diode lasers at temperatures up to 300 K , 1975 .

[10]  B. I. Miller,et al.  Double‐heterostructure GaAs distributed‐feedback laser , 1974 .

[11]  H. Lüthje,et al.  The influence of the target material on sputter etching processes , 1975 .

[12]  Grating masks suitable for ion-beam machining and chemical etching , 1974 .

[13]  L. Comerford,et al.  Selectively etched diffraction gratings in GaAs , 1974 .

[14]  Charles V. Shank,et al.  Optical technique for producing 0.1‐μ periodic surface structures , 1973 .

[15]  H. C. Casey,et al.  Room-temperature operation of low-threshold separate-confinement heterostructure injection laser with distributed feedback , 1975 .

[16]  R. Tsui,et al.  Calculation of Ion Bombarding Energy and Its Distribution in rf Sputtering , 1968 .

[17]  E. G. Spencer,et al.  Ion-Beam Techniques for Device Fabrication , 1971 .

[18]  A. Katzir,et al.  GaAs--GaAlAs distributed-feedback diode lasers with separate optical and carrier confinement , 1975 .

[19]  H. Casey,et al.  Epitaxial growth on optical gratings for distributed feedback GaAs injection lasers , 1975 .

[20]  G. N. Jackson,et al.  R.F. sputtering , 1970 .

[21]  Donald R. Scifres,et al.  Single-heterostructure distributed-feedback GaAs-diode lasers , 1975 .

[22]  M. Cantagrel,et al.  Argon ion etching in a reactive gas , 1973 .

[23]  M. Moulin,et al.  Evolution of well-defined surface contour submitted to ion bombardment: computer simulation and experimental investigation , 1975 .

[24]  M. W. Thompson,et al.  Microtopography of surfaces eroded by ion-bombardment , 1969 .

[25]  D. Botez,et al.  Optical bends and rings fabricated by preferential etching , 1975 .

[26]  E Garmire,et al.  Channel Optical Waveguides and Directional Couplers in GaAs-lmbedded and Ridged. , 1974, Applied optics.

[27]  J. E. Coker,et al.  Distributed-Feedback Double-Heterostructure GaAs Injection Laser with Fundamental Grating. , 1974, Applied optics.

[28]  Toshihisa Tsukada,et al.  GaAs–Ga1−xAlxAs buried‐heterostructure injection lasers , 1974 .

[29]  W. Tsang,et al.  Profile and groove‐depth control in GaAs diffraction gratings fabricated by preferential chemical etching in H2SO4‐H2O2‐H2O system , 1976 .

[30]  B. Miller,et al.  Proton-bombardment formation of stripe-geometry heterostructure lasers for 300 K CW operation , 1972 .

[31]  Per G. Glöersen.  Ion Beam Etching , 1975, Atomic Layer Processing.

[32]  J. C. Dyment,et al.  HERMITE‐GAUSSIAN MODE PATTERNS IN GaAs JUNCTION LASERS , 1967 .

[33]  J. Umeda,et al.  "Very low current operation of 'mesa-stripe' geometry double-heterostructure injection lasers" , 1972 .

[34]  M. Cantagrel,et al.  Development of a general surface contour by ion erosion. Theory and computer simulation , 1974 .

[35]  E Garmire,et al.  Ion beam micromachining of integrated optics components. , 1973, Applied optics.

[36]  A. Bayly.  Secondary processes in the evolution of sputter-topographies , 1972 .

[37]  Henry I. Smith,et al.  Fabrication techniques for surface-acoustic-wave and thin-film optical devices , 1974 .