In this study we report on our investigation of the microstructure of nickel oxide films produced by e-beam evaporation, sol-gel deposition and, sputtering techniques. We give characteristic cyclic voltammetry, current-voltage relationships, and optical transmission data for films made by each technique. Data is shown for electrodes both uncycled and cycled for 17-20 hrs. We found all samples have at least one phase corresponding to cubic nickel oxide (NaCl structure). Other phases, such as nickel hydroxide, may exist but are not immediately identifiable. The stucture of the films ranges from fine polycrystalline to amorphous. and varies over the surface of the sample. Films that were cycled for 17-20 hours all tended to have improved transmittance, as high as a 20% change. The highest transmission range from bleached to colored was for the evaporated films, which showed ΔT=60%. The sol-gel films showed a large residual coloration in the bleached state after cycling, about a 40% decline was noted. Overall, after cycling the films appeared to be slightly more crystalline. In all films after cycling there were increases in the coloration and bleaching current. Also peak shifts were noted after cycling, the coloration peak tended to shift to higher and the bleaching peak shifted to lower potentials. The overall coloration efficiency (550 nm) for these films ranged from 26-36 cm2/C.
[1]
C. Lampert,et al.
Electrochromic materials and devices for energy-efficient windows. [161 references]
,
1984
.
[2]
P. Falaras.
Optical techniques for the study of electrochromic phenomena application of Raman spectroscopy and optical multichannel analysis (OMA) to the coloration of oxides and polymer films
,
1990,
Other Conferences.
[3]
C. M. Lampert,et al.
Optical Properties Of Electrochromic Nickel Oxide Devices Utilizing A Polymeric Electrolyte
,
1989,
Other Conferences.
[4]
Carl M. Lampert.
Chemical and optical studies of electrochromic hydrated nickel oxide films and devices
,
1990,
Other Conferences.
[5]
Carl M. Lampert,et al.
Chemical and Optical Properties of Electrochromic Nickel Oxide Films
,
1985,
Optics & Photonics.
[6]
Carl M. Lampert,et al.
Spectroscopic and electrochemical studies of electrochromic hydrated nickel oxide films
,
1987
.