Nano-Cr-film-based solar selective absorber with high photo-thermal conversion efficiency and good thermal stability.

Optical properties and thermal stability of the solar selective absorber based on the metal/dielectric four-layer film structure were investigated in the variable temperature region. Numerical calculations were performed to simulate the spectral properties of multilayer stacks with different metal materials and film thickness. The typical four-layer film structure using the transition metal Cr as the thin solar absorbing layer [SiO(2)(90nm)/Cr(10nm)/SiO(2)(80nm)/Al (≥100nm)] was fabricated on the Si or K9 glass substrate by using the magnetron sputtering method. The results indicate that the metal/dielectric film structure has a good spectral selective property suitable for solar thermal applications with solar absorption efficiency higher than 95% in the 400-1200nm wavelength range and a very low thermal emittance in the infrared region. The solar selective absorber with the thin Cr layer has shown a good thermal stability up to the temperature of 873K under vacuum atmosphere. The experimental results are in good agreement with the calculated spectral results.

[1]  R. Collins,et al.  Optimization and analysis of solar selective surfaces with continuous and multilayer profiles , 1995 .

[2]  Steven G. Johnson,et al.  Design and global optimization of high-efficiency thermophotovoltaic systems. , 2010, Optics express.

[3]  Mukul Agrawal,et al.  High performance solar-selective absorbers using coated sub-wavelength gratings. , 2010, Optics express.

[4]  Reflective solar cooker designs , 1955 .

[5]  A. Sievers,et al.  Spectral selectivity of high-temperature solar absorbers. , 1980, Applied optics.

[6]  M. Povinelli,et al.  Optimal design of aperiodic, vertical silicon nanowire structures for photovoltaics. , 2011, Optics express.

[7]  O. Hunderi,et al.  Selective absorption of solar energy in ultrafine metal particles: Model calculations , 1979 .

[8]  E. Palik.  Handbook of Optical Constants of Solids , 1997 .

[9]  David R. Mills,et al.  Very low‐emittance solar selective surfaces using new film structures , 1992 .

[10]  J. Talghader,et al.  Absorption to reflection transition in selective solar coatings. , 2012, Optics express.

[11]  Mukul Agrawal,et al.  Design of wide-angle solar-selective absorbers using aperiodic metal-dielectric stacks. , 2009, Optics express.

[12]  David R. Mills,et al.  New cermet film structures with much improved selectivity for solar thermal applications , 1992 .

[13]  Ruey-Lin Chern,et al.  Polarization-independent broad-band nearly perfect absorbers in the visible regime. , 2011, Optics express.

[14]  R. W. Christy,et al.  Optical constants of transition metals: Ti, V, Cr, Mn, Fe, Co, Ni, and Pd , 1974 .

[15]  P. Zhou,et al.  High solar absorption of a multilayered thin film structure. , 2007, Optics express.

[16]  D. Lynch,et al.  Optical Properties of Antiferromagnetic Chromium and Dilute Cr-Mn and Cr-Re Alloys , 1970 .

[17]  W. R. Hunter,et al.  Comments on the Optical Constants of Metals and an Introduction to the Data for Several Metals , 1997 .

[18]  D. Mills.  Limits of solar selective surface performance. , 1985, Applied optics.

[19]  J. Meiss,et al.  Selective absorption enhancement in organic solar cells using light incoupling layers , 2010 .