The corrosion/wear mechanisms of Ti–6Al–4V alloy for different scratching rates

Abstract Titanium and its alloys are currently in use as implant materials for orthopaedic surgery. These materials possess outstanding corrosion resistance due to a dense and passive oxide film on the surface. When these alloys are implanted in a living body, removal of surface material takes place because of mechanical wear and corrosion. Simultaneous chemical and mechanical effects also limit long-term use of such materials. The aim of the present study is to clarify the damage accumulation mechanism of Ti–6Al–4V alloys under the simultaneous reaction of corrosion and wear. For this purpose, we developed a new tribocorrosion system and then evaluated corrosion wear characteristics of the alloys with special attention focused on the effects of scratching rate on repassivation behavior. Two types of corrosion wear tests were carried out: one was the free corrosion potential measurement and the other was the potentiostatic polarization test both with simultaneous application of wear damage. In corrosion wear environment, a transition of wear type from abrasive to adhesive was observed with increase of the scratching rates. Higher scratching rate prevented regeneration of passive films on worn surfaces, resulting in generation of relatively large corrosion pits and a change in the wear mechanism. These results suggested that the scratching rate was an important factor affecting the damage accumulation process.

[1]  Tiancheng Zhang,et al.  RETRACTED: Mechanisms responsible for synergy between fretting and corrosion for three biomaterials in saline solution , 2001 .

[2]  R. Barrack,et al.  Corrosion and wear at the modular interface of uncemented femoral stems. , 1994, The Journal of bone and joint surgery. British volume.

[3]  T. Hanawa,et al.  Metal ion release from titanium with active oxygen species generated by rat macrophages in vitro. , 2000, Journal of biomedical materials research.

[4]  D. Landolt,et al.  Influence of passivity on the tribocorrosion of carbon steel in aqueous solutions , 2001 .

[5]  P. Mutton,et al.  Some effects of microstructure on the abrasion resistance of metals , 1978 .

[6]  S. D. Cramer,et al.  Wear-corrosion study of white cast irons , 1995 .

[7]  O. Pohler,et al.  Unalloyed titanium for implants in bone surgery. , 2000, Injury.

[8]  K. L. Dahm,et al.  The corrosion–wear behaviour of thermally oxidised CP-Ti and Ti–6Al–4V , 2004 .

[9]  Xiaoxia Jiang,et al.  A study of the corrosive wear of Ti-6Al-4V in acidic medium , 1989 .

[10]  P. Ducheyne,et al.  Titanium serum and urine levels in rabbits with a titanium implant in the absence of wear. , 1996, Biomaterials.

[11]  C. Rieker,et al.  In vitro comparison of the two hard-hard articulations for total hip replacements , 2001, Proceedings of the Institution of Mechanical Engineers. Part H, Journal of engineering in medicine.

[12]  D. Landolt,et al.  Third body effects and material fluxes in tribocorrosion systems involving a sliding contact , 2004 .

[13]  Y. Toyama,et al.  Metal ions induce bone-resorbing cytokine production through the redox pathway in synoviocytes and bone marrow macrophages. , 2003, Biomaterials.

[14]  D. Landolt,et al.  Electrochemical effects on the fretting corrosion behaviour of Ti6Al4V in 0.9% sodium chloride solution , 2005 .

[15]  S. D. Cramer,et al.  Methods of measuring wear-corrosion synergism , 1995 .

[16]  Ricardo M. Souto,et al.  The effect of temperature on the nucleation of corrosion pits on titanium in Ringer's physiological solution. , 2005, Biomaterials.

[17]  E. Machtei,et al.  Fracture of Dental Implants: Literature Review and Report of a Case , 2002, Implant dentistry.

[18]  P. Tengvall,et al.  Surface immobilized bisphosphonate improves stainless-steel screw fixation in rats. , 2004, Biomaterials.

[19]  K. Bessho,et al.  Experimental long-term study of titanium ions eluted from pure titanium miniplates. , 1995, Journal of biomedical materials research.

[20]  Jiang Xiaoxia,et al.  Effect of environmental embrittlement on wear resistance of alloys in corrosive wear , 1999 .

[21]  Y. Okazaki,et al.  Implant Applications of Highly Corrosion-Resistant Ti-15Zr-4Nb-4Ta Alloy , 2002 .

[22]  Xinchun Lu,et al.  Effects of surface deformation on corrosive wear of stainless steel in sulfuric acid solution , 1999 .

[23]  P. D. Wilson,et al.  Metallic wear in failed titanium-alloy total hip replacements. A histological and quantitative analysis. , 1988, The Journal of bone and joint surgery. American volume.

[24]  K. L. Dahm,et al.  Hard coatings for orthopedic implants , 1995 .

[25]  T. Yamamuro,et al.  In vivo measurement of anodic polarization of orthopaedic implant alloys: comparative study of in vivo and in vitro experiments. , 1989, Biomaterials.

[26]  P. Ducheyne,et al.  Systemic titanium levels in rabbits with a titanium implant in the absence of wear , 1997, Journal of materials science. Materials in medicine.

[27]  J Fisher,et al.  A novel low wearing differential hardness, ceramic-on-metal hip joint prosthesis. , 2001, Journal of biomechanics.

[28]  Y. Okazaki.  Effect of friction on anodic polarization properties of metallic biomaterials. , 2002, Biomaterials.

[29]  S. Virtanen,et al.  Influence of surface self-modification in Ringer's solution on the passive behavior of titanium. , 2005, Journal of biomedical materials research. Part A.

[30]  J. Macák,et al.  Self-organized nanotubular oxide layers on Ti-6Al-7Nb and Ti-6Al-4V formed by anodization in NH4F solutions. , 2005, Journal of biomedical materials research. Part A.

[31]  Stefano Mischler,et al.  Influence of fretting regimes on the tribocorrosion behaviour of Ti6Al4V in 0.9 wt.% sodium chloride solution , 2004 .

[32]  P. Ducheyne,et al.  Local accumulation of titanium released from a titanium implant in the absence of wear. , 1996, Journal of biomedical materials research.

[33]  D. Landolt,et al.  A tribo-electrochemical apparatus for in vitro investigation of fretting–corrosion of metallic implant materials , 2002 .