Solar-blind AlGaN-based p-i-n photodiodes with low dark current and high detectivity

We report solar-blind Al/sub x/Ga/sub 1-x/N-based heterojunction p-i-n photodiodes with low dark current and high detectivity. After the p+ GaN cap layer was recess etched, measured dark current was below 3 fA for reverse bias values up to 6 V. The device responsivity increased with reverse bias and reached 0.11 A/W at 261 nm under 10-V reverse bias. The detectors exhibited a cutoff around 283 nm, and a visible rejection of four orders of magnitude at zero bias. Low dark current values led to a high differential resistance of 9.52/spl times/10/sup 15/ /spl Omega/. The thermally limited detectivity of the devices was calculated as 4.9/spl times/10/sup 14/ cm/spl middot/Hz/sup 1/2/W/sup -1/.

[1]  Theeradetch Detchprohm,et al.  Demonstration of Flame Detection in Room Light Background by Solar‐Blind AlGaN PIN Photodiode , 2001 .

[2]  Ekmel Ozbay,et al.  High-Performance Solar-Blind AlGaN Schottky Photodiodes , 2003 .

[3]  R. Dupuis,et al.  Low-noise photodetectors based on heterojunctions of AlGaN–GaN , 2001 .

[4]  M. M. Wong,et al.  Selective regrowth of Al0.30Ga0.70N p–i–n photodiodes , 2000 .

[5]  Joe C. Campbell,et al.  High quantum efficiency AlGaN/GaN solar-blind photodetectors grown by metalorganic chemical vapor deposition , 2001 .

[6]  J. F. Schetzina,et al.  Visible-Blind UV Digital Camera Based On a 32 × 32 Array of GaN/AlGaN p-i-n Photodiodes , 1999 .

[7]  Silvano Donati,et al.  Photodetectors: Devices, Circuits and Applications , 1999 .

[8]  Ekmel Ozbay,et al.  High-speed solar-blind photodetectors with indium-tin-oxide Schottky contacts , 2003 .

[9]  Ekmel Ozbay,et al.  Solar-blind AlGaN-based Schottky photodiodes with low noise and high detectivity , 2002 .

[10]  Michael S. Shur,et al.  Indium-Silicon Co-Doping of High-Aluminum-Content AlGaN for Solar Blind Photodetectors , 2001 .

[11]  Manijeh Razeghi,et al.  AlGaN ultraviolet photoconductors grown on sapphire , 1996 .

[12]  Henryk Temkin,et al.  Schottky barrier photodetectors based on AlGaN , 1998 .

[13]  High Performance Solar Blind Detectors Based on AlGaN Grown by MBE on Si , 2001 .

[14]  Joe C. Campbell,et al.  Improved detection of the invisible , 1999 .

[15]  Pierre Gibart,et al.  Analysis and modeling of AlxGa1−xN-based Schottky barrier photodiodes , 2000 .

[16]  E. Ozbay,et al.  High-speed visible-blind GaN-based indium–tin–oxide Schottky photodiodes , 2001 .

[17]  Manijeh Razeghi,et al.  Semiconductor ultraviolet detectors , 1996 .

[18]  Joe C. Campbell,et al.  Improved solar-blind external quantum efficiency of back-illuminated AlxGa1−xN heterojunction pin photodiodes , 2002 .