A method is reported for determining the two‐dimensional distribution of refractive‐index changes in Ti‐diffused LiNbO3 strip waveguides. The measurement process was as follows. Distributions of diffused Ti concentration in LiNbO3 were measured using an x‐ray microanalyzer. Using calibration curves the Ti concentrations were then converted into refractive‐index changes. To obtain high spatial resolution in the two‐dimensional XMA measurement the electron beam position was fixed and the sample was moved at a constant velocity. Lateral sliding of the sample perpendicular to the scanning direction was peformed mechanically, and the measured XMA data were corrected for edge effects. The results obtained for the Y‐cut LiNbO3 waveguide diffused at 1000 °C for 10 h with a 10‐μm‐wide 500‐A‐thick Ti strip showed that lateral diffusion of Ti was marked. The contour with a refractive‐index change of 1×10−3 is of approximate depth 3.5 μm and width 40 μm. The maximum values of Δne and Δn0 were 1×10−2 and 8×10−3, respe...
[1]
R. Schmidt,et al.
Switched directional couplers with alternating Δ Β
,
1976
.
[2]
J. Carruthers,et al.
Optical waveguiding layers in LiNbO3 and LiTaO3
,
1973
.
[3]
Juichi Noda,et al.
Electro‐optic amplitude modulation using three‐dimensional LiNbO3 waveguide fabricated by TiO2 diffusion
,
1975
.
[4]
E. A. J. Marcatili,et al.
Dielectric rectangular waveguide and directional coupler for integrated optics
,
1969
.
[5]
M. Minakata,et al.
Precise determination of refractive‐index changes in Ti‐diffused LiNbO3 optical waveguides
,
1978
.