Black anodic coatings for space applications: Study of the process parameters, characteristics and mechanical properties

Black inorganic anodized aluminium alloys are used for managing passive thermal control on spacecraft and for avoiding stray light in optical equipment. Spalling of these coatings has sometimes been observed after thermal cycling on 2XXX and 7XXX aluminium alloys. This phenomenon could generate particulate contamination in satellites and may affect mission lifetime. In this work, the influences of the four main steps of the process (pretreatments, sulphuric anodizing, colouring and sealing) on the coating characteristics have been studied for a 7175T7351 aluminium alloy. The chemical heterogeneity of the coating has been underlined, and its mechanical behaviour observed through crazing. Scratch-testing, used to evaluate coating adhesion to its substrate, revealed the negative impact of thermal cycling.

[1]  K. Shimizu,et al.  Interactions of alloying elements during anodizing of dilute Al-Au-Cu and Al-W-Zn alloys and consequences for film growth , 1998 .

[2]  G. Thompson,et al.  Influence of copper on the morphology of porous anodic alumina , 2006 .

[3]  Jiada Wu,et al.  Determination of Adhesion Energy of CNx Thin Film on Silicon from Micro-Scratch Testing , 2004 .

[4]  Yu-Chieh Huang,et al.  Study on the black electrolytic coloring of anodized aluminum in cupric sulfate , 2008 .

[5]  F. Keller,et al.  Structural Features of Oxide Coatings on Aluminum , 1953 .

[6]  Jian Lu,et al.  Four-point bending tests of thermally produced WC-Co coatings , 1996 .

[7]  J. Fransaer,et al.  Influence of the anodizing temperature on the porosity and the mechanical properties of the porous anodic oxide film , 2007 .

[8]  Yarong Wang,et al.  Effect of alloy types on the anodizing process of aluminum , 2006 .

[9]  Gérard Bernhart,et al.  Oxidation and oxide spallation of heat resistant cast steels for superplastic forming dies , 2002 .

[10]  L. Arurault.  Pilling–Bedworth ratio of thick anodic aluminium porous films prepared at high voltages in H2SO4 based electrolyte , 2008 .

[11]  Ming Gao,et al.  An analytical electron microscopy study of constituent particles in commercial 7075-T6 and 2024-T3 alloys , 1998 .

[12]  K. Shimizu,et al.  Grain orientation effects on copper enrichment and oxygen generation during anodizing of an Al-1at.%Cu alloy. , 2003 .

[13]  A. Galerie,et al.  Adhesion of oxide scales grown on ferritic stainless steels in solid oxide fuel cells temperature and atmosphere conditions , 2007 .

[14]  Steve Bull,et al.  Failure mode maps in the thin film scratch adhesion test , 1997 .

[15]  M. Ibrahim.  Black nickel electrodeposition from a modified Watts bath , 2006 .

[16]  G. Thompson,et al.  Porous anodic alumina: fabrication, characterization and applications , 1997 .

[17]  J. Earthman,et al.  Surface Characterization of 7075-T73 Aluminum Exposed to Anodizing Pretreatment Solutions , 2008, Journal of Materials Engineering and Performance.

[18]  Steve Bull,et al.  An overview of the potential of quantitative coating adhesion measurement by scratch testing , 2006 .

[19]  L. Dobrzański,et al.  The influence of cast method and anodizing parameters on structure and layer thickness of aluminium alloys , 2004 .

[20]  Anssi Laukkanen,et al.  A model for stresses, crack generation and fracture toughness calculation in scratched TiN-coated steel surfaces , 2003 .

[21]  D. Rickerby.  A review of the methods for the measurement of coating-substrate adhesion☆ , 1988 .

[22]  K. Shimizu,et al.  The influence of θ′ precipitates on the anodizing behaviour of binary Al-Cu alloys , 1997 .

[23]  H. Bhojraj,et al.  Anodizing and inorganic black coloring of aluminum alloys for space applications , 1997 .

[24]  Doug M. McCroskey,et al.  Aeroglaze Z306 black paint for cryogenic telescope use: outgassing and water vapor regain , 2000, SPIE Optics + Photonics.

[25]  Ray Levesque,et al.  Black anodize as a thermal control coating for Space Station Freedom , 1992 .

[26]  R. Mcclung,et al.  Anodized aluminum coatings for thermal control. II - Environmental effects and cracking , 1992 .

[27]  N. N. Regone,et al.  Al-based anodic oxide films structure observation using field emission gun scanning electron microscopy , 2006 .

[28]  H. Ollendorf,et al.  A comparative study of adhesion test methods for hard coatings , 1999 .

[29]  R. Buchheit.  A Compilation of Corrosion Potentials Reported for Intermetallic Phases in Aluminum Alloys , 1995 .

[30]  M. Laugier,et al.  An energy approach to the adhesion of coatings using the scratch test , 1984 .

[31]  R. Mcclung,et al.  Stresses in Sulfuric Acid Anodized Coatings on Aluminum , 1993 .