Failure analysis on abnormal wear of roller bearings in gearbox for wind turbine

Abstract The booming wind power industry as one of the predominant approaches of renewable energy resources is not independent of components reliability within the wind turbines, especially the rotating ones including blades, motors, gearboxes etc. Hence, case studies on failed parts of such components play an important role for failure prevention and deserves to be publicly reported for experience sharing. In this paper, a failure case concerning severe abnormal wear of the roller bearing's inner ring in the gearbox of one 1.5 MW wind turbine in China was reported. Since such roller bearings were imported from a foreign company and operated by a Chinese company, not only economic losses but also international commercial dispute would be induced if this case would not be immediately and properly solved. To this end, by means of comprehensive and systematic investigation into the base materials, process media, surface morphologies, micro-area compositions and even service environments, root causes of this failure were determined, detailed mechanisms were discussed, and pertinent countermeasures were proposed. Achievement of this paper would provide the solid evidence to distinguish the responsibilities for the failure, and would also help to prevent such failures of roller bearings with similar design in wind turbines.

[1]  Zhen‐Guo Yang,et al.  Failure analysis on abnormal wall thinning of heat-transfer titanium tubes of condensers in nuclear power plant Part I: Corrosion and wear , 2014 .

[2]  Yi Gong,et al.  Corrosion evaluation of one dry desulfurization equipment - Circulating fluidized bed boiler , 2011 .

[3]  Yibing Liu,et al.  Multi-fault detection and failure analysis of wind turbine gearbox using complex wavelet transform , 2016 .

[4]  Y. Gong,et al.  Acidic/caustic alternating corrosion on carbon steel pipes in heat exchanger of ethylene plant , 2011 .

[5]  Y. Gong,et al.  Failure analysis of leakage on titanium tubes within heat exchangers in a nuclear power plant. Part II: Mechanical degradation , 2012 .

[6]  Tao Feng,et al.  Design defect of wind turbine operating in typhoon activity zone , 2013 .

[7]  B. Gould,et al.  Investigating the Process of White Etching Crack Initiation in Bearing Steel , 2016, Tribology Letters.

[8]  V. Prabhu Raja,et al.  Failure analysis of shear pins in wind turbine generator , 2011 .

[9]  J. Ribrant,et al.  Survey of Failures in Wind Power Systems With Focus on Swedish Wind Power Plants During 1997–2005 , 2007, IEEE Transactions on Energy Conversion.

[10]  Wei Zhao,et al.  Preliminary failure investigation of a 52.3 m glass/epoxy composite wind turbine blade , 2014 .

[11]  Y. Gong,et al.  Heat Strength Evaluation and Microstructures Observation of the Welded Joints of One China-Made T91 Steel , 2012, Journal of Materials Engineering and Performance.

[12]  Jianzhong Xu,et al.  Structural failure analysis of wind turbines impacted by super typhoon Usagi , 2016 .

[13]  Sabbah Ataya,et al.  Damages of wind turbine blade trailing edge: Forms, location, and root causes , 2013 .

[14]  Y. Gong,et al.  Failure analysis of leakage on titanium tubes within heat exchangers in a nuclear power plant. Part I: Electrochemical corrosion , 2012 .

[15]  Y. Gong,et al.  Fracture failure analysis of automotive accelerator pedal arms with polymer matrix composite material , 2013 .

[16]  Zhen‐Guo Yang,et al.  Failure analysis on abnormal wall thinning of heat-transfer titanium tubes of condensers in nuclear power plant Part II: Erosion and cavitation corrosion , 2014 .

[17]  J. C. Marín,et al.  Study of fatigue damage in wind turbine blades , 2009 .

[18]  Xianghui Xiao,et al.  An analysis of premature cracking associated with microstructural alterations in an AISI 52100 failed wind turbine bearing using X-ray tomography , 2017 .

[19]  Zhenguo Yang,et al.  Mechanical and tribological properties of polyoxymethylene modified with nanoparticles and solid lubricants , 2008 .

[20]  Chen Dong,et al.  Partial Load: A Key Factor Resulting in the Failure of Gear in the Wind Turbine Gearbox , 2016, Journal of Failure Analysis and Prevention.

[21]  Sufang Zhang,et al.  Political and institutional analysis of the successes and failures of China’s wind power policy , 2013 .

[22]  Andrew Kusiak,et al.  Application of cyclic coherence function to bearing fault detection in a wind turbine generator under electromagnetic vibration , 2017 .

[23]  Mayorkinos Papaelias,et al.  Wind turbine reliability analysis , 2013 .

[24]  Manuela Sander,et al.  Fretting fatigue induced surface cracks under shrink fitted main bearings in wind turbine rotor shafts , 2016 .

[25]  Robert J.K. Wood,et al.  A FIB/TEM study of butterfly crack formation and white etching area (WEA) microstructural changes under rolling contact fatigue in 100Cr6 bearing steel , 2013 .

[26]  Jun Wang,et al.  Assessment of creep rupture properties for dissimilar steels welded joints between T92 and HR3C , 2011 .

[27]  Peder Klit,et al.  Observations of the effect of varying Hoop stress on fatigue failure and the formation of white etching areas in hydrogen infused 100Cr6 steel rings , 2015 .

[28]  M. Herbig,et al.  Atomic scale characterization of white etching area and its adjacent matrix in a martensitic 100Cr6 bearing steel , 2017 .

[29]  Yi Gong,et al.  Failure analysis of bursting on the inner pipe of a jacketed pipe in a tubular heat exchanger , 2010 .

[30]  Zhongjun Yin,et al.  Fracture analysis of wind turbine main shaft , 2013 .

[31]  Jui-Sheng Chou,et al.  Failure analysis of wind turbine blade under critical wind loads , 2013 .

[32]  Yingning Qiu,et al.  Monitoring wind turbine gearboxes , 2013 .

[33]  B. Amirzadeh,et al.  A computational framework for the analysis of rain-induced erosion in wind turbine blades, part I: Stochastic rain texture model and drop impact simulations , 2017 .

[34]  R. J. Hernandez,et al.  Analysis of catastrophic failure of axial fan blades exposed to high relative humidity and saline environment , 2015 .

[35]  Zhen‐Guo Yang,et al.  Failure analysis on abnormal corrosion of economizer tubes in a waste heat boiler , 2017 .

[36]  Torgeir Moan,et al.  A prognostic method for fault detection in wind turbine drivetrains , 2014 .

[37]  Y. Gong,et al.  Pitting corrosion on 316L pipes in terephthalic acid (TA) dryer , 2009 .

[38]  Yi Gong,et al.  Failure analysis of heat exchanger tubes in petrochemical industry: Microscopic analysis approach , 2016 .

[39]  Jiahai Yuan,et al.  Wind turbine manufacturing in China: A review , 2015 .

[40]  Yingning Qiu,et al.  Wind turbine condition monitoring: technical and commercial challenges , 2014 .

[41]  Shi Yan,et al.  Failure analysis on circulating water pump of duplex stainless steel in 1000 MW ultra-supercritical thermal power unit , 2015 .

[42]  Peter Tavner,et al.  Failure Modes and Effects Analysis (FMEA) for wind turbines. , 2010 .

[43]  Y. Gong,et al.  Failure analysis of one peculiar ‘Yin-Yang’ corrosion morphology on heat exchanger tubes in purified terephthalic acid (PTA) dryer , 2013 .

[44]  Yingning Qiu,et al.  Applying thermophysics for wind turbine drivetrain fault diagnosis using SCADA data , 2016 .

[45]  Jianzhong Xu,et al.  Failure investigation on a coastal wind farm damaged by super typhoon: A forensic engineering study , 2015 .

[46]  Byeng D. Youn,et al.  Classification of operating conditions of wind turbines for a class-wise condition monitoring strategy , 2017 .

[47]  Xuping Wang,et al.  Detection of gear cracks in a complex gearbox of wind turbines using supervised bounded component analysis of vibration signals collected from multi-channel sensors , 2016 .

[48]  Hongwei Liu,et al.  Fault analysis of wind turbines in China , 2016 .

[49]  A. Schwedt,et al.  Microstructural changes in White Etching Cracks (WECs) and their relationship with those in Dark Etching Region (DER) and White Etching Bands (WEBs) due to Rolling Contact Fatigue (RCF) , 2017 .

[50]  Y. Gong,et al.  Comparative study on degradation of ethylene-propylene rubber for nuclear cables from gamma and beta irradiation , 2017 .

[51]  Jui-Sheng Chou,et al.  Failure analysis and risk management of a collapsed large wind turbine tower , 2011 .

[52]  B. Amirzadeh,et al.  A computational framework for the analysis of rain-induced erosion in wind turbine blades, part II: Drop impact-induced stresses and blade coating fatigue life , 2017 .