Composite-coated aluminum bipolar plates for PEM fuel cells

Abstract Aluminum-based bipolar plates for proton exchange membrane (PEM) fuel cells offer high strength and durability while weighing up to 65% less than stainless steel. To protect the aluminum from electrochemical corrosion while maintaining electrical conductivity, coatings that are a composite of a fluoropolymer and one or more conductive inorganic fillers were investigated. Titanium carbide (TiC) and graphite were found to be the best candidates for conductive fillers among six powders that were tested for acid and electrochemical stability. Composite coatings of graphite, TiC, and ethylene-tetrafluoroethylene (ETFE) were applied to the aluminum or ceramic substrates by wet spraying followed by heat treatment, and then tested for in-plane sheet resistance, through-plane area specific resistance (ASR), electrochemical corrosion resistance, flexural strength, and flexibility. The composite-coated aluminum plates meet the U.S. DOE targets for bipolar plates for in-plane conductivity, flexural strength, and cathodic corrosion resistance. The targets for through-plane ASR and anodic corrosion resistance were not met due to the spraying process producing an undesirable layered microstructure and also a microstructure with connected porosity and pinholes.

[1]  Theodore J. Reinhart,et al.  Engineered materials handbook , 1987 .

[2]  R. Koç,et al.  Carbothermal synthesis of titanium carbide using ultrafine titania powders , 1997 .

[3]  G. V. Samsonov,et al.  Handbook of Refractory Compounds , 1980 .

[4]  Naved Siddiqui,et al.  Synthesis of Submicron/Nano Sized CaB6 from Carbon Coated Precursors , 2011 .

[5]  D. Hodge,et al.  Production of TiB2 from a precursor containing carbon coated TiO2 and B4C , 2000 .

[6]  D. Hodgson,et al.  A review of metal separator plate materials suitable for automotive PEM fuel cells , 2009 .

[7]  P. Haldar,et al.  Effect of surface roughness of composite bipolar plates on the contact resistance of a proton exchange membrane fuel cell , 2009 .

[8]  J. Mawdsley,et al.  Synthesis of Nano‐Size TiB2 Powders using Carbon Coated Precursors , 2011 .

[9]  K. S. Weil,et al.  Development of a niobium clad PEM fuel cell bipolar plate material , 2007 .

[10]  J. Sykes,et al.  Effects of inorganic additions on the performance of manganese-based conversion treatments , 2007 .

[11]  Heli Wang,et al.  Stainless steel as bipolar plate material for polymer electrolyte membrane fuel cells , 2003 .

[12]  F. Mansfeld,et al.  The CeMo process for the development of a stainless aluminum , 1992 .

[13]  Brian D. James,et al.  Mass Production Cost Estimation for Direct H2 PEM Fuel Cell Systems for Automotive Applications. 2008 Update , 2010 .

[14]  Y. Soma,et al.  Electrochemical Properties of Titanium in PEFC Bipolar Plate Environments , 2010 .

[15]  Haijun Yu,et al.  Anticorrosion properties of Ta-coated 316L stainless steel as bipolar plate material in proton exchange membrane fuel cells , 2009 .

[16]  Jun Du,et al.  Investigation of the Ce-Mn conversion coating on 6063 aluminium alloy , 2010 .

[17]  J. J. Lee,et al.  (Titanium, chromium) nitride coatings for bipolar plate of polymer electrolyte membrane fuel cell , 2009 .