Etching chemistry of benzocyclobutene (BCB) low-k dielectric films in F2+O2 and Cl2+O2 high density plasmas

The etching chemistry of benzocyclobutene (BCB) low-k dielectric films was studied in a high density plasma etcher using F2+O2 and Cl2+O2 plasmas. The etching rate in F2+O2 plasmas exceeded 1.2 μm/min with selectivity over oxide and nitride of 16 and 32, respectively. The etching rate in Cl2+O2 plasmas exceeded 0.6 μm/min with selectivity over oxide and nitride of 40 and 80, respectively. BCB films do not etch in pure Cl2 or pure O2 plasmas without ion bombardment, but etching rates of 1000 A/min were observed using F2 plasmas without ion bombardment. The ion flux in F2+O2 plasmas is primarily O2+ and O+, whereas in Cl2+O2 the dominant ion is ClO+. BCB etching yields in F2+O2 plasmas were measured with a plasma beam/quartz crystal microbalance system. The etching yields suggest that the neutral fluxes and surface chemistry control the etching rates under these conditions, not the ion flux. Using x-ray photoelectron spectroscopy, it was determined that oxygen plasmas preferentially remove the carbon content of BCB, leaving behind a silicon oxide surface. Chlorine plasmas preferentially remove the silicon, leaving behind a carbon surface. F2+O2 plasmas etch BCB through a fluorocarbon film layer, the thickness of which increases with increasing fluorine concentration in the plasma.The etching chemistry of benzocyclobutene (BCB) low-k dielectric films was studied in a high density plasma etcher using F2+O2 and Cl2+O2 plasmas. The etching rate in F2+O2 plasmas exceeded 1.2 μm/min with selectivity over oxide and nitride of 16 and 32, respectively. The etching rate in Cl2+O2 plasmas exceeded 0.6 μm/min with selectivity over oxide and nitride of 40 and 80, respectively. BCB films do not etch in pure Cl2 or pure O2 plasmas without ion bombardment, but etching rates of 1000 A/min were observed using F2 plasmas without ion bombardment. The ion flux in F2+O2 plasmas is primarily O2+ and O+, whereas in Cl2+O2 the dominant ion is ClO+. BCB etching yields in F2+O2 plasmas were measured with a plasma beam/quartz crystal microbalance system. The etching yields suggest that the neutral fluxes and surface chemistry control the etching rates under these conditions, not the ion flux. Using x-ray photoelectron spectroscopy, it was determined that oxygen plasmas preferentially remove the carbon conten...

[1]  Yicheng Wang,et al.  Ion energy distributions in inductively coupled radio-frequency discharges in argon, nitrogen, oxygen, chlorine, and their mixtures , 1999 .

[2]  T. W. Hamilton,et al.  Surface dependent electron and negative ion density in inductively coupled discharges , 1999 .

[3]  J. Coburn,et al.  Heterogeneous recombination of atomic bromine and fluorine , 1999 .

[4]  K. Kadota,et al.  Measurements of negative ion density in high-density oxygen plasmas by probe-assisted laser photodetachment , 1998 .

[5]  David B. Graves,et al.  The recombination of chlorine atoms at surfaces , 1998 .

[6]  C. Fleddermann,et al.  Negative ion densities in chlorine- and boron trichloride-containing inductively coupled plasmas , 1997 .

[7]  N. R. Rueger,et al.  Role of steady state fluorocarbon films in the etching of silicon dioxide using CHF3 in an inductively coupled plasma reactor , 1997 .

[8]  Jane P. Chang,et al.  Kinetic study of low energy ion-enhanced polysilicon etching using Cl, Cl2, and Cl+ beam scattering , 1997 .

[9]  C. Steinbrüchel,et al.  Patterning of Benzocyclobutene by Reactive Ion Etching , 1996 .

[10]  R. Hoekstra,et al.  Predictions of ion energy distributions and radical fluxes in radio frequency biased inductively coupled plasma etching reactors , 1996 .

[11]  C. Sullivan,et al.  Anisotropic ECR etching of benzocyclobutene , 1995 .

[12]  M. Schier.  Reactive Ion Etching of Benzocyclobutene Using a Silicon Nitride Dielectric Etch Mask , 1995 .

[13]  D. J. Economou,et al.  A two-region model of a radiofrequency low-pressure, high-density plasma , 1995 .

[14]  M. Kushner,et al.  Investigation of electron source and ion flux uniformity in high plasma density inductively coupled etching tools using two‐dimensional modeling , 1994 .

[15]  P. B. Chinoy,et al.  Processing and microwave characterization of multilevel interconnects using benzocyclobutene dielectric , 1993 .

[16]  D. C. Gray,et al.  Phenomenological modeling of ion‐enhanced surface kinetics in fluorine‐based plasma etching , 1993 .

[17]  Benjamin Alexandrovich,et al.  Measurement of electron energy distribution in low-pressure RF discharges , 1992 .

[18]  C. Steinbrüchel.  Universal energy dependence of physical and ion-enhanced chemical etch yields at low ion energy , 1989 .

[19]  H. F. Winters,et al.  Ion- and electron-assisted gas-surface chemistry—An important effect in plasma etching , 1979 .