In view of poor resin flexibility and easy to fall off of diamond grits during manufacturing process of single layer UV-curing resin diamond wire saw, a novel manufacturing approach of double layer UV-curing resin diamond wire saw is put forward. During the manufacturing process, a layer of UV-curing resin with a good pliability and strong binding ability is uniformly coated on the core wire surface, then it is cured by the UV light. After that, a layer of UV-curing resin containing diamond grits is coated on the wire surface coated with resin. Another curing is conducted by the UV light. Then the double layer UV-curing resin diamond wire saw is manufactured. The cutting experiments of single and double layer UV-curing resin diamond wire saw are performed for silicon ingot at a single wire sawing machine. Experimental results show that the cutting efficiency of double layer UV-curing resin diamond wire saw is up to 26mm2/min. Compared with single layer UV-curing resin diamond wire saw, lower kerf loss and damage are found, which means a higher utilizing rate of silicon material is achieved. Surface roughness reduces from Ra4.595μm to Ra1.031μm. The cutting performance of double layer UV-curing resin diamond wire saw improves significantly.
[1]
Mahendra Singh,et al.
Reaching a Kerf Loss Below 100 µm by Optimizing the Relation between Wire Thickness and Abrasive Size for Multi-Wire Sawing
,
2009
.
[2]
M. Key.
Research and Application on the Bonding Mechanism of the Photosensitive Resin Blade
,
2006
.
[3]
Hao Wu,et al.
Wire sawing technology: A state-of-the-art review
,
2016
.
[4]
Haedo Jeong,et al.
Multi-wire sawing of sapphire crystals with reciprocating motion of electroplated diamond wires
,
2013
.
[5]
David L. Marshall,et al.
Structural identification of hindered amine light stabilisers in coil coatings using electrospray ionisation tandem mass spectrometry.
,
2010,
Journal of mass spectrometry : JMS.