Porous Thermoplastic Molded Regenerated Silk Crosslinked by the Addition of Citric Acid

Thermoplastic molded regenerated silk fibroin was proposed as a structural material in tissue engineering applications, mainly for application in bone. The protocol allows us to obtain a compact non-porous material with a compression modulus in the order of a Giga Pascal in dry conditions (and in the order of tens of MPa in wet conditions). This material is produced by compressing a lyophilized silk fibroin powder or sponge into a mold temperature higher than the glass transition temperature. The main purpose of the produced resin was the osteofixation and other structural applications in which the lack of porosity was not an issue. In this work, we introduced the use of citric acid in the thermoplastic molding protocol of silk fibroin to obtain porosity inside the structural material. The citric acid powder during the compression acted as a template for the pore formation. The mean pore diameter achieved by the addition of the higher amount of citric acid was around 5 μm. In addition, citric acid could effectively crosslink the silk fibroin chain, improving its mechanical strength. This effect was proved both by evaluating the compression modulus (the highest value recorded was 77 MPa in wet conditions) and by studying the spectra obtained by Fourier transform infrared spectroscopy. This protocol may be applied in the near future to the production of structural bone scaffolds.

[1]  Chenjing Yang,et al.  Bioinspired Tough and Strong Fibers with Hierarchical Core–Shell Structure , 2022, Advanced Materials Interfaces.

[2]  A. Motta,et al.  Use of Bombyx mori silk fibroin in tissue engineering: From cocoons to medical devices, challenges, and future perspectives. , 2022, Biomaterials advances.

[3]  Zhenyu Wang,et al.  An injectable and photocurable methacrylate-silk fibroin hydrogel loaded with bFGF for spinal cord regeneration , 2022, Materials & Design.

[4]  Ozgun Can Onder,et al.  Self-assembled silk fibroin hydrogels: From preparation to biomedical applications , 2022, Materials Advances.

[5]  D. Maniglio,et al.  A genipin crosslinked silk fibroin monolith by compression molding with recovering mechanical properties in physiological conditions , 2021, Cell Reports Physical Science.

[6]  N. Pugno,et al.  Tidy dataset of the experimental design of the optimization of the alkali degumming process of Bombyx mori silk , 2021, Data in brief.

[7]  D. Weitz,et al.  Attractive Pickering Emulsion Gels , 2021, Advanced materials.

[8]  N. Pugno,et al.  A Design of Experiment Rational Optimization of the Degumming Process and Its Impact on the Silk Fibroin Properties. , 2021, ACS biomaterials science & engineering.

[9]  B. Zuo,et al.  Functional silk fibroin hydrogels: preparation, properties and applications. , 2021, Journal of materials chemistry. B.

[10]  H. Mirzadeh,et al.  Crosslinking strategies for silk fibroin hydrogels: promising biomedical materials , 2020, Biomedical materials.

[11]  S. Inoue,et al.  Fabrication of Silk Resin with High Bending Properties by Hot-Pressing and Subsequent Hot-Rolling , 2020, Materials.

[12]  P. Guerrero,et al.  The Effect of Cross-Linking with Citric Acid on the Properties of Agar/Fish Gelatin Films , 2020, Polymers.

[13]  Rui Xia,et al.  Effect of citric acid induced crosslinking on the structure and properties of potato starch/chitosan composite films , 2019 .

[14]  A. Quaranta,et al.  Preparation and Statistical Characterization of Tunable Porous Sponge Scaffolds using UV Cross-linking of Methacrylate-Modified Silk Fibroin. , 2019, ACS biomaterials science & engineering.

[15]  A. Quaranta,et al.  A Thermal‐Reflow‐Based Low‐Temperature, High‐Pressure Sintering of Lyophilized Silk Fibroin for the Fast Fabrication of Biosubstrates , 2019, Advanced Functional Materials.

[16]  D. Kaplan,et al.  Thermoplastic Molding of Regenerated Silk , 2019, Nature Materials.

[17]  Wuchao Wang,et al.  A comparative study of ultrasonic degumming of silk sericin using citric acid, sodium carbonate and papain , 2019, Coloration Technology.

[18]  Y. Tamada,et al.  Preparation of silk resins by hot pressing Bombyx mori and Eri silk powders. , 2019, Materials science & engineering. C, Materials for biological applications.

[19]  Chris Holland,et al.  The Biomedical Use of Silk: Past, Present, Future , 2018, Advanced healthcare materials.

[20]  Wei Xue,et al.  Controlled Release of BMP-2 from a Heparin-Conjugated Strontium-Substituted Nanohydroxyapatite/Silk Fibroin Scaffold for Bone Regeneration. , 2018, ACS biomaterials science & engineering.

[21]  A. Motta,et al.  Silk Fibroin Porous Scaffolds Loaded with a Slow-Releasing Hydrogen Sulfide Agent (GYY4137) for Applications of Tissue Engineering. , 2018, ACS biomaterials science & engineering.

[22]  K. Hofman,et al.  Intra-fibrillar citric acid crosslinking of marine collagen electrospun nanofibres. , 2018, International journal of biological macromolecules.

[23]  A. Quaranta,et al.  A comparative study of the refractive index of silk protein thin films towards biomaterial based optical devices , 2018 .

[24]  D. Maniglio,et al.  Silk fibroin porous scaffolds by N2O foaming , 2018, Journal of biomaterials science. Polymer edition.

[25]  H. Kim,et al.  Silk scaffolds in bone tissue engineering: An overview. , 2017, Acta biomaterialia.

[26]  A. Quaranta,et al.  Fabrication of Nanoscale Patternable Films of Silk Fibroin Using Benign Solvents , 2017 .

[27]  David L Kaplan,et al.  Programming function into mechanical forms by directed assembly of silk bulk materials , 2016, Proceedings of the National Academy of Sciences.

[28]  David Kumar,et al.  Crosslinking of agarose bioplastic using citric acid. , 2016, Carbohydrate polymers.

[29]  Z. Shao,et al.  Physically Crosslinked Biocompatible Silk‐Fibroin‐Based Hydrogels with High Mechanical Performance , 2016 .

[30]  Keita Ito,et al.  Silk fibroin as biomaterial for bone tissue engineering. , 2016, Acta biomaterialia.

[31]  Yiqi Yang,et al.  Low-temperature crosslinking of proteins using non-toxic citric acid in neutral aqueous medium: Mechanism and kinetic study , 2015 .

[32]  Sijie Tao,et al.  Differences in regenerated silk fibroin prepared with different solvent systems: From structures to conformational changes , 2015 .

[33]  L. Ambrosio,et al.  Effect of citric acid crosslinking cellulose-based hydrogels on osteogenic differentiation. , 2015, Journal of biomedical materials research. Part A.

[34]  Jaworski C. Capricho,et al.  Citric acid crosslinking of paper products for improved high-humidity performance. , 2014, Carbohydrate polymers.

[35]  Thushara J. Athauda,et al.  In situ citric acid crosslinking of alginate/polyvinyl alcohol electrospun nanofibers , 2013 .

[36]  H. Tao,et al.  Protein‐Protein Nanoimprinting of Silk Fibroin Films , 2013, Advanced materials.

[37]  Rangam Rajkhowa,et al.  Silk fibroin biomaterials for tissue regenerations. , 2013, Advanced drug delivery reviews.

[38]  David L Kaplan,et al.  Salt-leached silk scaffolds with tunable mechanical properties. , 2012, Biomacromolecules.

[39]  A. Ramadan,et al.  Citric acid used as a crosslinking agent for the grafting of chitosan onto woolen fabric , 2012 .

[40]  Haiyan Wu,et al.  Structure and properties of composites compression‐molded from silk fibroin powder and waterborne polyurethane , 2012 .

[41]  T. Hashimoto,et al.  Characterization of a Silk-Resinified Compact Fabricated Using a Pulse-Energizing Sintering Device , 2012 .

[42]  C. Cao,et al.  Optimization of macroporous 3-D silk fibroin scaffolds by salt-leaching procedure in organic solvent-free conditions , 2012, Journal of Materials Science: Materials in Medicine.

[43]  N. Reddy,et al.  Low-Temperature Wet-Cross-linking of Silk with Citric Acid , 2011 .

[44]  Majibur Rahman Khan,et al.  Physical properties and dyeability of silk fibers degummed with citric acid. , 2010, Bioresource technology.

[45]  N. Reddy,et al.  Citric acid cross-linking of starch films , 2010 .

[46]  B. Mandal,et al.  Non-bioengineered silk fibroin protein 3D scaffolds for potential biotechnological and tissue engineering applications. , 2008, Macromolecular bioscience.

[47]  David L. Kaplan,et al.  Determining Beta-Sheet Crystallinity in Fibrous Proteins by Thermal Analysis and Infrared Spectroscopy , 2006 .

[48]  Yasushi Tamada,et al.  New process to form a silk fibroin porous 3-D structure. , 2005, Biomacromolecules.

[49]  David L Kaplan,et al.  Porous 3-D scaffolds from regenerated silk fibroin. , 2004, Biomacromolecules.

[50]  I. Um,et al.  The role of formic acid in solution stability and crystallization of silk protein polymer. , 2003, International journal of biological macromolecules.

[51]  T. Park,et al.  A novel fabrication method of macroporous biodegradable polymer scaffolds using gas foaming salt as a porogen additive. , 2000, Journal of biomedical materials research.