Fatigue Failure by In-line Flow-induced Vibration and Fatigue Life Evaluation

The phenomenon of fatigue failure by the In-line flow-induced vibration was studied. A newly water-flow-induced vibration system was made and used to reproduce fatigue failure by flow-induced vibration. A medium carbon steel specimen was fixed to the experimental equipment. A small artificial hole was introduced onto the specimen surface. Fatigue crack initiated from the artificial hole. A small portable strain histogram recorder (Mini Rainflow Corder, MRC) developed in another project of the authors' team was used to acquire the service strain histogram at a critical point of the specimen and to measure the variation of natural frequency. Cumulative fatigue damage D defined by the Modified Miner Rule was calculated by using the strain histogram at the initial stage of test. The value of D was almost unity in the case of In-line vibration, while the values of D in the case of the Cross-flow vibration ranged from 0.2 to 0.8.