Immobilization of MSWI fly ash through geopolymerization: effects of water-wash.

The present research explored the role played by water-wash on geopolymerization for the immobilization and solidification of municipal solid waste incineration (MSWI) fly ash. The water-wash pretreatment substantially promoted the early strength of geopolymer and resulted in a higher ultimate strength compared to the counterpart without water-wash. XRD pattern of water-washed fly ash (WFA) revealed that NaCl and KCl were nearly eliminated in the WFA. Aside from geopolymer, ettringite (Ca(6)Al(2)(SO(4))(3)(OH)(12)·26H(2)O) was formed in MSWI fly ash-based geopolymer (Geo-FA). Meanwhile, calcium aluminate hydrate (Ca(2)Al(OH)(7)·3H(2)O), not ettringite, appeared in geopolymer that was synthesized with water-washed fly ash (Geo-WFA). Leached Geo-WFA (Geo-WFA-L) did not exhibit any signs of deterioration, while there was visual cracking on the surface of leached Geo-FA (Geo-FA-L). The crack may be caused by the migration of K(+), Na(+), and Cl(-) ions outside Geo-FA and the negative effect from crystallization of expansive compounds can not be excluded. Furthermore, transformation of calcium aluminate hydrate in Geo-WFA to ettringite in Geo-WFA-L allowed the reduction of the pore size of the specimen. IR spectrums suggested that Geo-WFA can supply more stable chemical encapsulation for heavy metals. Static monolithic leaching tests were conducted for geopolymers to estimate the immobilization efficiency. Heavy metal leaching was elucidated using the first-order reaction/diffusion model. Combined with the results from compressive strength and microstructure of samples, the effects of water-wash on immobilization were inferred in this study.

[1]  J. Deventer,et al.  The effects of inorganic salt contamination on the strength and durability of geopolymers , 2002 .

[2]  J.S.J. van Deventer,et al.  Effect of Al source and alkali activation on Pb and Cu immobilisation in fly-ash based “geopolymers” , 2004 .

[3]  S. Hansen,et al.  Expansive properties of ettringite in a mixture of calcium aluminate cement, Portland cement and β-calcium sulfate hemihydrate , 2001 .

[4]  J. V. Deventer,et al.  Effects of Anions on the Formation of Aluminosilicate Gel in Geopolymers , 2002 .

[5]  Katrien Audenaert,et al.  Chloride binding of cement-based materials subjected to external chloride environment – A review , 2009 .

[6]  T. Bakharev,et al.  Durability of Geopolymer Materials in Sodium and Magnesium Sulfate Solutions , 2005 .

[7]  Raymond John Hodges,et al.  Using inorganic polymer to reduce leach rates of metals from brown coal fly ash , 2004 .

[8]  Zhang Yunsheng,et al.  Synthesis and heavy metal immobilization behaviors of slag based geopolymer. , 2007, Journal of hazardous materials.

[9]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[10]  Jianzhong Xu,et al.  Study on the factors of affecting the immobilization of heavy metals in fly ash-based geopolymers , 2006 .

[11]  J. Deventer,et al.  Structural reorganisation of class F fly ash in alkaline silicate solutions , 2002 .

[12]  Hua Xu,et al.  Effect of Curing Temperature and Silicate Concentration on Fly-Ash-Based Geopolymerization , 2006 .

[13]  G. H. Frischat,et al.  Initial stages of glass corrosion in water , 1990 .

[14]  J.S.J. van Deventer,et al.  Effect of the Alkali Metal Activator on the Properties of Fly Ash-Based Geopolymers , 1999 .

[15]  Sifeng Liu,et al.  Influence of Slag as Additive on Compressive Strength of Fly Ash-Based Geopolymer , 2007 .

[16]  P. K. Mehta,et al.  Hydration Characteristics and Properties of Shrinkage-Compensating Cements , 1973 .

[17]  David S. Kosson,et al.  An Integrated Framework for Evaluating Leaching in Waste Management and Utilization of Secondary Materials , 2002 .

[18]  C. Cremisini,et al.  Digestion methods for analysis of fly ash samples by atomic absorption spectrometry , 1999 .

[19]  J. Phair,et al.  Effect of the silicate activator pH on the microstructural characteristics of waste-based geopolymers , 2002 .

[20]  B. Felekoglu,et al.  Effects of limestone replacement ratio on the sulfate resistance of Portland limestone cement mortars exposed to extraordinary high sulfate concentrations , 2009 .

[21]  J. Deventer,et al.  Reaction mechanisms in the geopolymeric conversion of inorganic waste to useful products. , 2007, Journal of hazardous materials.

[22]  D. Calabrese,et al.  Hydration Behaviour of Mixtures of Cement and Fly Ash with High Sulphate and Chloride Content , 2000 .

[23]  Kazuyuki Suzuki,et al.  Leaching characteristics of stabilized/solidified fly ash generated from ash-melting plant. , 2008, Chemosphere.

[24]  H.A.F. Dehwah,et al.  Effect of sulfate concentration and associated cation type on concrete deterioration and morphological changes in cement hydrates , 2007 .