Electrochemical instabilities due to pitting corrosion of iron

Electrochemical instabilities induced by chlorides and bromides due to pitting corrosion of iron in sulfuric acid solutions are investigated. Analysis of the electrochemical instabilities as a function of the applied potential and the nature and concentration of the aggressive chemical species shows that the system exhibits a transition from aperiodic bursting of large-amplitude to small-amplitude chaotic oscillations at a critical potential (bifurcation potential, Ebif). The Ebif is determined by the halide concentration inside the pits and coincides with the repassivation potential defined in corrosion studies to explain pit repassivation due to changes in pit chemistry. Surface observations show that, at E < Ebif, an active-passive state dissolution (etching) occurs, while at E > Ebif, a polishing state dissolution is reached. Spatial interactions between early initiated pits and the adjacent electrode surface, oxide film alteration, aggressive species accumulation around active pits, and formation of ferrous salt layers in front of the Fe electrode are all considered to be associated with electrochemical instabilities emerging during pitting corrosion of iron under different dissolution states.

[1]  N. Sato.  Anodic Breakdown of Passive Films on Metals , 1982 .

[2]  D. Sazou,et al.  On the mechanism initiating bursting oscillatory patterns during the pitting corrosion of a passive rotating iron-disc electrode in halide-containing sulphuric acid solutions , 1998 .

[3]  J. L. Hudson,et al.  On the Franck‐FitzHugh Model of the Dynamics of Iron Electrodissolution in Sulfuric Acid , 1990 .

[4]  M. Janik-Czachor,et al.  An Assessment of the Processes Leading to Pit Nucleation on Iron , 1981 .

[5]  M. Pagitsas,et al.  Non-linear dynamics of the passivity breakdown of iron in acidic solutions , 2003 .

[6]  N. Sato.  1989 Whitney Award Lecture: Toward a More Fundamental Understanding of Corrosion Processes , 1989 .

[7]  Jingli Luo,et al.  Effect of interface chloride ion perturbation on oscillatory electrodissolution , 2005 .

[8]  H. Engell.  Stability and breakdown phenomena of passivating films , 1977 .

[9]  N. Sato.  The stability of localized corrosion , 1995 .

[10]  M. Pagitsas,et al.  The influence of chloride ions on the dynamic characteristics observed at the transition between corrosion and passivation states of an iron electrode in sulphuric acid solutions , 1992 .

[11]  J. Yorke,et al.  Crises, sudden changes in chaotic attractors, and transient chaos , 1983 .

[12]  A. Pinkowski.  About a critical thickness of the passive layer on iron at the flade potential , 1986 .

[13]  A. D. Davydov,et al.  Oscillatory convective instability in electrochemical systems , 1998 .

[14]  Grebogi,et al.  Critical exponent of chaotic transients in nonlinear dynamical systems. , 1986, Physical review letters.

[15]  D. R. Rosseinsky,et al.  Electrode Potentials and Hydration Energies. Theories and Correlations , 1965 .

[16]  M. Pagitsas,et al.  ELECTROCHEMICAL CURRENT OSCILLATIONS DURING LOCALIZED CORROSION OF IRON , 2003 .

[17]  M. Pagitsas,et al.  Distinction between general and pitting corrosion based on the nonlinear dynamical response of passive iron surfaces perturbed chemically by halides , 2001 .

[18]  M. Pagitsas,et al.  Complex periodic and chaotic current oscillations related to different states of the localized corrosion of iron in chloride-containing sulfuric acid solutions , 2000 .

[19]  J. Newman,et al.  Anodic Dissolution of Iron in Acidic Sulfate Electrolytes II . Mathematical Model of Current Oscillations Observed under Potentiostatic Conditions , 1986 .

[20]  Brian W. Johnson,et al.  Practical considerations of the ir attenuated-total-reflection (ir-ATR) technique for electrochemical investigations , 1992 .

[21]  D. Sazou,et al.  Morphological surface changes of the Fe electrodissolution in 2M H2SO4 during bursting oscillations induced by Br , 1996 .

[22]  A. Pearlstein,et al.  Electrodissolution Kinetics of Iron in Chloride Solutions VIII . Chaos in Potential/Current Oscillations , 1971 .

[23]  T. Fahidy,et al.  Recent Advances in the Study of the Dynamics of Electrode Processes , 1995 .

[24]  D. Macdonald.  The Point Defect Model for the Passive State , 1992 .

[25]  N. Sato.  The Stability of Pitting Dissolution of Metals in Aqueous Solution , 1982 .

[26]  M. Pagitsas,et al.  Generalized Hopf, saddle-node infinite period bifurcations and excitability during the electrodissolution and passivation of iron in a sulfuric acid solution , 1993 .

[27]  G. Frankel.  Pitting Corrosion of Metals A Review of the Critical Factors , 1998 .

[28]  J. Newman,et al.  Periodic Behavior in the Iron/Sulfuric Acid System , 1995 .

[29]  M. Toney,et al.  Atomic Structure of the Passive Oxide Film Formed on Iron , 1997 .

[30]  J. L. Hudson,et al.  Electrochemical Reaction Dynamics - A Review , 1994 .

[31]  J. L. Hudson,et al.  Origins of Persistent Interaction among Localized Corrosion Sites on Stainless Steel , 2004 .

[32]  M. Pagitsas,et al.  Current oscillations induced by chlorides during the passive–active transition of iron in a sulfuric acid solution , 1999 .

[33]  M. Pagitsas,et al.  Bursting and beating current oscillatory phenomena induced by chloride ions during corrosion/passivation of iron in sulphuric acid solutions , 1993 .

[34]  P. Marcus,et al.  Corrosion Mechanisms in Theory and Practice , 1995 .

[35]  N. Sato.  Interfacial ion-selective diffusion layer and passivation of metal anodes , 1996 .

[36]  A. Pearlstein,et al.  Global and Conditional Stability of the Steady and Periodic Solutions of the Franck‐FitzHugh Model of Electrodissolution of Fe in H 2 SO 4 , 1989 .

[37]  Z. Szklarska‐Śmiałowska.  Review of Literature on Pitting Corrosion Published Since 1960 , 1971 .

[38]  A. Arvia,et al.  The Potentiostatic Current Oscillations at Iron/Sulfuric Acid Solution Interfaces , 1979 .

[39]  D. Macdonald.  Passivity–the key to our metals-based civilization , 1999 .

[40]  M. Pagitsas,et al.  A point defect model for the general and pitting corrosion on iron∣oxide∣electrolyte interface deduced from current oscillations , 2003 .

[41]  M. Pagitsas,et al.  Chemical perturbation of the passive-active transition state of Fe in a sulfuric acid solution by adding halide ions. Current oscillations and stability of the iron oxide film , 2000 .

[42]  M. Pagitsas,et al.  General and pitting corrosion deduced from current oscillations in the passive–active transition state of the Fe ∣ H2SO4 electrochemical system , 2002 .

[43]  R. P. Frankenthal,et al.  Passivity of Metals , 1980 .

[44]  Xuelin Wang,et al.  Electrodissolution Kinetics of Iron in Chloride Solutions VII . Experimental Potential/Current Oscillations , 1990 .

[45]  Brian E. Conway,et al.  Modern Aspects of Electrochemistry , 1974 .

[46]  Ralph G. Pearson,et al.  HARD AND SOFT ACIDS AND BASES , 1963 .

[47]  S. M. Sharland,et al.  A review of the theoretical modelling of crevice and pitting corrosion , 1987 .