Evaluation of the fracture toughness properties of polytetrafluoroethylene

Polytetrafluoroethylene (PTFE) (Dupont Tradename Teflon) is a common polymer with many structural applications including sheet, gaskets, bearing pads, piston rings and diaphragms. The interest here developed because this polymer is being considered as the major component of a newly proposed `reactive' material with a possible application as a projectile to replace common inertial projectiles. Little mechanical property data is available on this material since it is commonly used only as a coating material with the dominant properties being its low friction coefficient and high application temperature. Previous work (Joyce, 2003) on commercially available sheet PTFE material has demonstrated the applicability of the normalization method of ASTM E1820 (1999), the elastic-plastic fracture toughness standard to develop fracture toughness properties of this material over a range of test temperatures and loading rates. Additional work on the aluminum filled `reactive' derivative of the basic PTFE polymer (Joyce and Joyce, 2004) has also recently been completed. In this work, standard ASTM E1820 fracture toughness specimens machined from sintered pucks of PTFE were tested at four test temperatures and at a range of test rates to determine the JIc and J resistance curve characteristics of the PTFE material. The major results are that while crack extension is difficult at standard laboratory loading rates at ambient (21 °C) temperature or above, for temperatures slightly below ambient or for elevated loading rates, a rapid degradation of fracture resistance occurs and cracking occurs in a ductile or even nearly brittle manner.

[1]  John D. Landes,et al.  The load separation criterion and methodology in ductile fracture mechanics , 1991 .

[2]  C. Bernal,et al.  On the applicability of the load separation criterion to acrylonitrile/butadiene/styrene terpolymer resins , 1996 .

[3]  Direct Evaluation of J-Resistance Curves from Load Displacement Records , 1980 .

[4]  J. Williams,et al.  Fracture characterization of tough polymers using the J method , 1986 .

[5]  J. Landes,et al.  Normalization Method for Developing J-R Curves with the LMN Function , 1991 .

[6]  J. Landes,et al.  APPLICATION OF A NORMALIZATION METHOD FOR DETERMINING J-R CURVES IN GLASSY POLYMER PVC AT DIFFERENT CROSSHEAD SPEEDS , 1997 .

[7]  J. Williams,et al.  J-integral studies of crack initiation of a tough high density polyethylene , 1993, International Journal of Fracture.

[8]  J. Williams,et al.  J testing of toughened nylons , 1987 .

[9]  P. Montemartini,et al.  The use of load separation criterion and normalization method in ductile fracture characterization of thermoplastic polymers , 1996 .

[10]  J. Joyce Analysis of a high rate round robin based on proposed Annexes to ASTM E 1820 , 2001 .

[11]  C. Bernal,et al.  A simple method for J-R curve determination in ABS polymers , 1995 .

[12]  J. Landes,et al.  J-R curve calculation with the normalization method for toughened polymers , 1994 .

[13]  J. Williams,et al.  Determination of J Ic for Polymers Using the Single Specimen Method , 1991 .

[14]  J. Joyce Fracture toughness evaluation of polytetrafluoroethylene , 2003 .

[15]  J. Landes,et al.  Application of load separation and normalization methods for polycarbonate materials , 1993 .