Finite Element Modelling of Composite Materials and Structures
暂无分享,去创建一个
Constantinos Soutis | Frank L. Matthews | F. L. Matthews | D. Hitchings | G. A. O. Davies | D. Hitchings | Constantinos Soutis | G. Davies
[1] N. J. Pagano,et al. Influence of the free edge upon the strength of angle-ply laminates , 1973 .
[2] S. Tang,et al. A variational approach to edge stresses of circular cutouts in composites , 1979 .
[3] B. Harris,et al. Fatigue and accumulation of damage in reinforced plastics , 1977 .
[4] D. E. Cooper,et al. The Effects of Pin Elasticity, Clearance, and Friction on the Stresses in a Pin-Loaded Orthotropic Plate , 1987 .
[5] Norman A. Fleck,et al. Static Compression Failure of Carbon Fibre T800/924C Composite Plate with a Single Hole , 1990 .
[6] T. Adam,et al. An empirical fatigue-life model for high-performance fibre composites with and without impact damage , 1999 .
[7] Leif Asp,et al. Delamination buckling and growth for delaminations at different depths in a slender composite panel , 2001 .
[8] F. L. Matthews,et al. The strength of bolted joints in glass fibre/epoxy laminates , 1985 .
[9] R. Talreja,et al. Fatigue of composite materials: damage mechanisms and fatigue-life diagrams , 1981, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.
[10] Zvi Hashin,et al. Analysis of cracked laminates: a variational approach , 1985 .
[11] Chien-Chang Lin,et al. Method for Calculating the Interlaminar Stresses in Symmetric Laminates Containing a Circular Hole , 1991 .
[12] D. Purslow,et al. Some fundamental aspects of composites fractography , 1981 .
[13] M. Kanninen,et al. A finite element calculation of stress intensity factors by a modified crack closure integral , 1977 .
[14] Seng-Chuan Tan,et al. Stress Concentrations in Laminated Composites , 1994 .
[15] Chang-Seon Hong,et al. PAPERS : Three - Dimensional Finite Element Analysis of Interlaminar Stresses in Thick Composite Laminates , 1990 .
[16] F. L. Matthews,et al. A review of the strength of joints in fibre-reinforced plastics. Part 2. Adhesively bonded joints , 1982 .
[17] L. J. Hart-Smith,et al. Mechanically-Fastened Joints for Advanced Composites — Phenomenological Considerations and Simple Analyses , 1980 .
[18] K. Schulte. DEVELOPMENT OF MICRODAMAGE IN COMPOSITE LAMINATES DURING FATIGUE LOADING , 1983 .
[19] J. Eisenmann,et al. Macroscopic Fracture Mechanics of Advanced Composite Materials , 1971 .
[20] S. G. Lekhnit︠s︡kiĭ. Theory of elasticity of an anisotropic body , 1981 .
[21] K. J. Pascoe,et al. The behaviour of single-lap bolted joints in CFRP laminates , 1986 .
[22] S. Ogin,et al. Application of the Paris Equation to the Fatigue Growth of Transverse Ply Cracks , 1989 .
[23] S. Gali,et al. Two-Dimensional Interlaminar Stress Distribution within the Adhesive Layer of a Symmetrical Doubler Model , 1977 .
[24] Asd Wang,et al. A Stochastic Model for the Growth of Matrix Cracks in Composite Laminates , 1984 .
[25] Ozcan Konur,et al. Effect of the properties of the constituents on the fatigue performance of composites: a review , 1989 .
[26] P. Camanho,et al. Application of numerical methods to the strength prediction of mechanically fastened joints in composite laminates , 1999 .
[27] P. Beaumont,et al. The failure of fibre composites: An overview , 1989 .
[28] Z. Hashin. Failure Criteria for Unidirectional Fiber Composites , 1980 .
[29] V. Murti,et al. A universal optimum quarter point element , 1986 .
[30] E. F. Rybicki,et al. Effect of Stacking Sequence and Lay-Up Angle on Free Edge Stresses Around a Hole in a Laminated Plate Under Tension , 1978 .
[31] F. L. Matthews,et al. Predicting Progressive Delamination of Composite Material Specimens via Interface Elements , 1999 .
[32] George A. Kardomateas,et al. An introduction to fatigue in metals and composites , 1996 .
[33] Costas Soutis,et al. Analysis of multiple matrix cracking in [±θm/90n]s composite laminates. Part 1: In-plane stiffness properties , 1992 .
[34] Pedro P. Camanho,et al. Stress analysis and strength prediction of mechanically fastened joints in FRP: A review , 1997 .
[35] M. M. Mikulas,et al. Effects of Orthotropy and Width on the Compression Strength of Graphite-Epoxy Panels with Holes , 1984 .
[36] Costas Soutis,et al. Analysis of multiple matrix cracking in [±θm/90n]s composite laminates. Part 2: Development of transverse ply cracks , 1992 .
[37] N. J. Pagano,et al. On the Calculation of Interlaminar Normal Stress in Composite Laminate , 1974 .
[38] Sam Tang,et al. Interlaminar Stresses of Uniformly Loaded Rectangular Composite Plates , 1976 .
[39] B. L. Agarwal. Static Strength Prediction of Bolted Joint in Composite Material , 1980 .
[40] N. J. Pagano,et al. Influence of End Constraint in the Testing of Anisotropic Bodies , 1968 .
[41] MINISTRY OF DEFENCE,et al. The Strength of Bolted Joints in Multi-Directional CFRP Laminates , 1975 .
[42] Costas Soutis,et al. Strain energy release rate associated with local delamination in cracked composite laminates , 1994 .
[43] K. Berg. PROBLEMS IN THE DESIGN OF JOINTS AND ATTACHMENTS , 1970 .
[44] N. Pagano,et al. Exact Solutions for Rectangular Bidirectional Composites and Sandwich Plates , 1970 .
[45] F. L. Matthews,et al. A Finite Element Analysis of Single and Two-Hole Bolted Joints in Fibre Reinforced Plastic , 1981 .
[46] P T Curtis,et al. The fatigue behaviour of fibrous composite materials , 1989 .
[47] Fz Hu,et al. A 3-D failure analysis of scarf patch repaired CFRP plates , 1998 .
[48] Kenneth Reifsnider,et al. Fracture of fatigue-loaded composite laminates , 1982 .
[49] J. G. Williams,et al. The mixed-mode delamination of fibre composite materials , 1993 .
[50] H. A. Evensen,et al. Interlaminar Shear in Laminated Composites Under Generalized Plane Stress , 1970 .
[51] A.S.D. Wang,et al. Some New Results on Edge Effect in Symmetric Composite Laminates , 1977 .
[52] Ramesh Talreja,et al. A continuum mechanics characterization of damage in composite materials , 1985, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.
[53] Jacob Aboudi,et al. Stiffness reduction of cracked solids , 1987 .
[54] E. Dill,et al. Theory of Elasticity of an Anisotropic Elastic Body , 1964 .
[55] James M. Whitney,et al. Free-Edge Delamination of Tensile Coupons , 1972 .
[56] R. Nuismer,et al. Constitutive Relations of a Cracked Composite Lamina , 1988 .
[57] Charles E.S. Ueng,et al. Stresses Around a Pin-loaded Hole in Orthotropic Plates , 1984 .
[58] R. Jamison. The role of microdamage in tensile failure of graphite/epoxy laminates☆ , 1985 .
[59] P. T. Curtis,et al. On the transverse cracking and longitudinal splitting behaviour of glass and carbon fibre reinforced epoxy cross ply laminates and the effect of Poisson and thermally generated strain , 1979, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.
[60] J. Whitney,et al. Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations , 1974 .
[61] N. J. Pagano,et al. The Influence of Stacking Sequence on Laminate Strength , 1971 .
[62] A. W. Leissa,et al. Analysis of Heterogeneous Anisotropic Plates , 1969 .
[63] William M. Murray,et al. Fatigue and fracture of metals , 1952 .
[64] Kenneth Reifsnider,et al. Characterization and Analysis of Damage Mechanisms in Tension-Tension Fatigue of Graphite/Epoxy Laminates , 1984 .
[65] K. Reifsnider,et al. Internal Load Distribution Effects During Fatigue Loading of Composite Laminates , 1986 .
[66] T. K. Obrien,et al. Analysis of local delaminations and their influence on composite laminate behavior , 1985 .
[67] N. J. Pagano,et al. Interlaminar Stresses in Composite Laminates—An Approximate Elasticity Solution , 1974 .
[68] Norman A. Fleck,et al. Failure Prediction Technique for Compression Loaded Carbon Fibre-Epoxy Laminate with Open Holes , 1991 .
[69] J. Whitney,et al. Free-Edge Effects in the Characterization of Composite Materials , 1973 .
[70] O. L. Bowie. Analysis of an Infinite Plate Containing Radial Cracks Originating at the Boundary of an Internal Circular Hole , 1956 .
[71] N. Laws,et al. Stiffness changes in unidirectional composites caused by crack systems , 1983 .
[72] Constantinos Soutis,et al. Interlaminar stresses in composite laminates with a circular hole , 1997 .
[73] A. Levy,et al. Finite-Element Analysis of Interlaminar Shear in Fibrous Composites , 1971 .
[74] Charles E. Harris,et al. A Cumulative Damage Model for Continuous Fiber Composite Laminates with Matrix Cracking and Interply Delaminations , 1988 .
[75] R. Pipes,et al. Moiré Analysis of the Interlaminar Shear Edge Effect in Laminated Composites , 1971 .
[76] T. O'Brien. Characterization of delamination onset and growth in a composite laminate , 1982 .
[77] John H. Crews,et al. Interlaminar stress singularities at a straight free edge in composite laminates , 1981 .
[78] L. Ingvar Eriksson,et al. Contact stresses in bolted joints of composite laminates , 1986 .
[79] M. Ashby,et al. The fatigue damage mechanics of a carbon fibre composite laminate: I—development of the model , 1986 .
[80] A.S.D. Wang,et al. The Dependence of Transverse Cracking and Delamination on Ply Thickness in Graphite/Epoxy Laminates , 1982 .
[81] Ramesh Talreja,et al. Fatigue of composite materials , 1987 .
[82] R. J. Nuismer,et al. A Theory for Progressive Matrix Cracking in Composite Laminates , 1989 .
[83] N. J. Pagano,et al. Interlaminar Stresses in Composite Laminates Under Uniform Axial Extension , 1970 .
[84] Ramesh Talreja,et al. Damage development in composites: Mechanisms and modelling , 1989 .
[85] N. Pagano,et al. Exact Solutions for Composite Laminates in Cylindrical Bending , 1969 .
[86] Costas Soutis,et al. Effects of matrix cracking and hygrothermal stresses on the strain energy release rate for edge delamination in composite laminates , 1994 .
[87] Gretchen B. Murri,et al. Characterization of Mode I and Mode II delamination growth and thresholds in AS4/PEEK composites , 1990 .
[88] F. L. Matthews,et al. Stress distribution around a single bolt in fibre-reinforced plastic , 1982 .
[89] J. Tong,et al. On matrix crack growth in quasi-isotropic laminates—I. Experimental investigation , 1997 .
[90] F. Chang,et al. A Progressive Damage Model for Laminated Composites Containing Stress Concentrations , 1987 .
[91] Constantinos Soutis,et al. Progressive Matrix Cracking in Composite Laminates Loaded in Tension , 1992 .
[92] C. Kassapoglou,et al. An Efficient Method for the Calculation of Interlaminar Stresses in Composite Materials , 1986 .
[93] T. A. Collings,et al. On the bearing strengths of cfrp laminates , 1982 .
[94] T. Adam,et al. A Power Law Fatigue Damage Model for Fibre-Reinforced Plastic Laminates , 1986 .
[95] E. F. Rybicki,et al. Approximate Three-Dimensional Solutions for Symmetric Laminates Under Inplane Loading * , 1971 .
[96] Kenneth Reifsnider,et al. Stiffness-reduction mechanisms in composite laminates , 1982 .