Sustained damage and remaining useful life assessment in leadfree electronics subjected to sequential multiple thermal environments

Field deployed electronics us often subjected to a combination of thermal aging and thermal cycling. The thermal cycle magnitudes may vary over the lifetime of the product. Long-life systems may be re-deployed several times over the use life of the product. Aging has been previously shown to effect the reliability and constitutive behaviour of second-level leadfree interconnects. Often the equipment may not have any macro-indicators of damage such as cracks or delamination. The ability to identify impending failures in systems and their sub-components has great potential to mitigate the risks of unanticipated failures and reduce the support costs. The presented approach in this paper is intended to address the need for tools and techniques for prognosticating the prior accrued damage and the remaining useful life of the product prior to redeployment. Leadfree assemblies with Sn3Ag0.5Cu solder have been subjected to various duration-combinations of thermal aging at 125°C, thermal cycling from -40°C to 125°C and thermal cycling from 0°C to 100°C. The presented methodology uses leading indicators of failure based on micro-structural evolution of damage to identify accrued damage in electronic systems subjected to sequential stresses of thermal aging and thermal cycling. Leading indicators studied in this paper include the phase growth parameter and the intermetallic thickness. Damage equivalency relationships have been developed to map damage accrued in thermal aging to the reduction in thermo-mechanical cyclic life based on damage proxies. Accrued damage between different thermal cyclic magnitudes has also been mapped for -40°C to 125°C and 0°C to 100°C thermal cycles. The presented method for interrogation of the accrued damage for the field deployed electronics, significantly prior to failure, may allow insight into the damage initiation and progression of the deployed system. The expected error with interrogation of system state and assessment of residual life has been quantified.

[1]  P. Lall,et al.  Damage mechanics of electronics on metal-backed substrates in harsh environments , 2006, IEEE Transactions on Components and Packaging Technologies.

[2]  D. D. Morrison.  Methods for nonlinear least squares problems and convergence proofs , 1960 .

[3]  P. Lall,et al.  Feature extraction and health monitoring using image correlation for survivability of leadfree packaging under shock and vibration , 2008, EuroSimE 2008 - International Conference on Thermal, Mechanical and Multi-Physics Simulation and Experiments in Microelectronics and Micro-Systems.

[4]  K. Goebel,et al.  Assessment of residual damage in leadfree electronics subjected to multiple thermal environments of thermal aging and thermal cycling , 2010, 2010 Proceedings 60th Electronic Components and Technology Conference (ECTC).

[5]  Parker,et al.  Design for Testability—A Survey , 1982, IEEE Transactions on Computers.

[6]  J. Lee,et al.  Feature extraction and damage-precursors for prognostication of lead-free electronics , 2006, ECTC 2006.

[7]  Manolis I. A. Lourakis.  A Brief Description of the Levenberg-Marquardt Algorithm Implemented by levmar , 2005 .

[8]  Y. Zorian.  A structured testability approach for multi-chip modules based on BIST and boundary-scan , 1994 .

[9]  Michael Pecht,et al.  In-situ sensors for product reliability monitoring , 2002, Symposium on Design, Test, Integration, and Packaging of MEMS/MOEMS.

[10]  R. Boudreau.  Foreword contributions from the 50th electronic components and technology conference , 2001 .

[11]  P. Lall,et al.  Health monitoring for damage initiation & progression during mechanical shock in electronic assemblies , 2006, 56th Electronic Components and Technology Conference 2006.

[12]  P. Lall,et al.  Prognostics Health Monitoring (PHM) for Prior-Damage Assessment in Electronics Equipment under Thermo-Mechanical Loads , 2007, 2007 Proceedings 57th Electronic Components and Technology Conference.

[13]  P. Lall,et al.  Statistical Pattern Recognition and Built-in Reliability Test for Feature Extraction and Health Monitoring of Electronics under Shock Loads , 2009, 2007 Proceedings 57th Electronic Components and Technology Conference.

[14]  Pradeep Lall,et al.  Explicit submodeling and digital image correlation based life-prediction of leadfree electronics under shock-impact , 2009, 2009 59th Electronic Components and Technology Conference.

[15]  P. Lall,et al.  Health Monitoring for Damage Initiation and Progression During Mechanical Shock in Electronic Assemblies , 2008, IEEE Transactions on Components and Packaging Technologies.

[16]  P. Lall,et al.  Algorithms for prognostication of prior damage and residual life in lead-free electronics subjected to thermo-mechanical loads , 2008, 2008 11th Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems.

[17]  K. Goebel,et al.  Interrogation of system state for damage assessment in lead-free electronics subjected to thermo-mechanical loads , 2008, 2008 58th Electronic Components and Technology Conference.

[18]  K. Goebel,et al.  Resistance spectroscopy-based condition monitoring for prognostication of high reliability electronics under shock-impact , 2009, 2009 59th Electronic Components and Technology Conference.

[19]  R. Drees,et al.  Role of BIT in support system maintenance and availability , 2004, IEEE Aerospace and Electronic Systems Magazine.

[20]  P. Lall,et al.  Solder-joint reliability in electronics under shock and vibration using explicit finite-element sub-modeling , 2006, 56th Electronic Components and Technology Conference 2006.

[21]  P. Lall,et al.  Leading indicators-of-failure for prognosis of electronic and MEMS packaging , 2004, 2004 Proceedings. 54th Electronic Components and Technology Conference (IEEE Cat. No.04CH37546).

[22]  Pradeep Lall,et al.  Prognostication of latent damage and residual life in leadfree electronics subjected to multiple thermal-environments , 2009, 2009 59th Electronic Components and Technology Conference.

[23]  Benoit Nadeau-Dostie,et al.  BIST of PCB interconnects using boundary-scan architecture , 1992, IEEE Trans. Comput. Aided Des. Integr. Circuits Syst..

[24]  P. Lall,et al.  Prognostication and health monitoring of leaded and lead free electronic and MEMS packages in harsh environments , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[25]  P. Lall,et al.  Models for Reliability Prediction of Fine-Pitch BGAs and CSPs in Shock and Drop-Impact , 2004, IEEE Transactions on Components and Packaging Technologies.

[26]  D. Rosenthal,et al.  Predicting and eliminating built-in test false alarms , 1990 .

[27]  R. Chandramouli,et al.  Testing systems on a chip , 1996 .

[28]  D. Allen.  Probabilities associated with a built-in-test system, focus on false alarms , 2003, Proceedings AUTOTESTCON 2003. IEEE Systems Readiness Technology Conference..

[29]  Pradeep Lall,et al.  The effects of SAC alloy composition on aging resistance and reliability , 2009, 2009 59th Electronic Components and Technology Conference.

[30]  P. Lall,et al.  Model for BGA and CSP reliability in automotive underhood applications , 2004, IEEE Transactions on Components and Packaging Technologies.

[31]  Kaj Madsen,et al.  Methods for Non-Linear Least Squares Problems , 1999 .

[32]  P. Lall,et al.  Prognostics and Health Management of Electronic Packaging , 2006, IEEE Transactions on Components and Packaging Technologies.

[33]  Pradeep Lall,et al.  Smeared-Property Models for Shock-Impact Reliability of Area-Array Packages , 2007 .

[34]  P. Lall,et al.  Failure-Envelope Approach to Modeling Shock and Vibration Survivability of Electronic and MEMS Packaging , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[35]  Thomas W. Williams.  Design for Testability , 1982, 19th Design Automation Conference.

[36]  Pradeep Lall,et al.  Fault-mode classification for health monitoring of electronics subjected to drop and shock , 2009, 2009 59th Electronic Components and Technology Conference.