The Effect of Cold Expansion on the Fatigue Life of the Chamfered Holes

The cold expansion method is one of the most popular techniques in the fatigue enhancement processes, and it has been widely used as a means of improving the fatigue resistance for aircraft structures with holes. Cold expanded holes have lower compressive residual stresses on the entry surface rather than the middle and exit surfaces. Due to the nonuniform residual stress distribution, fatigue crack initiation often occurs on the entry surface. This study proposes a new approach to increase the compressive residual stress magnitude at the entry of the hole. The new method is to apply chamfers into holes before the cold expansion process. Split mandrel process was used to cold work the hole with and without chamfers. Both numerical and experimental studies were done to verify the effects of hole chamfers on the residual stress distribution of the cold expanded holes. Finite element analysis (FEA) was conducted in order to see the effects of the chamfer geometries on the residual stress distributions. The FEA results showed an improvement of compressive residual stress magnitudes at the entry position of the cold expanded hole. The numerical results were compared with X-ray diffraction measurements. Fatigue tests were done to compare the fatigue life of the holes with various chamfer sizes and angles. The cold expansion chamfered holes showed a clear improvement in fatigue life over cold expanded holes without chamfers.

[1]  Lf Impellizzeri,et al.  Fatigue Analysis of Cold-Worked and Interference Fit Fastener Holes , 1977 .

[2]  A. Dias,et al.  Residual Stresses around an Expanded Hole in an Aluminum Clad Sheet , 2005 .

[3]  P.M.S.T. de Castro,et al.  Residual stress effect on fatigue striation spacing in a cold-worked rivet hole , 2004 .

[4]  Cgc Poussard,et al.  A finite element simulation of the cold working process for fastener holes , 1997 .

[5]  Chang-Sung Seok,et al.  Finite element analysis of the residual stress by cold expansion method under the influence of adjacent holes , 2004 .

[6]  R. C. McClung,et al.  A literature survey on the stability and significance of residual stresses during fatigue , 2007 .

[7]  Jidong Kang,et al.  Three-Dimensional Finite Element Analysis of the Cold Expansion of Fastener Holes in Two Aluminum Alloys , 2002 .

[8]  Cheol Kim,et al.  Analysis of Residual Stresses Induced by Cold Expansion Using Finite Element Method , 2002 .

[9]  R. Hermann,et al.  Three-dimensional stress distribution around cold expanded holes in aluminium alloys , 1994 .

[10]  Dl Ball,et al.  Experimental investigation on the effects of cold expansion of fastener holes , 1998 .

[11]  Jeffrey Vogwell,et al.  A novel method of cold expansion which creates near‐uniform compressive tangential residual stress around a fastener hole , 2004 .

[12]  Shaker A. Meguid,et al.  Three-dimensional finite element analysis of cold expansion of adjacent holes , 1998 .

[13]  L. Edwards,et al.  RELAXATION OF RESIDUAL STRESSES AT COLD‐WORKED FASTENER HOLES DUE TO FATIGUE LOADING , 1997 .

[14]  Abdelwaheb Amrouche,et al.  Cold expansion effect on the initiation and the propagation of the fatigue crack , 2003 .

[15]  M. J. Pavier,et al.  Prediction of the growth rate for fatigue cracks emanating from cold expanded holes , 2004 .

[16]  Gérard Mesmacque,et al.  Fatigue life estimation after crack repair in 6005 A-T6 aluminium alloy using the cold expansion hole technique , 2000 .