Crack growth in single-crystal silicon

Crack growth in single-crystal silicon at room temperature in air was evaluated by double torsion (DT) load-relaxation method and monitored by acoustic emission (AE) technique.

[1]  S. Freiman,et al.  Prediction of Flaw Sizes from Acoustic Emission Measurements in Ceramics , 1976 .

[2]  L. D. Pye,et al.  Introduction to Glass Science , 1972 .

[3]  C. P. Chen,et al.  Stress Rate and Proof‐Testing of Silicon Wafers , 1985 .

[4]  James R. Rice,et al.  Ductile versus brittle behaviour of crystals , 1974 .

[5]  V. Fréchette.  The Fractology of Glass , 1972 .

[6]  Anthony G. Evans,et al.  Slow crack growth in brittle materials under dynamic loading conditions , 1974 .

[7]  Albert S. Kobayashi,et al.  Fracture Mechanics Applied to Brittle Materials , 1979 .

[8]  S. Wiederhorn,et al.  Stress Corrosion and Static Fatigue of Glass , 1970 .

[9]  D. Thompson,et al.  Review of Progress in Quantitative Nondestructive Evaluation , 1982 .

[10]  S. Bhaduri,et al.  Slow Crack Growth Studies in Silicon , 1983 .

[11]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .

[12]  A. Evans,et al.  Fracture Mechanics of Ceramics , 1986 .

[13]  W. J. Knapp,et al.  The Fracture of Single-Crystal Silicon Under Several Liquid Environments , 1980 .

[14]  Anthony Kelly,et al.  Ductile and brittle crystals , 1967 .

[15]  L. Russell,et al.  Acoustic emission and crack propagation in polycrystalline alumina , 1974 .

[16]  T. Michalske,et al.  A Molecular Mechanism for Stress Corrosion in Vitreous Silica , 1983 .

[17]  Sw Freiman,et al.  Determination of Fracture Mechanics Parameters Through Fractographic Analysis of Ceramics , 1979 .

[18]  Anthony G. Evans,et al.  Influence of a Tangential Force on the Fracture of Two Contacting Elastic Bodies , 1983 .

[19]  E. Fuller,et al.  An Evaluation of Double-Torsion Testing—Experimental , 1979 .

[20]  S. W. Wiederhorn.  Environmental Stress Corrosion Cracking of Glass , 1971 .