Effect of elevated temperature on alkali-activated geopolymeric binders compared to portland cement-based binders

Abstract This research focused on developing thermally-stable materials based on alkali-activation of slag, fly ash, and metakaolin compared to portland cement mixtures by using a hierarchical approach to material design. At lower length scales, X-ray diffraction (XRD) characterized the mineralogy that coupled to higher length scale experiments using thermogravimetric analysis (TGA) for determining the materials thermal stability. Additionally, high-energy X-ray computed microtomography (μCT) determined the best-performing material formulation that minimized thermal damage when exposed to high temperatures (650 °C). The thermal loading was ramped up to 650 °C from ambient temperature in 60 s and then held for a total of 10 min. The μCT identified that the alkali-activated fly ash mortar had less initial porosity than the ordinary portland cement mixtures, with more than 66% of the pores between 20 and 50 μm in diameter. Consequently, the alkali-activated fly ash mortar was able to dissipate approximately 565 °C in just 50 mm of material, outperforming all the other mixes studied in this paper with μCT confirming minimal damage after the temperature exposure.

[1]  W. Rickard,et al.  Performance of solid and cellular structured fly ash geopolymers exposed to a simulated fire , 2014 .

[2]  J. Sanjayan,et al.  Effect of transient creep on compressive strength of geopolymer concrete for elevated temperature exposure , 2014 .

[3]  P. D. Arumairaj,et al.  Optimum mix for the geopolymer concrete , 2012 .

[4]  C. Weiss,et al.  Improvement in the geopolymer-to-steel bond using a reactive vitreous enamel coating , 2013 .

[5]  Ángel Palomo,et al.  Corrosion resistance in activated fly ash mortars , 2005 .

[6]  Jay G. Sanjayan,et al.  Geopolymer and Portland cement concretes in simulated fire , 2011 .

[7]  O. Es-Said,et al.  The effects of heat damage of aluminum 6061-T6 AM-2 Mats and High Power Run-Up Anchor , 2011 .

[8]  Nicholas J. Carino,et al.  FIRE PERFORMANCE OF HIGH STRENGTH CONCRETE: RESEARCH NEEDS. APPLIED TECHNOLOGY IN STRUCTURAL ENGINEERING , 2000 .

[9]  B. Vijaya Rangan,et al.  ON THE DEVELOPMENT OF FLY ASH-BASED GEOPOLYMER CONCRETE , 2004 .

[10]  Kwesi Sagoe-Crentsil,et al.  Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures , 2007 .

[11]  Kenneth J. D. MacKenzie,et al.  Thermal behaviour of inorganic geopolymers and composites derived from sodium polysialate , 2003 .

[12]  Faris Ali,et al.  Explosive spalling of high-strength concrete columns in fire , 2001 .

[13]  Kwesi Sagoe-Crentsil,et al.  Factors affecting the performance of metakaolin geopolymers exposed to elevated temperatures , 2008 .

[14]  J. Deventer,et al.  Geopolymer technology: the current state of the art , 2007 .

[15]  Jay G. Sanjayan,et al.  Damage behavior of geopolymer composites exposed to elevated temperatures , 2008 .

[16]  Jay G. Sanjayan,et al.  Effect of elevated temperatures on geopolymer paste, mortar and concrete , 2010 .

[17]  Francisca Puertas,et al.  MECHANICAL AND DURABLE BEHAVIOUR OF ALKALINE CEMENT MORTARS REINFORCED WITH POLYPROPYLENE FIBRES , 2003 .

[18]  T. Cheng,et al.  Fire-resistant geopolymer produced by granulated blast furnace slag , 2003 .

[19]  J. Davidovits.  Geopolymer chemistry and applications , 2008 .

[20]  K. MacKenzie,et al.  Synthesis and thermal behaviour of potassium sialate geopolymers , 2003 .

[21]  이종규,et al.  Geopolymer의 현황과 전망 , 2006 .

[22]  Ali Nadjai,et al.  Assessment of the Susceptibility of Normal and High Strength Concrete for Explosive Spalling , 2004 .

[23]  T. Bakharev,et al.  Thermal behaviour of geopolymers prepared using class F fly ash and elevated temperature curing , 2006 .

[24]  P. Allison,et al.  Nanoindentation and SEM/EDX characterization of the geopolymer-to-steel interfacial transition zone for a reactive porcelain enamel coating , 2015 .

[25]  P. Balaguru,et al.  Functional Geopolymer Composites for Structural Ceramic Applications , 2006 .

[26]  Ángel Palomo,et al.  Composition and Microstructure of Alkali Activated Fly Ash Binder: Effect of the Activator , 2005 .

[27]  Ailar Hajimohammadi,et al.  Time-resolved and spatially-resolved infrared spectroscopic observation of seeded nucleation controlling geopolymer gel formation. , 2011, Journal of colloid and interface science.