Effect of temperature, steam-to-carbon ratio, and alkali metal additives on improving the sulfur tolerance of a Rh/La–Al2O3 catalyst reforming gasoline for fuel cell applications

Abstract 2 wt% Rh/La–Al 2 O 3 was tested for autothermal reforming (ATR) of S-free and 34 ppm-S-gasoline and characterized by scanning electron microscopy, elemental analyses, surface area, CO chemisorption, DRIFTS and X-ray absorption spectroscopy. The poisoning effect of S was more pronounced during ATR at 700 °C than at 800 °C. Complete recovery of the initial activity could be achieved when switching from S-containing gasoline to S-free gasoline at 800 °C, while only 50% of the activity could be recovered at 700 °C. Sulfur increased Rh sintering due to an increase in the catalyst temperature caused by a greater inhibition of steam reforming than partial oxidation. An increase in the H 2 O:C from 2.0 to 3.0, or the addition of K to Rh significantly enhanced the sulfur tolerance of the catalysts. The beneficial effect of temperature, steam, and alkali metal was attributed to the inhibition of coke, which was the major cause of catalyst deactivation.

[1]  Alan M. Lane,et al.  Catalytic autothermal reforming of diesel fuel for hydrogen generation in fuel cells: I. Activity tests and sulfur poisoning , 2005 .

[2]  Shudong Wang,et al.  Autothermal reforming of gasoline on Rh-based monolithic catalysts , 2007 .

[3]  P. Cheekatamarla,et al.  Catalytic autothermal reforming of diesel fuel for hydrogen generation in fuel cells: II. Catalyst poisoning and characterization studies , 2006 .

[4]  M. D. Amiridis,et al.  FTIR studies of CO adsorption on Rh-Ge/Al2O3 catalysts prepared by surface redox reactions. , 2004, Langmuir : the ACS journal of surfaces and colloids.

[5]  P. Griffiths,et al.  Diffuse Reflectance FT-IR Studies of the Adsorption of CO on Rh/Al2O3 Catalysts , 1987 .

[6]  Krister Sjöström,et al.  Sulfur-Deactivated Steam Reforming of Gasified Biomass , 1998 .

[7]  Daniel J. Haynes,et al.  Catalytic partial oxidation of n-tetradecane in the presence of sulfur or polynuclear aromatics: Effects of support and metal , 2006 .

[8]  M Newville,et al.  ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. , 2005, Journal of synchrotron radiation.

[9]  Luca Basini,et al.  In Situ EXAFS Study of Rh/Al2O3 Catalysts for Catalytic Partial Oxidation of Methane , 2001 .

[10]  A. Azad,et al.  Development of ceria-supported sulfur tolerant nanocatalysts: Rh-based formulations , 2007 .

[11]  Ienwhei Chen,et al.  Resistivity to sulfur poisoning of nickel-alumina catalysts , 1988 .

[12]  M. Illán-Gómez,et al.  Effect of potassium content in the activity of K-promoted Ni/Al2O3 catalysts for the dry reforming of methane , 2006 .

[13]  C. H. Bartholomew,et al.  Sulfur Poisoning of Metals , 1982 .

[14]  Daniel Duprez,et al.  Effect of sulphur on the coking of rhodium in the steam reforming of 1-methylnaphthalene , 1989 .

[15]  Chunshan Song.  An overview of new approaches to deep desulfurization for ultra-clean gasoline, diesel fuel and jet fuel , 2003 .

[16]  S. Goto,et al.  Partial Oxidation of Methane on Supported Nickel Catalysts , 1999 .

[17]  Jens R. Rostrup-Nielsen,et al.  Activity of nickel catalysts for steam reforming of hydrocarbons , 1973 .

[18]  C. Garland,et al.  Infrared Studies of Carbon Monoxide Chemisorbed on Rhodium , 1957 .

[19]  C. H. Bartholomew.  Mechanisms of catalyst deactivation , 2001 .

[20]  J. Odriozola,et al.  Influence of alkali additives on activity and toxicity of H2S and thiophene over a Ni/SiO2 catalyst , 1998 .