Strained epilayers effectively reduce plasma-induced fluorine damage in P-HEMTs

We intentionally inserted several strained epilayers, namely In/sub 0.5/Ga/sub 0.5/As, InAs, and InSb, as fluorine-trapping barriers in a conventional pseudomorphic high electron mobility transistor (P-HEMT) structure and investigated their effectiveness against plasma-induced fluorine damage using Hall measurements and secondary ion mass spectrometry (SIMS) analysis. The strained barriers effectively diminished plasma-induced fluorine incorporation into deeper layers than the /spl delta/-doped layer and improved the carrier density and electron mobility compared with those of the conventional P-HEMT. In particular, when the most strained InSb barrier was inserted into the P-HEMT using post-thermal annealing, the carrier density and electron mobility remarkably recovered to 85% and 97% of their respective values before processing because of diminished fluorine incorporation and reduction of incorporated fluorine from the channel layer to the upper layers. This confirms that highly strained barriers are very effective at suppressing plasma-induced fluorine damage in P-HEMTs.

[1]  T. Ohno,et al.  Fluorine atoms in AlAs, GaAs, and InAs: Stable state, diffusion, and carrier passivation , 2000 .

[2]  Y. Su,et al.  Photoreflectance and C-V Measurement Investigations of Dry Etched Gate Recesses for GaInP/InGaAs/GaAs Pseudomorphic High Electron Mobility Transistors (HEMTs) Using BCl3/Ar Plasma. , 1997 .

[3]  U. Mishra,et al.  AlGaAs/GaAs high electron mobility transistor with a low-temperature grown GaAs ion damage blocking layer , 1997 .

[4]  T. Mishima,et al.  Improved photoluminescence properties of highly strained InGaAs/GaAs quantum wells grown by molecular‐beam epitaxy , 1995 .

[5]  M. Kudo,et al.  Dry Etching Damage and Activation Ratio Degradation in δ-Doped AlGaAs/InGaAs High Electron Mobility Transistors , 1994 .

[6]  A. Furukawa.  Dependence of electron accumulation in AlSb/InAs quantum well on thin surface materials of InAs and GaSb , 1993 .

[7]  Ohno.  Reactions of Cl with GaAs: A theoretical understanding of GaAs-surface etching. , 1991, Physical review. B, Condensed matter.

[8]  F. Ren,et al.  Dry etch processing of GaAs/AlGaAs high electron mobility transistor structures , 1991 .

[9]  K. Kuhn,et al.  Selective etching of GaAs and Al0.30Ga0.70As with citric acid/hydrogen peroxide solutions , 1990 .

[10]  M. Kudo,et al.  Control of plasma induced fluorine damage in P-HEMT using InSb barrier layer , 2004, 16th IPRM. 2004 International Conference on Indium Phosphide and Related Materials, 2004..

[11]  Hiroyuki Uchiyama,et al.  Plasma-Induced Fluorine Damage in P-HEMT Caused by C2F6/CHF3 RIE Plasma , 2004, IEICE Electron. Express.

[12]  Hiroyuki Uchiyama,et al.  Suppression of plasma-induced fluorine damage in P-HEMTs using strained InSb barrier , 2004, IEICE Electron. Express.

[13]  T. Sonoda,et al.  Selective wet etching for highly uniform GaAs/Al0.15Ga0.85As heterostructure field effect transistors , 1997 .

[14]  R. Grundbacher,et al.  Single step lithography for double-recessed gate pseudomorphic high electron mobility transistors , 1997 .

[15]  Takuji Sonoda,et al.  Donor passivation in n-AlInAs layers by fluorine , 1995, Seventh International Conference on Indium Phosphide and Related Materials.

[16]  C. B. Cooper,et al.  Damage studies of dry etched GaAs recessed gates for field effect transistors , 1991 .