Spalling formation mechanism for gears

Though the basic phenomenon of wear on gear tooth contact surfaces is the removal of a piece of material from the working surface, the sizes of the wear debris may be different, due to the different physical causes in their formation processes. No common definitions have been established to distinguish spalling from pitting in the literature. This is probably due to the fact that the physical causes of pitting and spalling have not yet been established. In this paper, a brief literature review is presented with the intention to differentiate spalling from pitting. Three types of wear phenomena are defined. Furthermore, the results of a recent experimental study of gear tooth spalling formation in AISI 4340 gears in a test rig are also presented to demonstrate a possible process of spalling due to the development of cracks beneath the tooth contact surfaces and crack linkages in plastically-collapsed metal ligament between the crack tip and the adjacent tooth contact surface. These experimental results substantiated the ligament collapse spalling mechanism proposed by Ding et al. [Y. Ding, R. Jones, B.T. Kuhnell, Elastic-plastic finite element analysis of spall formation in gears, Wear 197 (1996) 197-205; M. Heems, F. Lagarde, R. Courtel, P. Sorin, C. R. Acad. Sci. 257 (3) (1963) 3293].

[1]  M. D. Bryant,et al.  A Pitting Model for Rolling Contact Fatigue , 1983 .

[2]  Yan Ding,et al.  Numerical analysis of subsurface crack failure beneath the pitch line of a gear tooth during engagement , 1995 .

[3]  G. T. Hahn,et al.  Elasto-plastic finite element analyses of two-dimensional rolling and sliding contact deformation of bearing steel , 1989 .

[4]  J. W. Blake,et al.  A Surface Pitting Life Model for Spur Gears: Part I—Life Prediction , 1991 .

[5]  Lester E. Alban.  Systematic Analysis of Gear Failures , 1985 .

[6]  A. Bower.  The influence of crack face friction and trapped fluid on surface initiated rolling contact fatigue cracks , 1988 .

[7]  Gregory R. Miller,et al.  The Role of Near-Surface Inclusions in the Pitting of Gears , 1985 .

[8]  M. Kaneta,et al.  Growth Mechanism of Subsurface Crack Due to Hertzian Contact , 1986 .

[9]  T. E. Tallian,et al.  Failure atlas for Hertz contact machine elements , 1992 .

[10]  Leon M Keer,et al.  SUBSURFACE AND SURFACE CRACKING DUE TO HERTZIAN CONTACT. , 1982 .

[11]  Nam P. Suh,et al.  Mechanics of crack propagation in delamination wear , 1977 .

[12]  D. C. Stouffer,et al.  Inelastic Deformation of Metals: Models, Mechanical Properties, and Metallurgy , 1996 .

[13]  Carol A. Rubin,et al.  The driving force for mode II crack growth under rolling contact , 1985 .

[14]  M. Kaneta,et al.  Mechanism of Crack Growth in Lubricated Rolling/Sliding Contact , 1985 .

[15]  Yan Ding,et al.  Elastic-plastic finite element analysis of spall formation in gears , 1996 .

[17]  G. T. Hahn,et al.  Finite element modelling of subsurface mode II cracks under contact loads , 1989 .