Growth and characterization of Ga2O3 on sapphire substrates for UV sensor applications

The β-Ga2O3 films were grown on (0001) sapphire at 500 °C by metal organic chemical vapor deposition. In the analysis of crystal structure, we found that the (-201) oriented single crystal β-Ga2O3 epilayer can be obtained under low chamber pressure of 15 torr. Moreover, a metal-semiconductor-metal solar-blind deep ultraviolet photodetector was fabricated with the β-Ga2O3 epilayer. As the bias voltage is 5 V, the photodetector exhibits a relatively low dark current about 0.2 pA, which induced by the highly resistive nature of the β-Ga2O3 thin films. From the responsivity result, it can be observed that photodetector shows a maximum responsivity at 260 nm, revealing the β-Ga2O3 photodetector was really solar-blind. The responsivity of the photodetector was as high as 20.1 A/W with an applied bias of 5 V and an incident light wavelength of 260 nm. The improved performance is attributed to the high quality of β-Ga2O3 epilayer.

[1]  Shinji Nakagomi,et al.  Enhancement of responsivity in solar-blind β-Ga2O3 photodiodes with a Au Schottky contact fabricated on single crystal substrates by annealing , 2009 .

[2]  Takayoshi Oshima,et al.  Ga2O3 Thin Film Growth on c-Plane Sapphire Substrates by Molecular Beam Epitaxy for Deep-Ultraviolet Photodetectors , 2007 .

[3]  Nam Ho Kim,et al.  Annealing effects on the properties of Ga2O3 thin films grown on sapphire by the metal organic chemical vapor deposition , 2004 .

[4]  Phil D. C. King,et al.  Observation of shallow-donor muonium in Ga2O3: Evidence for hydrogen-induced conductivity , 2010 .

[5]  Jens Bauer,et al.  Growth of β‐Ga2O3 on Al2O3 and GaAs using metal‐organic vapor‐phase epitaxy , 2009 .

[6]  Yoshitaka Toyoda,et al.  High Temperature Oxygen Sensor Using a Pt–Ga2O3–Pt Sandwich Structure , 2004 .

[7]  Manijeh Razeghi,et al.  Solar-blind AlGaN photodiodes with very low cutoff wavelength , 2000 .

[8]  Shigeo Fujita,et al.  Molecular Beam Epitaxy of High Magnesium Content Single-Phase Wurzite MgxZn1-xO Alloys (x≃0.5) and Their Application to Solar-Blind Region Photodetectors , 2003 .

[9]  Theeradetch Detchprohm,et al.  Demonstration of Flame Detection in Room Light Background by Solar‐Blind AlGaN PIN Photodiode , 2001 .

[10]  E. Muñoz,et al.  Photoconductive gain modelling of GaN photodetectors , 1998 .

[11]  Hideo Hosono,et al.  Field-induced current modulation in epitaxial film of deep-ultraviolet transparent oxide semiconductor Ga2O3 , 2006 .

[12]  Shinji Nakagomi,et al.  Sol-gel prepared β-Ga2O3 thin films for ultraviolet photodetectors , 2007 .

[13]  James S. Speck,et al.  β-Ga2O3 growth by plasma-assisted molecular beam epitaxya) , 2010 .

[14]  Joel B. Varley,et al.  Oxygen vacancies and donor impurities in β-Ga2O3 , 2010 .

[15]  Yicheng Lu,et al.  GaN and AlGaN metal–semiconductor–metal photodetectors , 1997 .

[16]  Meiyong Liao,et al.  Thermally stable visible-blind diamond photodiode using tungsten carbide Schottky contact , 2005 .

[17]  Takayoshi Oshima,et al.  Vertical Solar-Blind Deep-Ultraviolet Schottky Photodetectors Based on β-Ga2O3 Substrates , 2008 .

[18]  Manijeh Razeghi,et al.  Semiconductor ultraviolet detectors , 1996 .