Identification of Three Trapping Centers in Calcium Tungstate

Partial thermal annealing of nominally pure calcium tungstate, after gamma irradiation at 78 °K, provided evidence for identifying three major 4900 A thermoluminescence peaks at 0.36, 0.55, and 0.72 eV with three groups of electron spin resonance lines of paramagnetic tungsten at g001 = 2.009 and 1.843 and niobium at g001 = 2.021, respectively. The impurity center identified with the paramagnetic Nb+4 ion is assigned to a tungsten site and a NbO complex. Arguments are presented for the assignment of two lattice defect models, a WO complex with nearby WO3 and NbO complexes, and a WO complex with a nearby calcium deficiency, to the paramagnetic (W+5)A and (W+5)B ions, respectively. Teilweise Temperung von gamma-bestrahlten (78 °K), sogenannten reinen CaWO4-Einkristallen ermoglichte die Identifizierung von drei ausgepragten 4900 A Thermolumineszenzmaxima bei 0,36, 0,55 und 0,72 eV mit drei Gruppen von ESR-Spektren, die mit paramagnetischem Wolfram mit g001 = 2,009 und 1,843 bzw. Niobium mit g001 = 2,021 verbunden sind. Die Fremdstorstelle wird als Nb+4 Ion auf Wolfram-Platz identifiziert und einem NbO-Komplex zugeordnet. Argumente fur die Zuordnung der paramagnetischen (W+5)A- bzw. (W+5)B-Ionen zu zwei Eigenstorstellenmodellen, einem WO-Komplex mit benachbarten WO3- und NbO-Komplexen und einem WO-Komplex mit einer benachbarten Kalzium-Fehlstelle, werden angefuhrt.