Temperature and Material Flow Prediction in Friction-Stir Spot Welding of Advanced High-Strength Steel

Friction-stir spot welding (FSSW) has been shown to be capable of joining advanced high-strength steel, with its flexibility in controlling the heat of welding and the resulting microstructure of the joint. This makes FSSW a potential alternative to resistance spot welding if tool life is sufficiently high, and if machine spindle loads are sufficiently low that the process can be implemented on an industrial robot. Robots for spot welding can typically sustain vertical loads of about 8 kN, but FSSW at tool speeds of less than 3000 rpm cause loads that are too high, in the range of 11–14 kN. Therefore, in the current work, tool speeds of 5000 rpm were employed to generate heat more quickly and to reduce welding loads to acceptable levels. Si3N4 tools were used for the welding experiments on 1.2-mm DP 980 steel. The FSSW process was modeled with a finite element approach using the Forge® software. An updated Lagrangian scheme with explicit time integration was employed to predict the flow of the sheet material, subjected to boundary conditions of a rotating tool and a fixed backing plate. Material flow was calculated from a velocity field that is two-dimensional, but heat generated by friction was computed by a novel approach, where the rotational velocity component imparted to the sheet by the tool surface was included in the thermal boundary conditions. An isotropic, viscoplastic Norton-Hoff law was used to compute the material flow stress as a function of strain, strain rate, and temperature. The model predicted welding temperatures to within 4%, and the position of the joint interface to within 10%, of the experimental results.

[1]  G. Grant,et al.  Friction stir spot welding of DP780 carbon steel , 2010 .

[2]  L. Treviño,et al.  Weldability of Martensitic Steel by Resistance Spot Welding a Neural Network Optimization in the Automotive Industry , 2009 .

[3]  N. Tsuji,et al.  Friction stir welding of high carbon steel with excellent toughness and ductility , 2010 .

[4]  A. Reynolds,et al.  Friction stir welding of DH36 steel , 2003 .

[5]  Toru Kato,et al.  Joinability of aluminium alloy and mild steel sheets by self piercing rivet , 2006 .

[6]  H. Kokawa,et al.  Microstructural evolution of ultrahigh carbon steel during friction stir welding , 2007 .

[7]  H. Kokawa,et al.  Characteristics of Microstructure in Ultrahigh Carbon Steel Produced during Friction Stir Welding , 2008 .

[8]  Abdelmageed Elmustafa,et al.  Experimental and numerical investigation of the plunge stage in friction stir welding , 2008 .

[9]  M. Awang,et al.  Energy Generation during Friction Stir Spot Welding (FSSW) of Al 6061-T6 Plates , 2010 .

[10]  M. Pouranvari,et al.  Microstructure and failure behaviour of resistance spot welded DP980 dual phase steel , 2010 .

[11]  A. Gerlich,et al.  Resistance and friction stir spot welding of DP600: A comparative study , 2007 .

[12]  S. Bhole,et al.  Expulsion monitoring in spot welded advanced high strength automotive steels , 2006 .

[13]  K. Nogi,et al.  Friction stir welding of hypereutectoid steel (SK5) below eutectoid temperature , 2009 .

[14]  Michael L Santella,et al.  Friction stir spot welding of hot-stamped boron steel , 2007 .

[15]  Michael Miles,et al.  Comparison of formability of friction stir welded and laser welded dual phase 590 steel sheets , 2006 .