Photocatalytic cementitious materials: influence of the microstructure of cement paste on photocatalytic pollution degradation.

Incorporation of nanophotocatalysts into cementitious materials is an important development in the field of photocatalytic pollution mitigation. In this study, the photocatalytic nitrogen oxides (NO(x)) conversion by titanium dioxide (TiO(2)) blended cement pastes was used as a standard process to evaluate the internal factors that may influence the depollution performance. The chemical composition and microstructure of the TiO(2) modified cement pastes were characterized and analyzed. The active photocatalytic sites related to the surface area of TiO(2) are the key factor in determining the photocatalytic activity. Ordinary Portland cement pastes showed lower photocatalytic activity than white cement pastes probably due to the influence of minor metallic components. X-ray diffraction and thermal gravity analysis demonstrated that TiO(2) was chemically stable in the hydrated cement matrix. The NO(x) removal ability decreased with the increase of curing age. This could be attributed to the cement hydration products which filled up capillary pores forming diffusion barriers to both reactants and photons. It was also proved that surface carbonation could reduce the photocatalytic pollution removal efficiency after the hydration of cement.

[1]  J. Verran,et al.  PHOTOCATALYTIC TITANIA BASED SURFACES: ENVIRONMENTAL BENEFITS , 2008 .

[2]  David A Lange,et al.  Variation of microstructure with carbonation in lime and blended pastes , 2006 .

[3]  Jennifer M. Stokke,et al.  Photocatalytic degradation of methanol using silica-titania composite pellets: effect of pore size on mass transfer and reaction kinetics. , 2008, Environmental science & technology.

[4]  John Bensted,et al.  Hydration of Portland Cement , 1983 .

[5]  Pierre Pichat,et al.  State of the art and perspectives on materials and applications of photocatalysis over TiO2 , 2005 .

[6]  G. Camera-Roda,et al.  Optimization of the thickness of a photocatalytic film on the basis of the effectiveness factor , 2007 .

[7]  G Götz Hüsken,et al.  Experimental study of photocatalytic concrete products for air purification , 2009 .

[8]  Alberto Strini,et al.  Measurement of benzene, toluene, ethylbenzene and o-xylene gas phase photodegradation by titanium dioxide dispersed in cementitious materials using a mixed flow reactor , 2005 .

[9]  Jo Dewulf,et al.  Heterogeneous photocatalytic removal of toluene from air on building materials enriched with TiO2 , 2008 .

[10]  Anita Rachel,et al.  Comparison of photocatalytic efficiencies of TiO2 in suspended and immobilised form for the photocatalytic degradation of nitrobenzenesulfonic acids , 2002 .

[11]  Chi Sun Poon,et al.  Photocatalytic construction and building materials: From fundamentals to applications , 2009 .

[12]  L. De Ceukelaire,et al.  ACCELERATED CARBONATION OF A BLAST-FURNACE CEMENT CONCRETE , 1993 .

[13]  A. K. Ray,et al.  External and internal mass transfer effect on photocatalytic degradation , 2001 .

[14]  R. Herz.  Intrinsic kinetics of first-order reactions in photocatalytic membranes and layers , 2004 .

[15]  N. Moussiopoulos,et al.  Photocatalytic degradation of NOx in a pilot street canyon configuration using TiO2-mortar panels , 2007, Environmental monitoring and assessment.

[16]  Chi Sun Poon,et al.  NO removal efficiency of photocatalytic paving blocks prepared with recycled materials , 2007 .

[17]  Jun Chen,et al.  Photocatalytic activity of titanium dioxide modified concrete materials - influence of utilizing recycled glass cullets as aggregates. , 2009, Journal of environmental management.

[18]  Reinhard Niessner,et al.  Photocatalytic activity of semiconductor-modified cement. Influence of semiconductor type and cement ageing , 2003 .

[19]  A. Fujishima,et al.  TiO2 photocatalysis and related surface phenomena , 2008 .