The Instantaneous Apparent Activation Energy of Cement Hydration Measured Using a Novel Calorimetry‐Based Method

A new calorimetry-based method for calculating the activation energy of cement hydration is described. The method requires a scanning calorimeter that can change the sample temperature relatively quickly and has a stable baseline, but the technique is straightforward to perform. Activation energy values can be calculated at multiple hydration times from a single specimen, allowing any changes with time to be assessed. With this method, the measured activation energy at a given time does not depend on the previous microstructural development, as is the case with traditional methods of calculating the activation energy from parallel specimens hydrated isothermally at different temperatures. For tricalcium silicate (C3S) hydrated in pure water or in a calcium chloride solution, the activation energy remains statistically constant from the earliest times until the degree of hydration exceeds 0.65, with an overall average value of (51.1 ± 1.8) kJ/mol. For cement hydration, the activation energy is also constant until well past the main hydration peak, with slightly lower average values. These results suggest that the rate-controlling step in the hydration process does not change during the early hydration period (the first few days after mixing), as different reaction steps tend to have different activation energies.

[1]  D. Bentz,et al.  In situ quasi-elastic neutron scattering study of the hydration of tricalcium silicate , 1998 .

[2]  Jeffrey J. Thomas,et al.  Effects of D2O and Mixing on the Early Hydration Kinetics of Tricalcium Silicate , 1999 .

[3]  Jeffrey J. Thomas,et al.  A multi-technique investigation of the nanoporosity of cement paste , 2007 .

[4]  Rachel J. Detwiler,et al.  Backscattered electron imaging of cement pastes hydrated at different temperatures , 1990 .

[5]  S. Grant,et al.  Effect of temperature on hydration kinetics and polymerization of tricalcium silicate in stirred suspensions of CaO-saturated solutions , 2006 .

[6]  K. Scrivener,et al.  Studying nucleation and growth kinetics of alite hydration using μic , 2009 .

[7]  J. Tirlocq,et al.  Influence de la temperature de recuit sur la cinetique de l'hydratation du silicate tricalcique , 1982 .

[8]  George W. Scherer,et al.  Effect of Pressure on Early Hydration of Class H and White Cement , 2010 .

[9]  Jie Zhang,et al.  Nucleation and growth models for hydration of cement , 2012 .

[10]  P. Baglioni,et al.  Hydration kinetics of tricalcium silicate by calorimetric methods. , 2011, Journal of colloid and interface science.

[11]  J. Bullard,et al.  Mechanisms of cement hydration , 2011 .

[12]  B. Duthoit,et al.  Determination of apparent activation energy of concrete by isothermal calorimetry , 2000 .

[13]  Jeffrey J. Thomas,et al.  Hydration Kinetics and Microstructure Development of Normal and CaCl2-Accelerated Tricalcium Silicate Pastes , 2009 .

[14]  Jeffrey W. Bullard,et al.  Modeling and simulation of cement hydration kinetics and microstructure development , 2011 .

[15]  A. Bentur,et al.  Structural Properties of Calcium Silicate Pastes: II, Effect of Curing Temperature , 1979 .

[16]  Kyle A. Riding,et al.  Methods for Calculating Activation Energy for Portland Cement , 2007 .

[17]  L. G. Longsworth.  Temperature Dependence of Diffusion in Aqueous Solutions , 1954 .

[18]  Jeffrey J. Thomas,et al.  A New Approach to Modeling the Nucleation and Growth Kinetics of Tricalcium Silicate Hydration , 2007 .

[19]  A. Craievich,et al.  Effects of temperature and of the addition of accelerating and retarding agents on the kinetics of hydration of tricalcium silicate , 2000 .