Impact specimen geometry on T23 and TP347HFG steels behaviour during steam oxidation at harsh conditions

Ferritic T23 steel and austenitic TP347HFG steel have been studied with an emphasis on understanding the impact of specimen geometry on their steam oxidation behaviour. The selected materials were tested over a wide range of temperatures from 600 to 750°C. The tests were carried out in 100% steam conditions for 1000 hours. The tests indicated that the ‘curved-shaped’ specimens show slower mass gain, scale ticking and void nucleation rates than ‘bridge-shaped’ specimens (with flat and convex surfaces combined). Furthermore, a bridge TP347HFG sample showed the formation of lower amount of flaky oxide at 750°C.

[1]  G. G. Stokes "J." , 1890, The New Yale Book of Quotations.

[2]  C. W. Tuck,et al.  The oxidation of iron at 950°C in oxygen/water vapour mixtures , 1969 .

[3]  J. C. Griess,et al.  Long term corrosion of Cr-Mo steels in superheated steam at 482 and 538 C , 1982 .

[4]  B. Lefebvre,et al.  High Temperature Corrosion Behaviour of some Boiler Steels in Pure Water Vapour , 2001 .

[5]  L. Verelst,et al.  Superheater Materials Testing for USC Boilers: Steam Side Oxidation Rate of 9 Advanced Materials in Industrial Conditions , 2001 .

[6]  I. Wright,et al.  An Assessment of the High Temperature Oxidation Behavior of Fe-Cr Steels in Water Vapor and Steam , 2002 .

[7]  A. T. Fry,et al.  Oxidation of alloys in steam environments - a review. , 2002 .

[8]  S. Osgerby,et al.  The influence of laboratory test procedures on scale growth kinetics and microstructure during steam oxidation testing , 2005 .

[9]  M. Igarashi,et al.  10-Year Experience With T23(2.25Cr-1.6W) and T122(12Cr-0.4Mo-2W) in a Power Boiler , 2005 .

[10]  N. Komai,et al.  Japanese experience with steam oxidation of advanced heat-resistant steel tubes in power boilers , 2005 .

[11]  W. Quadakkers,et al.  Steam oxidation of ferritic steels – laboratory test kinetic data , 2005 .

[12]  N. Ōtsuka Fracture behavior of steam-grown oxide scales formed on 2–12%Cr steels , 2005 .

[13]  J. Hald,et al.  Long term steam oxidation of TP 347H FG in power plants , 2005 .

[14]  L. Singheiser,et al.  Enhanced oxidation of the 9%Cr steel P91 in water vapour containing environments , 2006 .

[15]  R. Viswanathan,et al.  Boiler materials for ultra-supercritical coal power plants—Steamside oxidation , 2006 .

[16]  S. Saunders,et al.  Current Understanding of Steam Oxidation - Power Plant and Laboratory Experience , 2006 .

[17]  W. J. Quadakkers,et al.  Implications of steam oxidation for the service life of high-strength martensitic steel components in high-temperature plant , 2007 .

[18]  W. J. Quadakkers,et al.  Mechanisms of steam oxidation in high strength martensitic steels , 2007 .

[19]  Fred Starr,et al.  Some aspects of plant and research experience in the use of new high strength martensitic steel P91 , 2007 .

[20]  Jeff Henry,et al.  Lessons from the past: materials-related issues in an ultra-supercritical boiler at Eddystone plant , 2007 .

[21]  F. Pérez,et al.  Effect of Chromium Content on the Oxidation Behaviour of Ferritic Steels for Applications in Steam Atmospheres at High Temperatures , 2009 .

[22]  I. Wright,et al.  A review of the oxidation behaviour of structural alloys in steam , 2010 .

[23]  J. Nicholls,et al.  Impact specimen geometry on T23 and TP347HFG steels behaviour during steam oxidation at harsh conditions , 2017 .

[24]  Aaas News,et al.  Book Reviews , 1893, Buffalo Medical and Surgical Journal.