Solution-processed lithium-doped zinc oxide thin-film transistors at low temperatures between 100 and 300 °C

Abstract Lithium-doped zinc oxide (Li-ZnO) thin-film transistors (TFTs) were fabricated by solution process at the low temperatures ranged from 100 to 300 °C. Li-ZnO TFTs fabricated at 300 °C under nitrogen condition showed a mobility of 1.2 cm2/Vs. Most importantly, the mobility of Li-ZnO TFT devices fabricated at 100 °C could be increased significantly from 0.08 to 0.4 cm2/Vs by using double spin-coated and UV irradiation-treated Li-ZnO film, and the on-/off-current ratio is in the order of 106. Notably, the XPS analyses proved that the performance improvement was originated from the chemical composition or stoichiometry evolution, in which the hydroxide was converted into metal oxide and accelerated the formation of the oxygen vacancies. Furthermore, low-voltage operating Li-ZnO TFTs were demonstrated by using a high-capacitance ion gel gate dielectrics. The Li-ZnO TFTs with an operating voltage as low as 2 V exhibited the carrier mobilities of 2.1 and 0.65 cm2/Vs for the devices treated at 300 and 100 °C, respectively. The low-temperature, solution-processed Li-ZnO TFTs showed greatly potential applications in flexible displays, smart label, and sensors.

[1]  Wi Hyoung Lee,et al.  High-mobility low-temperature ZnO transistors with low-voltage operation , 2010 .

[2]  Sunho Jeong,et al.  Solution-Processed Zinc Tin Oxide Semiconductor for Thin-Film Transistors , 2008 .

[3]  Mihai Irimia-Vladu,et al.  "Green" electronics: biodegradable and biocompatible materials and devices for sustainable future. , 2014, Chemical Society reviews.

[4]  B. Bae,et al.  High performance solution-processed amorphous zinc tin oxide thin film transistor , 2009 .

[5]  Aram Amassian,et al.  High‐Performance ZnO Transistors Processed Via an Aqueous Carbon‐Free Metal Oxide Precursor Route at Temperatures Between 80–180 °C , 2013, Advanced materials.

[6]  T. Lodge,et al.  “Cut and Stick” Rubbery Ion Gels as High Capacitance Gate Dielectrics , 2012, Advanced materials.

[7]  A. Facchetti,et al.  Role of Gallium Doping in Dramatically Lowering Amorphous‐Oxide Processing Temperatures for Solution‐Derived Indium Zinc Oxide Thin‐Film Transistors , 2010, Advances in Materials.

[8]  H. Sirringhaus,et al.  Low-temperature, high-performance solution-processed metal oxide thin-film transistors formed by a ‘sol–gel on chip’ process. , 2011, Nature materials.

[9]  Kon Yi Heo,et al.  Photosensitivity of solution-based indium gallium zinc oxide single-walled carbon nanotubes blend thin film transistors , 2009 .

[10]  H. Sirringhaus,et al.  High Performance, Low Temperature Solution-Processed Barium and Strontium Doped Oxide Thin Film Transistors , 2013, Chemistry of materials : a publication of the American Chemical Society.

[11]  S. Cho,et al.  Novel Zinc Oxide Inks with Zinc Oxide Nanoparticles for Low-Temperature, Solution-Processed Thin-Film Transistors , 2012 .

[12]  Young-Min Choi,et al.  Metal salt-derived In–Ga–Zn–O semiconductors incorporating formamide as a novel co-solvent for producing solution-processed, electrohydrodynamic-jet printed, high performance oxide transistors , 2013 .

[13]  K. Char,et al.  Patterning of Flexible Transparent Thin‐Film Transistors with Solution‐Processed ZnO Using the Binary Solvent Mixture , 2011 .

[14]  Jooho Moon,et al.  Solution-processable tin-doped indium oxide with a versatile patternability for transparent oxide thin film transistors , 2011 .

[15]  R. McLean,et al.  Transparent ZnO thin-film transistor fabricated by rf magnetron sputtering , 2003 .

[16]  M. Kanatzidis,et al.  Low-temperature fabrication of high-performance metal oxide thin-film electronics via combustion processing. , 2011, Nature materials.

[17]  Chunxiang Zhu,et al.  Solution-processed LiF-doped ZnO films for high performance low temperature field effect transistors and inverted solar cells. , 2013, ACS applied materials & interfaces.

[18]  J. Cho,et al.  The structural, optical and electrical characterization of high-performance, low-temperature and solution-processed alkali metal-doped ZnO TFTs , 2013 .

[19]  Yong-Young Noh,et al.  Flexible metal-oxide devices made by room-temperature photochemical activation of sol–gel films , 2012, Nature.

[20]  Jin-seong Park,et al.  Atomic Layer Deposition ZnO:N Thin Film Transistor: The Effects of N Concentration on the Device Properties , 2010 .

[21]  Sunho Jeong,et al.  Low-temperature, solution-processed metal oxide thin film transistors , 2012 .

[22]  Yongli Gao,et al.  Ion-dependent gate dielectric characteristics of ion-conducting SiO(2) solid-electrolytes in oxide field-effect transistors. , 2014, Physical chemistry chemical physics : PCCP.

[23]  Tae Il Lee,et al.  Low‐Temperature, Solution‐Processed and Alkali Metal Doped ZnO for High‐Performance Thin‐Film Transistors , 2012, Advanced materials.

[24]  John F. Muth,et al.  Room temperature pulsed laser deposited indium gallium zinc oxide channel based transparent thin film transistors , 2007 .

[25]  Marius Grundmann,et al.  One decade of fully transparent oxide thin‐film transistors: fabrication, performance and stability , 2013 .

[26]  Yongli Gao,et al.  Crystal-Domain Orientation and Boundary in Highly Ordered Organic Semiconductor Thin Film , 2015 .