Effect of degassing addition on the solidification segregation of nickel aluminum bronze

The effect of degassing agent addition on the solidification segregation of Nickel Aluminum Bronze was investigated. The complex relationship between the development of the solidification microstructures and buildup of microsegregation in Nickel Aluminum Bronze was obtained by using microstructure analysis and EDS analysis. This experiment describes the characterization of microsegregation in Nickel Aluminum Bronze which was made using point to count microanalysis along the microstructure. With this method, the differences of elements distribution in alloys solidified in the microstructure were clearly evidenced. The results show a microstructure directly affected by segregation of elements in Nickel Aluminum Bronze matrix. There is segregation of elements in the Late To Freeze (LTF) region after solidification from melting. As for degassing treatment, higher degassing addition on the Nickel Aluminum Bronze increased the elements segregation.The effect of degassing agent addition on the solidification segregation of Nickel Aluminum Bronze was investigated. The complex relationship between the development of the solidification microstructures and buildup of microsegregation in Nickel Aluminum Bronze was obtained by using microstructure analysis and EDS analysis. This experiment describes the characterization of microsegregation in Nickel Aluminum Bronze which was made using point to count microanalysis along the microstructure. With this method, the differences of elements distribution in alloys solidified in the microstructure were clearly evidenced. The results show a microstructure directly affected by segregation of elements in Nickel Aluminum Bronze matrix. There is segregation of elements in the Late To Freeze (LTF) region after solidification from melting. As for degassing treatment, higher degassing addition on the Nickel Aluminum Bronze increased the elements segregation.

[1]  H. Masjuki,et al.  Tribology with biodiesel: A study on enhancing biodiesel stability and its fuel properties , 2017 .

[2]  H. Cui,et al.  Effect of phase composition and microstructure on the corrosion resistance of Ni-Al intermetallic compounds , 2017 .

[3]  Mrityunjoy Hazra,et al.  Failure of a nickel aluminium bronze (NAB) canned motor pump impeller working under polluted sea water – Influence of material selection, section thickness dependent microstructure and temper annealing heat treatment , 2016 .

[4]  D. K. Dwivedi,et al.  Study of the effect of friction stir processing of the sliding wear behavior of cast NiAl bronze: A statistical analysis , 2016 .

[5]  Jiazhen Yan,et al.  The microstructure and mechanical properties of 1Cr17Ni2/QAl7 brazed joints using Cu-Mn-Ni-Ag brazing alloy , 2016 .

[6]  Xinping Zhang,et al.  Size effects on tensile strength of aluminum–bronze alloy at room temperature , 2015 .

[7]  M. Shamanian,et al.  Effect of friction stir processing on erosion–corrosion behavior of nickel–aluminum bronze , 2014 .

[8]  A. Manonukul,et al.  Effect of hot working on microstructure evolution of as-cast Nickel Aluminum Bronze alloy , 2014 .

[9]  A. Davoodi,et al.  The role of constituent phases on corrosion initiation of NiAl bronze in acidic media studied by SEM–EDS, AFM and SKPFM , 2014 .

[10]  Yogesh Chandra Sharma,et al.  A critical review on corrosion of compression ignition (CI) engine parts by biodiesel and biodiesel blends and its inhibition , 2012 .

[11]  B. Xiao,et al.  Inhomogeneous microstructure and mechanical properties of friction stir processed NiAl bronze , 2009 .

[12]  Julian A. Wharton,et al.  Erosion and erosion–corrosion performance of cast and thermally sprayed nickel–aluminium bronze , 2005 .

[13]  T. Jayakumar,et al.  Influence of Mean Stress and Defect Distribution on the High Cycle Fatigue Behaviour of Cast Ni-Al Bronze , 2014 .