Optimised NASICON ceramics for Na+ sensing

NASICON dense ceramics were obtained from solid state reaction between SiO2, Na3PO4·12H2O and two different types of zirconia: monoclinic ZrO2 and the yttria-doped tetragonal phase (ZrO2)0.97(Y2O3)0.03. Higher temperatures were needed to obtain dense samples of the yttrium free composition (1265 °C). The electrical conductivity, at room temperature, of the yttria-doped samples sintered at 1230 °C (0.20 S/m) is significantly higher than the value obtained with the material prepared from pure ZrO2. The impedance spectra show that the differences in conductivity are predominantly due to the higher grain boundary resistance of the undoped ceramics, probably due to formation of monoclinic zirconia and glassy phases along the grain boundary. Further improvement of the electrical conductivity could be achieved after optimization of the grain size and density of grain boundaries. A maximum conductivity value of about 0.27 S/m at room temperature was obtained with the yttria-doped samples sintered at 1220 °C for 40 h. Yttria-doped and undoped ceramics were tested as Na+ potentiometric sensors. The detection limit of the yttria-doped sample (10−4 mol/l) was one order of magnitude lower than the obtained with the undoped material.

[1]  R. S. Gordon,et al.  Fabrication and characterization of Nasicon electrolytes , 1981 .

[2]  J. Labrincha,et al.  Monitoring of the corrosion of YSZ by impedance spectroscopy , 1998 .

[3]  P. Colomban,et al.  Well densified nasicon type ceramics, elaborated using sol-gel process and sintering at low temperatures , 1984 .

[4]  P. Colomban.  Gel technology in ceramics, glass-ceramics and ceramic-ceramic composites☆ , 1989 .

[5]  P. Fabry,et al.  Optimization of NASICON composition for Na+ recognition , 1997 .

[6]  R. O. Fuentes,et al.  Processing and electrical properties of NASICON prepared from yttria-doped zirconia precursors , 2001 .

[7]  John Aurie Dean,et al.  Lange's Handbook of Chemistry , 1978 .

[8]  F. Mauvy,et al.  Reactivity of NASICON with water and interpretation of the detection limit of a NASICON based Na(+) ion selective electrode. , 1999, Talanta.

[9]  Toshio Maruyama,et al.  Potentiometric gas sensor for carbon dioxide using solid electrolytes , 1987 .

[10]  N. Yamazoe,et al.  Stability of NASICON-based CO2 sensor under humid conditions at low temperature , 2001 .

[11]  E. Siebert,et al.  Microsensor based on NASICON for the analysis of Na+ in the gingival fluid , 2001 .

[12]  Daniele Mazza,et al.  Conductivity Measurements on Nasicon and Nasicon-modified materials , 1999 .

[13]  H. Hong,et al.  Crystal structures and crystal chemistry in the system Na1+xZr2SixP3−xO12☆ , 1976 .

[14]  P. Taylor,et al.  Characterization of protonically exchanged NASICON , 1991 .

[15]  R. O. Fuentes,et al.  Reaction of NASICON with water , 2001 .

[16]  John B. Goodenough,et al.  Fast Na+-ion transport in skeleton structures , 1976 .

[17]  Takehiko Saiki,et al.  Humidity sensor using NASICON not containing phosphorus , 1991 .

[18]  Mel I. Mendelson,et al.  Average Grain Size in Polycrystalline Ceramics , 1969 .

[19]  T. A. Wheat,et al.  Dependence of the properties of Nasicons on their composition and processing , 1987 .

[20]  Kazunari Kaneyasu,et al.  A carbon dioxide gas sensor based on solid electrolyte for air quality control , 1998 .

[21]  Toshio Maruyama,et al.  Potentiometric sensor for sulfur oxides using nasicon as a solid electrolyte , 1985 .