Damage evolution in GLARE fibre-metal laminate under repeated low-velocity impact tests

An experimental study was performed on the repeated low-velocity impact behaviour of GLARE. Damage evolution in the material constituents was characterised with successive number of impacts. Records were correlated with visual inspection, ultrasound C-scan and chemical etching. The stiffness of the plate varied when cumulating the number of impacts. Damage accumulation was limited thanks to the synthesis of unidirectional composite and metal. The glass/epoxy plies with high elastic tensile strength could withstand several impacts before perforation despite delamination growth in the vicinity of the impacted area. The damage tolerant aluminium layers prevented the penetration of the projectile and avoided the expansion of delamination. This efficient mechanism preserved the structural integrity of GLARE until first aluminium cracking at the non-impacted side. Among the different failure modes, plate deformation absorbed most of the impact energy. The findings will support the development of a generic quasi-static analytical model and numerical methods.

[1]  J. Paik,et al.  Impact perforation of aluminium alloy plates , 2012 .

[2]  Yanxiong Liu,et al.  Low-Velocity Impact on GLARE 5 Fiber-Metal Laminates: Influences of Specimen Thickness and Impactor Mass , 2012 .

[3]  H. Murthy,et al.  Investigation of Repeated Low Velocity Impact Behaviour of GFRP /Aluminium and CFRP /Aluminium Laminates , 2012 .

[4]  H. N. Narasimha Murthy,et al.  Experimental Investigation of Low-Velocity Repeated Impacts on Glass Fiber Metal Composites , 2012, Journal of Materials Engineering and Performance.

[5]  F. Delale,et al.  Effect of repeated impacts on the response of plain-woven hybrid composites , 2010 .

[6]  Yanxiong Liu,et al.  Effects of Constituents and Lay-up Configuration on Drop-Weight Tests of Fiber-Metal Laminates , 2010 .

[7]  Yanxiong Liu,et al.  Drop-weight impact tests and finite element modeling of cast acrylic/aluminum plates , 2009 .

[8]  G. Belingardi,et al.  On the rate of growth and extent of the steady damage accumulation phase in repeated impact tests , 2009 .

[9]  William M. Banks,et al.  An experimental study of damage accumulation in balanced CFRP laminates due to repeated impact , 2008 .

[10]  A. Khatibi,et al.  A study on the manufacturing of Glass-Fiber-Reinforced Aluminum Laminates and the effect of interfacial adhesive bonding on the impact behavior , 2008 .

[11]  Jenn‐Ming Yang,et al.  The impact properties and damage tolerance and of bi-directionally reinforced fiber metal laminates , 2007 .

[12]  René Alderliesten,et al.  Fatigue and damage tolerance issues of GLARE in aircraft structures , 2006 .

[13]  Robin Olsson,et al.  Impact on composite structures , 2004, The Aeronautical Journal (1968).

[14]  G. Caprino,et al.  Low-velocity impact behaviour of fibreglass-aluminium laminates , 2004 .

[15]  Duane M. Revilock,et al.  Impact resistance of lightweight hybrid structures for gas turbine engine fan containment applications , 2003 .

[16]  Jan Willem Gunnink,et al.  Fibre Metal Laminates , 2001 .

[17]  Jan Willem Gunnink,et al.  Fibre metal laminates : an introduction , 2001 .

[18]  B. Liaw,et al.  Impact Damage Mechanisms in Fiber-Metal Laminates , 2001 .

[19]  Stephen R Reid,et al.  Impact behaviour of fibre-reinforced composite materials and structures , 2000 .

[20]  L. J. Greaves,et al.  5 – Damage resistance and tolerance of thick laminated woven roving GFRP plates subjected to low-velocity impact , 2000 .

[21]  A. Vlot,et al.  Impact Damage Resistance of Various Fibre Metal Laminates , 1997 .

[22]  A. Vlot,et al.  Low-velocity impact loading: on fibre reinforced aluminium laminates (ARALL and GLARE) and other aircraft sheet materials , 1993 .

[23]  E. Pasanella.  Digital filtering and acceleration pulse interpretation , 1986 .

[24]  C. Sciammarella,et al.  Response of glass-fiber-reinforced epoxy specimens to high rates of tensile loading , 1973 .