Premature creep failure in strength enhanced high Cr ferritic steels caused by static recovery of tempered martensite lath structures

Abstract The apparent activation energy for rupture life sometimes changes from a high value of short-term creep region “H” to a low value of long-term creep region “L”. This change results in overestimation of rupture life during long-term creep. This is called “premature creep failure”. Premature creep failure has been studied by the evaluation of microstructures of three kinds of Gr. 122 type steels and by paying attention to subgrains recovery of tempered martensite lath structures. Subgrain structures remain unchanged during short-term aging, whereas static recovery of subgrain structure proceeds when diffusion distance during aging becomes sufficiently long. Strain-induced recovery is the dominant recovery mechanism in the short-term creep region, whereas the contribution of static recovery of the subgrain structures proceeds as well as strain-induced recovery in the long-term creep region. Hence, static recovery brings about premature creep failure. Static recovery of the subgrain structures can be evaluated well at all temperatures by hardness measurement of aged microstructures. Static recovery after incubation causes a drop in hardness due to the loss of subgrain boundaries as main obstacles against motion of dislocations. The less serious premature creep failure in 9% Cr steel as compared to that in 12% Cr is related to the slower speed of static recovery of the subgrain structure in 9% Cr steel. The static recovery is caused by the loss of particle pinning mainly due to MX and M 23 C 6 precipitates and controlled by their thermal stability. The spacing of MX does not change considerably after long-term aging for 9 and 10.5% Cr steels. Therefore, the static recovery of dislocation substructure cannot be attributed to the disappearance of MX particles, though the disappearance of MX can accelerate the recovery of the dislocation substructure in 12% Cr steel. The static recovery is controlled by the loss of strengthening due to M 23 C 6 precipitates. The M 23 C 6 spacing increases slowly in the 9% Cr steel, corresponding to the slow static recovery of its tempered martensite lath structure. The stability of M 23 C 6 precipitates may be affected by the change of chemical composition in M 23 C 6 particles during high temperature exposure.

[1]  Michael F. Ashby,et al.  Overview No. 3 Fracture-mechanism maps and their construction for f.c.c. metals and alloys , 1979 .

[2]  Jae Seung Lee,et al.  Causes of breakdown of creep strength in 9Cr-1.8W-0.5Mo-VNb steel , 2006 .

[3]  H. G. Armaki,et al.  Prediction of Breakdown Transition of Creep Strength in Advanced High Cr Ferritic Steels by Hardness Measurement of Aged Structures at High Temperature , 2007 .

[4]  Stuart Holdsworth,et al.  Creep and fracture in high-temperature components—Design and life assessment issues , 2008 .

[5]  Kouichi Maruyama,et al.  Strengthening Mechanisms of Creep Resistant Tempered Martensitic Steel , 2001 .

[6]  A. Strang,et al.  Z phase formation in martensitic 12CrMoVNb steel , 1996 .

[7]  Kouichi Maruyama,et al.  Prevention of the overestimation of long-term creep rupture life by multiregion analysis in strength enhanced high Cr ferritic steels , 2008 .

[8]  Kouichi Maruyama,et al.  Multiregion analysis of creep rupture data of 316 stainless steel , 2007 .

[9]  Peter Hofer,et al.  The Influence of Microstructural Aspects on the Service Behaviour of Advanced Power Plant Steels , 1999 .

[10]  S. Matsuoka,et al.  Contribution of Microstructural Factors to Hardness Change during Creep Exposure in Mod.9Cr-1Mo Steel , 2005 .

[11]  Fujio Abe,et al.  Creep-resistant Steels , 2008 .

[12]  M. Igarashi,et al.  Long-term creep deformation characteristics of advanced ferritic steels for USC power plants , 2007 .

[13]  Koichi Yagi,et al.  Errors of Creep Rupture Life Extrapolated by Time-Temperature Parameter Methods , 1994 .

[14]  W. Blum,et al.  Evolution of microstructure and deformation resistance in creep of tempered martensitic 9–12%Cr–2%W–5%Co steels , 2006 .

[15]  H. G. Armaki,et al.  Creep Damage Evaluation by Hardness in Advanced High Cr Ferritic Steels , 2007 .

[16]  Kouichi Maruyama,et al.  Cr concentration dependence of overestimation of long term creep life in strength enhanced high Cr ferritic steels , 2010 .

[17]  Kouichi Maruyama,et al.  Static recovery of tempered lath martensite microstructures during long-term aging in 9–12% Cr heat resistant steels , 2009 .

[18]  K. Maruyama,et al.  Influence of Data Analysis Method and Allowable Stress Criterion on Allowable Stress of Gr.122 Heat Resistant Steel , 2007 .

[19]  Kazuhiro Kimura,et al.  TTP Diagrams of Z Phase in 9–12% Cr Heat-Resistant Steels , 2007 .

[20]  Ramaswamy Viswanathan,et al.  Damage Mechanisms and Life Assessment of High Temperature Components , 1989 .

[21]  Gunther Eggeler,et al.  The effect of long-term creep on particle coarsening in tempered martensite ferritic steels , 1989 .

[22]  Jacques Besson,et al.  Study of the microstructure of the Grade 91 steel after more than 100,000 h of creep exposure at 600 °C , 2010 .