In situ trench etching and releasing technique of high aspect ratio beams using magnetically enhanced reactive ion etching

This article describes an in situ trench etching and releasing technique to fabricate high aspect-ratio beams for high performance microelectromechanical systems (MEMS) accelerometers using magnetically enhanced reactive ion etching (MERIE) technique. In the conventional process, lateral encroachment due to the release etching is severe underneath the SiO2 etching mask. In this process, the sidewall of the beams was passivated by inhibiting layers formed during the HBr/SiF4/O2 trench etching, and the beams were not attacked by the subsequent SF6 release etching. Auger electron spectroscopy showed the etch inhibiting layer to consist mostly of Si and O. This was also confirmed by x-ray photoelectron spectroscopy as SiOx (1<x<2) was detected as a predominant species. The in situ process eliminated (1) sidewall deposition step and (2) floor etching step of the conventional process. In addition, the dependency of MERIE etching rates on open ratio and pattern size was studied for high aspect-ratio MEMS structu...

[1]  E. V. D. Drift,et al.  Kinetics and crystal orientation dependence in high aspect ratio silicon dry etching , 2000 .

[2]  J. Weigold,et al.  Etching and boron diffusion of high aspect ratio Si trenches for released resonators , 1997 .

[3]  Ivo W. Rangelow,et al.  Dry etching with gas chopping without rippled sidewalls , 1999 .

[4]  V. M. Donnelly,et al.  Composition of trench sidewalls and bottoms for SiO2-masked Si(100) etched in Cl2 plasmas , 2000 .

[5]  D. Vender,et al.  Sidewall passivation during the etching of poly‐Si in an electron cyclotron resonance plasma of HBr , 1994 .

[6]  W. Juan,et al.  Released Si microstructures fabricated by deep etching and shallow diffusion , 1996 .

[7]  Martin A. Schmidt,et al.  Microfabrication and testing of suspended structures compatible with silicon-on-insulator technology , 1999 .

[8]  Hans Loschner,et al.  Reactive ion etching for microelectrical mechanical system fabrication , 1995 .

[9]  C. W. Jurgensen,et al.  Microscopic uniformity in plasma etching , 1992 .

[10]  M. Esashi,et al.  High-rate directional deep dry etching for bulk silicon micromachining , 1995 .

[11]  Stella W. Pang,et al.  Dry etching of Si field emitters and high aspect ratio resonators using an inductively coupled plasma source , 1998 .

[12]  S. Aachboun,et al.  Deep anisotropic etching of silicon , 1999 .

[13]  Ian Ronald Johnston,et al.  Recent advances in silicon etching for MEMS using the ASE™ process , 1999 .

[14]  Gottlieb S. Oehrlein,et al.  Study of sidewall passivation and microscopic silicon roughness phenomena in chlorine‐based reactive ion etching of silicon trenches , 1990 .

[15]  N. C. MacDonald,et al.  SCREAM I: A single mask, single-crystal silicon, reactive ion etching process for microelectromechanical structures , 1994 .