Optical characterization of high quality GaN produced by high rate magnetron sputter epitaxy

The thick films of GaN were investigated using X-ray diffraction, micro-Raman spectroscopy and photoluminescence spectroscopy. The thick films of GaN were prepared on (0001) sapphire using high rate magnetron sputter epitaxy with growth rates as high as 10–60 m/min. The width of the X-ray rocking curve ((0002) reflection) for the sample produced by this method is ∼300 arc-sec. Only the allowed modes were observed in the polarized Raman spectra. The background electron concentration is lower than 3×10 16 cm −3 , which was determined from the Raman spectra. The phonon lifetime determined from Raman E 2 (2) mode was 1.6 ps, which is comparable to that of bulk single crystal GaN grown by sublimation (1.4 ps). The full-width-at-half-maximum of the near band-edge photoluminescence peak obtained at 77K is ∼100 meV.

[1]  D. Clarke,et al.  Progress Toward Making Gallium Nitride Seed Crystals Using Hydride Vapor-Phase Epitaxy , 2004 .

[2]  L. Hultman,et al.  Misfit defect formation in thick GaN layers grown on sapphire by hydride vapor phase epitaxy , 2002 .

[3]  J. Hayes,et al.  Phonon lifetimes in bulk AlN and their temperature dependence , 2000 .

[4]  J. B. Webb,et al.  Influence of crystalline defects on transport properties of GaN grown by ammonia-molecular beam epitaxy and magnetron sputter epitaxy , 2000 .

[5]  M. Stroscio,et al.  Raman analysis of phonon lifetimes in AlN and GaN of wurtzite structure , 1999 .

[6]  J. Persio,et al.  Relationship between physical properties and gas purification in GaN grown by metalorganic vapor phase epitaxy , 1998 .

[7]  Fan Yang,et al.  Growth and characterization of GaN thin films by magnetron sputter epitaxy , 1998 .

[8]  Fan Yang,et al.  Magnetron Sputter Epitaxy of Gallium Nitride on (0001) Sapphire , 1997 .

[9]  L. Romano,et al.  Structure of GaN films grown by hydride vapor phase epitaxy , 1997 .

[10]  T. Gustafson,et al.  Single crystal wurtzite GaN on (111) GaAs with AlN buffer layers grown by reactive magnetron sputter deposition , 1993 .

[11]  Y. Kobayashi,et al.  Preparation and properties of III‐V nitride thin films , 1989 .

[12]  R. Egan,et al.  Properties of sputtered nitride semiconductors , 1988 .

[13]  H. Hovel,et al.  Electrical and Optical Properties of rf‐Sputtered GaN and InN , 1972 .

[14]  Charles Howard Henry,et al.  Mixing of Visible and Near-Resonance Infrared Light in GaP , 1966 .

[15]  A. Mooradian,et al.  Observation of the Interaction of Plasmons with Longitudinal Optical Phonons in GaAs , 1966 .

[16]  B. B. Varga,et al.  Coupling of Plasmons to Polar Phonons in Degenerate Semiconductors , 1965 .

[17]  Manuel Cardona,et al.  Light Scattering in Solids , 2000 .

[18]  A. Mitsuishi,et al.  Characterization of the free‐carrier concentrations in doped β‐SiC crystals by Raman scattering , 1987 .