Performance grading of the Lamont, Alberta C-SHRP pavement trial binders

This paper documents and discusses an investigation into the improved performance grading of asphalt binders that were used in the Canadian Strategic Highway Research Program (C-SHRP) pavement trial in Lamont, Alberta. Binders were assessed for their tendency to reversibly age at low-temperatures. While the correlation between cracking severity and regular AASHTO M320 and MP1a grades was weak (r 2=0.73 and 0.49, respectively), the predictive ability of the BBR method increased significantly when binders were tested after 1, 3 and 8 days of conditioning (r 2=0.94–0.97). Brittle and ductile fracture energies were measured in single-edge-notched bending (SENB) and double-edge-notched tension (DENT), respectively. In the brittle state, the SENB test revealed little difference between the binders. However, in the ductile state, the DENT test revealed significant differences between materials, with binders that showed the least amount of cracking having the highest works of fracture at 0°C.

[1]  B. Cotterell,et al.  The essential work of plane stress ductile fracture , 1977, International Journal of Fracture.

[2]  David Martin,et al.  Low-temperature rheological and fracture properties of polymer-modified bitumens , 2000 .

[3]  H. Soenen,et al.  FATIGUE TESTING OF BITUMINOUS BINDERS WITH A DYNAMIC SHEAR RHEOMETER , 2000 .

[4]  M G Bouldin,et al.  IMPLICATIONS OF THE NEW LOW TEMPERATURE SPECIFICATION ON PG GRADING AND TESTING OF ASPHALT BINDERS , 2000 .

[5]  David A. Anderson,et al.  PREDICTING THERMAL CRACKING OF PAVEMENTS FROM BINDER PROPERTIES: THEORETICAL BASIS AND FIELD VALIDATION , 2000 .

[6]  Simon A M Hesp,et al.  Canadian Technical Asphalt Association Proceedings 2001 46 th Annual Meeting, Toronto, Ontario Fracture Energy and Critical Crack Tip Opening Displacement: Fracture Mechanics- Based Failure Criteria for Low-Temperature Grading of Asphalt Binders , 2001 .

[7]  A Stawiarski,et al.  EUROPEAN BITSPEC SEMINARS 2002-2003: A COMMUNICATION PROJECT TO SUPPORT THE DEVELOPMENT OF THE EUROPEAN BITUMEN STANDARDISATION , 2004 .

[8]  S. Hesp,et al.  Chlorinated Polyolefins for Asphalt Binder Modification , 1994 .

[9]  Mihai O. Marasteanu,et al.  Techniques for Determining Errors in Asphalt Binder Rheological Data , 2001 .

[10]  W. Heukelom.  OBSERVATIONS ON THE RHEOLOGY AND FRACTURE OF BITUMENS AND ASPHALT MIXES , 1966 .

[11]  Hussain U Bahia,et al.  NON-LINEAR VISCOELASTIC AND FATIGUE PROPERTIES OF ASPHALT BINDERS , 1999 .

[12]  Anastasios M. Ioannides,et al.  Fracture Mechanics in Pavement Engineering: The Specimen-Size Effect , 1997 .

[13]  Ulf Isacsson,et al.  Laboratory study on the low temperature physical hardening of conventional and polymer modified bitumens , 2000 .

[14]  Simon A M Hesp,et al.  Low-Temperature Fracture Testing of Asphalt Binders: Regular and Modified Systems , 2000 .

[15]  Simon A M Hesp,et al.  Time-Temperature Superposition and Physical Hardening Effects in Low-Temperature Asphalt Binder Grading , 2003 .

[16]  Kk Tam,et al.  Improved Approach to Low Temperature and Fatigue Fracture Performance Grading of Asphalt Cements , 2004 .

[17]  David A. Anderson,et al.  Low-Temperature Thermal Cracking of Asphalt Binders as Ranked by Strength and Fracture Properties , 2000 .

[18]  W C Vonk,et al.  Low temperature performance of SBS-modified asphalt mixes , 2000 .

[19]  Ulf Isacsson,et al.  Influence of polymer modification on low temperature behaviour of bituminous binders and mixtures , 2003 .

[20]  R. N. Traxler,et al.  Rheological Properties of Asphalts IV Observations Concerning the Anomalous Flow Characteristics of Air‐Blown Asphalts , 1937 .

[21]  S Watkins.  Performance related properties for bituminous binders , 2000 .

[22]  David A. Anderson,et al.  BINDER CHARACTERIZATION AND EVALUATION. VOLUME 3: PHYSICAL CHARACTERIZATION , 1994 .

[23]  P S Pell,et al.  FATIGUE CHARACTERISTICS OF BITUMEN AND BITUMINOUS MIXES , 1962 .

[24]  X. Lu,et al.  IMPACT OF BITUMEN WAX ON ASPHALT PERFORMANCE - LOW TEMPERATURE CRACKING , 2004 .

[25]  E E Readshaw.  ASPHALT SPECIFICATIONS IN BRITISH COLUMBIA FOR LOW TEMPERATURE PERFORMANCE , 1972 .

[26]  T. W. Kennedy,et al.  Development of SHRP binder specification , 1993 .

[27]  Simon A M Hesp,et al.  Field Validation Study of Low-Temperature Performance Grading Tests for Asphalt Binders , 2004 .

[28]  D. Anderson,et al.  Glass transition behaviour and physical hardening of asphalt binders , 1993 .

[29]  David A. Anderson,et al.  Physical Hardening of Asphalt Binders Relative to Their Glass Transition Temperatures , 1999 .

[30]  Ezio Santagata,et al.  A Rheological Investigation on the Physical Hardening of Modified Asphalt Binders , 1996 .

[31]  R. Dongre.  EFFECT OF PHYSICAL HARDENING ON STRESS RELAXATION BEHAVIOUR OF ASPHALT BINDERS , 2000 .

[32]  Xiaohu Lu,et al.  Isothermal hardening in bitumen and in asphalt mixtures , 2004 .

[33]  S. Hesp,et al.  Compact Tension Testing of Asphalt Binders at Low Temperatures , 2006 .

[34]  Pedro Romero,et al.  Low-Temperature Physical Hardening of Hot-Mix Asphalt , 1999 .

[35]  C. Poel.  A general system describing the visco‐elastic properties of bitumens and its relation to routine test data , 2007 .

[36]  Nolan K. Lee,et al.  Low temperature fracture of polyethylene-modified asphalt binders and asphalt concrete mixes , 1995 .

[37]  M. Wiley,et al.  FORCE DUCTILITY -- AN ASPHALT PERFORMANCE INDICATOR , 1976 .

[38]  Adrian Andriescu,et al.  Essential and Plastic Works of Ductile Fracture in Asphalt Binders , 2004 .

[39]  Mihai O. Marasteanu,et al.  Evaluation of Fatigue Criteria for Asphalt Binders , 2001 .

[40]  Simon A M Hesp,et al.  LOW-TEMPERATURE FRACTURE TOUGHNESS OF POLYETHYLENE-MODIFIED ASPHALT BINDERS , 1994 .

[41]  J Gavin,et al.  The Lamont Test Road - Twelve Years of Performance Monitoring , 2003 .