High critical current density and improved irreversibility field in bulk MgB2 made by a scaleable, nanoparticle addition route

Bulk samples of MgB2 were prepared with 5, 10, and 15 wt % Y2O3 nanoparticles, added using a simple solid-state reaction route. Transmission electron microscopy showed a fine nanostructure consisting of ∼3–5 nm YB4 nanoparticles embedded within MgB2 grains of ∼400 nm size. Compared to an undoped control sample, an improvement in the in-field critical current density JC was observed, most notably for 10% doping. At 4.2 K, the lower bound JC value was ∼2×105 A cm−2 at 2 T. At 20 K, the corresponding value was ∼8×104 A cm−2. Irreversibility fields were 11.5 T at 4.2 K and 5.5 T at 20 K.

[1]  F. M. Mueller,et al.  Observation of coherent oxide precipitates in polycrystalline MgB2 , 2002, cond-mat/0203292.

[2]  S. Dou,et al.  Influence of Ag, Cu and Fe sheaths on MgB2 superconducting tapes , 2002 .

[3]  L. Schultz,et al.  Improved superconducting properties in nanocrystalline bulk MgB2 , 2001, cond-mat/0111585.

[4]  A. Palenzona,et al.  Magnetic characterization of sintered MgB2 samples: effect of substitution or 'doping' with Li, Al and Si , 2001, cond-mat/0105212.

[5]  M. Murakami,et al.  Improvement of critical current density in MgB2 superconductors by Zr doping at ambient pressure , 2001 .

[6]  X. H. Liu,et al.  Transport behavior and critical current densities in MgB2 wires , 2001 .

[7]  Japan.,et al.  Review of the superconducting properties of MgB2 , 2001, cond-mat/0108265.

[8]  M. Murakami,et al.  High critical current density of MgB2 bulk superconductor doped with Ti and sintered at ambient pressure , 2001 .

[9]  H. Suo,et al.  Large transport critical currents in dense Fe- and Ni-clad MgB2 superconducting tapes , 2001, cond-mat/0106341.

[10]  D. Larbalestier,et al.  Potential application of magnesium diboride for accelerator magnet applications , 2001, PACS2001. Proceedings of the 2001 Particle Accelerator Conference (Cat. No.01CH37268).

[11]  Jh H. Choi,et al.  High critical current density and enhanced irreversibility ® eld in superconducting MgB 2 thin ® lms , 2001 .

[12]  D. Larbalestier,et al.  Electronic anisotropy, magnetic field-temperature phase diagram and their dependence on resistivity in c-axis oriented MgB2 thin films , 2001, cond-mat/0104562.

[13]  P. Toulemonde,et al.  Transport and inductive critical current densities in superconducting MgB2 , 2001, cond-mat/0104395.

[14]  L. Cohen,et al.  Enhancement of the high-magnetic-field critical current density of superconducting MgB2 by proton irradiation , 2001, Nature.

[15]  D. C. Larbalestier,et al.  High critical current density and enhanced irreversibility field in superconducting MgB2 thin films , 2001, Nature.

[16]  R. Cava,et al.  Strongly linked current flow in polycrystalline forms of the superconductor MgB2 , 2001, Nature.

[17]  C. P. Bean,et al.  Magnetization of High-Field Superconductors , 1964 .